Foreign-object damage and high-cycle fatigue: role of microstructure in Ti–6Al–4V

The objective of this study was to evaluate the influence of microstructure on the susceptibility to high-cycle fatigue (HCF) failure in Ti–6Al–4V following foreign-object damage (FOD), specifically by comparing a fine-grained bi-modal microstructure with a coarse grained lamellar microstructure. FOD was simulated by high-velocity impacts of steel spheres on a flat surface. This caused a marked reduction in the smooth-bar fatigue strength in both microstructures, primarily because of the premature initiation of fatigue cracking resulting from the stress concentration associated with damage site and FOD-induced microcracking. The FODinitiated microcracks were found to be of a size comparable with microstructural dimensions, and on subsequent fatigue loading were seen to propagate at applied stress-intensity levels below K1 MPa m 1/2 , i.e. a factor of roughly two less than the ‘worstcase’ threshold stress-intensity range in Ti–6Al–4V for a crack of large size compared to microstructural dimensions (a ‘continuumsized’ crack). A rational approach against HCF failures from such microcracks is proposed for the fine-grained bi-modal microstructure based on the Kitagawa–Takahashi diagram. For the bi-modal microstructure, the Kitagawa–Takahashi diagram provides a basis for describing the threshold conditions for FOD-induced HCF failures, in terms of the stress concentration corrected smooth-bar fatigue limit for small crack sizes and the worst-case threshold for larger continuum-sized cracks. However, this approach was found to be less applicable to the coarse grained lamellar microstructure, primarily because of low small-crack growth resistance relative to its higher smooth-bar fatigue limit.  2001 Elsevier Science Ltd. All rights reserved.

[1]  R. Ritchie,et al.  Propagation of short fatigue cracks , 1984 .

[2]  Brad Lee Boyce,et al.  The residual stress state due to a spherical hard-body impact , 2001 .

[3]  B. A. Cowles,et al.  High cycle fatigue in aircraft gas turbines—an industry perspective , 1996 .

[4]  R. S. Bertke,et al.  Impact damage on titanium leading edges from small hard objects , 1980 .

[5]  R. Ritchie,et al.  Small fatigue cracks , 1986 .

[6]  R O R I T C H I E,et al.  High-cycle fatigue of Ti–6Al–4V , 1999 .

[7]  T. Nicholas,et al.  On the use of the Goodman diagram for high cycle fatigue design , 1996 .

[8]  James C. Newman,et al.  An empirical stress-intensity factor equation for the surface crack , 1981 .

[9]  John W. Hutchinson,et al.  Foreign object damage and fatigue crack threshold: Cracking outside shallow indents , 2001 .

[10]  M. E. Haddad,et al.  Prediction of non propagating cracks , 1979 .

[11]  R. Ritchie,et al.  Influence of foreign-object damage on crack initiation and early crack growth during high-cycle fatigue of Ti–6Al–4V , 2000 .

[12]  R. Ritchie,et al.  Small fatigue cracks: mechanics, mechanisms and engineering applications , 2001 .

[13]  Charles Annis,et al.  An assessment of the role of near-threshold crack growth in high-cycle-fatigue life prediction of aerospace titanium alloys under turbine engine spectra , 1996 .

[14]  E. R. Rios,et al.  The Behaviour of short fatigue cracks , 1986 .

[15]  P. Lukas,et al.  Stress intensity factor for small notch-emanated cracks , 1987 .

[16]  R. Ritchie,et al.  Role of foreign-object damage on thresholds for high-cycle fatigue in Ti-6Al-4V , 2000 .

[17]  R. Boyer,et al.  Fatigue behavior of titanium alloys , 1999 .