Nonlinear elastic–plastic stress investigation for two interacting 3‐D cracks in offshore pipelines

Under continuous loading conditions, small closely distanced cracks can grow and coalesce into a large one that may subsequently pose a threat to the integrity and safety of structures. Although many research works were carried out for predicting fatigue growth of multiple cracks, few papers focusing on nonlinear elastic–plastic analysis of multiple cracks' fracture behaviours can be referred to. In this study, 3-D elastic–plastic investigation has been performed on fracture behaviours of two collinear cracks located in offshore pipelines. The influences of the cracks configuration, the separation distance and internal pressure of the pipeline on the crack behaviours are investigated. On the basis of the numerical results, a new strain-based crack tip opening displacement estimation method is proposed for assessing the fracture behaviour of flawed pipelines with two interacting collinear cracks.

[1]  A. Kotousov,et al.  Local plastic collapse conditions for a plate weakened by two closely spaced collinear cracks , 2014 .

[2]  Zhongmin Xiao,et al.  On 3-D crack problems in offshore pipeline with large plastic deformation , 2013 .

[3]  P. J. Budden.  Failure assessment diagram methods for strain-based fracture , 2006 .

[4]  Yao Zhang,et al.  Elastic–plastic fracture analyses for pipeline girth welds with 3D semi-elliptical surface cracks subjected to large plastic bending , 2013 .

[5]  Zhongmin Xiao,et al.  Fracture analysis of girth welded pipelines with 3D embedded cracks subjected to biaxial loading conditions , 2012 .

[6]  Weiliang Jin,et al.  Buckling response of offshore pipelines under combined tension and bending , 2012 .

[7]  Shinji Konosu,et al.  Multiple Fatigue Crack Growth Prediction Using Stress Intensity Factor Solutions Modified by Empirical Interaction Factors , 2012 .

[8]  Masayuki Kamaya,et al.  Growth evaluation of multiple interacting surface cracks. Part I: Experiments and simulation of coalesced crack , 2008 .

[9]  A. F. Grandt,et al.  RESIDUAL STRENGTH OF UNSTIFFENED ALUMINUM PANELS WITH MULTIPLE SITE DAMAGE , 1997 .

[10]  D. Cartwright,et al.  An analytical solution for two equal-length collinear strip yield cracks , 2001 .

[11]  Nikzad Nourpanah,et al.  Development of a reference strain approach for assessment of fracture response of reeled pipelines , 2010 .

[12]  B. Jahromi,et al.  Instability of cylindrical shells with single and multiple cracks under axial compression , 2012 .

[13]  S. Tan,et al.  Elastic–plastic fracture behavior of a radial matrix crack interacting with a circle inclusion with generalized Irwin corrections , 2014 .

[14]  S.-T. Tu,et al.  AN ENGINEERING ASSESSMENT OF FATIGUE CRACK GROWTH OF IRREGULARLY ORIENTED MULTIPLE CRACKS , 1994 .

[15]  Z. Xiao,et al.  An interfacial arc-shaped Zener–Stroh crack due to inclusion–matrix debonding in composites , 2014 .

[16]  A. Kotousov,et al.  A strip yield model for two collinear cracks , 2012 .

[17]  Xiao Zhong-min,et al.  Fracture capacity of girth welded pipelines with 3D surface cracks subjected to biaxial loading conditions , 2012 .

[18]  Erling Østby.  Fracture Control — Offshore Pipelines: New Strain-Based Fracture Mechanics Equations Including the Effects of Biaxial Loading, Mismatch, and Misalignment , 2005 .

[19]  Andrei Kotousov,et al.  A strip yield model for two collinear cracks in plates of arbitrary thickness , 2012, International Journal of Fracture.

[20]  H. S. Kushwaha,et al.  Improved integrity assessment equations of pipe bends , 2009 .

[21]  Erling Østby,et al.  Fracture response of pipelines subjected to large plastic deformation under tension , 2004 .

[22]  D. Ouinas,et al.  Numerical modelling of the interaction macro-multimicrocracks in a plate under tensile stress , 2011, J. Comput. Sci..

[23]  Z. Xiao,et al.  On the Plastic Zone Size and the Crack Tip Opening Displacement of an Interface Crack Between two Dissimilar Materials , 2012, International Journal of Fracture.