ZnTe single crystal growth by the liquid encapsulated pulling method

Large diameter ZnTe single crystals were grown by the liquid-encapsulated pulling method using a double crucible. Crystals of around 80 mm in diameter and 40 mm in length were reproducibly obtained by this method. Both (100) and (110) crystals were successfully grown. The strong facet growth was observed when the shoulder part of the bulk was formed. Rectangular facet growth was observed in (100) growth and hexagonal facet growth was observed in (110) growth. The etch pit density of the grown crystal was lower than 10000 cm -2 and the strain in the crystal was lower than that of modified liquid encapsulated Kyropoulos method.

[1] S. Takeuchi,et al. Stacking-fault energy of II–VI compounds , 1985 .

[2] Xiang Zhang,et al. Two‐dimensional electro‐optic imaging of THz beams , 1996 .

[3] Osamu Oda,et al. ZnTe pure green light-emitting diodes fabricated by thermal diffusion , 2000 .

[4] M. Hosoda,et al. Frequency domain spectroscopy of free-space terahertz radiation , 2000 .

[5] S. Kyropoulos. Ein Verfahren zur Herstellung großer Kristalle , 1926 .

[6] M. Luqman,et al. Ohmic contacts to zinc telluride and their high temperature behavior , 1987 .

[7] Kenji Sato,et al. Growth and Characterization of Large Diameter ZnTe Single Crystals , 2002 .

[8] O. Oda,et al. Growth of long-length 3 inch diameter Fe-doped InP single crystals , 1996 .