Evolution of Microstructure and Microchemistry in Cold-worked 316 Stainless Steels under PWR Irradiation

The evolution of microstructures and microchemistry was examined by transmission electron microscopy in cold-worked SUS 316 stainless steel components irradiated in a pressurized water reactor to 1–73 dpa at 565–596 K. Homogenous nucleation of dislocation loops, helium bubbles and γ′ precipitates was detected. The dislocation loops consisted of a high density of Frank loops and black dots. The black dots are considered to be small Frank loops, some fraction of which could be vacancy-type. The size distribution showed a double peak, which remained unchanged up to 73 dpa, suggesting that the dislocation structure was saturated under a balance of nucleation and disappearance. The helium bubbles were extremely dense and fine, resulting in swelling of less than 0.1%. Such bubble structure was formed under irradiation with a high He/dpa ratio. The γ′ precipitation was detected at doses higher than 4 dpa with an increasing density for higher doses. The measured radiation hardening was almost explained by these visible microstructural features. Radiation-induced segregation at grain boundaries was confirmed to continuously develop up to 73 dpa whereas no significant segregation could be detected at Frank loops.

[1]  O. Maksimkin,et al.  Characterization of 08Cr16Ni11Mo3 stainless steel irradiated in the BN-350 reactor , 2004 .

[2]  N. Baluc,et al.  The microstructure and associated tensile properties of irradiated fcc and bcc metals , 2000 .

[3]  F. Garner,et al.  Swelling and void-induced embrittlement of austenitic stainless steel irradiated to 73–82 dpa at 335–365°C , 1998 .

[4]  N. Nakajima,et al.  Stress corrosion cracking on irradiated 316 stainless steel , 2001 .

[5]  P. J. Maziasz,et al.  Overview of microstructural evolution in neutron-irradiated austenitic stainless steels , 1993 .

[6]  M. Victoria,et al.  Deformation modes of proton and neutron irradiated stainless steels , 2000 .

[7]  G. E. Lucas,et al.  The evolution of mechanical property change in irradiated austenitic stainless steels , 1993 .

[8]  A. Hishinuma,et al.  Temperature dependence of swelling in type 316 stainless steel irradiated in HFIR , 1988 .

[9]  Stephen M. Bruemmer,et al.  Influence of irradiation temperature and dose gradients on the microstructural evolution in neutron-irradiated 316SS , 2003 .

[10]  E. Kenik,et al.  Radiation-induced segregation in FFTF-irradiated austenitic stainless steels , 1992 .

[11]  F. Garner,et al.  Evolution of microstructure in face-centered cubic metals during irradiation , 1993 .

[12]  K. Fujii,et al.  IASCC Susceptibility and Slow Tensile Properties of Highly-irradiated 316 Stainless Steels , 2004 .

[13]  P. Dubuisson,et al.  Irradiation damage in 304 and 316 stainless steels: experimental investigation and modeling. Part I: Evolution of the microstructure , 2004 .

[14]  Katsuhiko Fujii,et al.  Separation of Microstructural and Microchemical Effects in Irradiation Assisted Stress Corrosion Cracking using Post-irradiation Annealing , 2004 .

[15]  E. Simonen,et al.  Evolution of fine-scale defects in stainless steels neutron-irradiated at 275 C , 2003 .

[16]  M. G. Burke,et al.  316 stainless steel cavity swelling in a PWR , 1995 .