Synthesis and water sorption properties of a new composite “CaCl2 confined into SBA-15 pores”

Abstract The composite CaCl 2 @SBA-15 with the mass ratio Ca/Si = 0.58 has been synthesized via impregnation of nano-structured mesoporous silica SBA-15 with saturated aqueous solution of calcium chloride. The material was studied by methods of X-ray diffraction, differential scanning calorimetry, infrared spectroscopy, nitrogen adsorption and thermal analysis. It was shown that calcium chloride is located basically in the pores of silica. The isotherms and kinetics curves of water ad/desorption were measured at temperature 50 °C and vapor pressure range from 0 to 50 mbar. A small hysteresis was observed for the formation di- and tetra-hydrates of CaCl 2 in the pores. The equilibrium pressure over the dispersed CaCl 2 dihydrate was found to be 2.5–4 times lower relative to the bulk one, allowing a significant improvement of the salt desiccative properties. The possible reasons of this pressure decrease might be the higher mobility of water in the dispersed dihydrate and/or the increase in the surface energy of the salt (hydrate) confined to the SBA pores. The latter effect is a reason of the melting point depression for dispersed hydrates CaCl 2 · n H 2 O with n  = 2, 4 and 6 that was revealed by DSC tests. The effective water diffusivity in SBA pores has been determined. The Knudsen diffusion in the SBA mesopores was found to be a rate-limiting stage of water sorption on CaCl 2 @SBA-15. The equilibrium sorption curves for the new composite were compared with other composite sorbents “CaCl 2 in porous matrix”. Several possible applications of the new sorbent, among which are the gas drying, heat storage and adsorptive heat pumps, were preliminary evaluated.

[1]  Manuel R. Conde,et al.  Properties of aqueous solutions of lithium and calcium chlorides: formulations for use in air conditioning equipment design , 2004 .

[2]  G. Stucky,et al.  Mesoporous and Mesostructured Materials for Optical Applications , 2001 .

[3]  R. Radermacher,et al.  Heat Conversion Systems , 1993 .

[4]  E. Teller,et al.  ADSORPTION OF GASES IN MULTIMOLECULAR LAYERS , 1938 .

[5]  A. Gedanken,et al.  Evaluation of metal oxide phase assembling mode inside the nanotubular pores of mesostructured silica , 2005 .

[6]  G. Halsey,et al.  Physical Adsorption on Non‐Uniform Surfaces , 1948 .

[7]  Yury I. Aristov,et al.  Novel Materials for Adsorptive Heat Pumping and Storage: Screening and Nanotailoring of Sorption Properties , 2007 .

[8]  Bradley F. Chmelka,et al.  Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures , 1998 .

[9]  Jörg Kärger,et al.  Diffusion in Zeolites and Other Microporous Solids , 1992 .

[10]  J. Quinson,et al.  The Role of Thermoporometry in the Study of Porous Solids , 1988 .

[11]  Yu. I. Aristov,et al.  New composite sorbent CaCl2 in mesopores for sorption cooling/heating , 2002 .

[12]  Bénédicte Lebeau,et al.  Chemical strategies to design textured materials: from microporous and mesoporous oxides to nanonetworks and hierarchical structures. , 2002, Chemical reviews.

[13]  E. Barrett,et al.  (CONTRIBUTION FROM THE MULTIPLE FELLOWSHIP OF BAUGH AND SONS COMPANY, MELLOX INSTITUTE) The Determination of Pore Volume and Area Distributions in Porous Substances. I. Computations from Nitrogen Isotherms , 1951 .

[14]  Ruzhu Wang,et al.  New composite adsorbent for solar-driven fresh water production from the atmosphere , 2007 .

[15]  T. Bein,et al.  Inclusion Chemistry in Periodic Mesoporous Hosts , 1998 .

[16]  J. B. Higgins,et al.  A new family of mesoporous molecular sieves prepared with liquid crystal templates , 1992 .

[17]  D. Ackermann,et al.  Studies of the water adsorption on Zeolites and modified mesoporous materials for seasonal storage of solar heat , 2004 .

[18]  S. Lowell,et al.  Powder surface area and porosity , 1984 .

[19]  Yu. I. Aristov,et al.  Use of Modern Composite Materials of the Chemical Heat Accumulator Type for Fire Protection and Fire Extinguishing , 1999 .

[20]  A. Freni,et al.  Kinetics of water sorption on SWS-1L (calcium chloride confined to mesoporous silica gel): Influence of grain size and temperature , 2006 .

[21]  K. Daou,et al.  Desiccant cooling air conditioning : a review , 2006 .

[22]  Yuri I. Aristov,et al.  Effective Inorganic Hybrid Adsorbents of Water Vapor by the Sol−Gel Method , 1997 .

[23]  Yuri I. Aristov,et al.  Kinetics of water adsorption on loose grains of SWS-1L under isobaric stages of adsorption heat pumps: The effect of residual air , 2008 .

[24]  S. Joo,et al.  X-ray diffraction analysis of mesostructured materials by continuous density function technique , 2003 .

[25]  Giovanni Restuccia,et al.  Selective water sorbents for multiple applications, 1. CaCl2 confined in mesopores of silica gel: Sorption properties , 1996 .

[26]  Yuri I. Aristov,et al.  Water sorption on composite ''silica modified by calcium nitrate" , 2009 .