Gibbs energy of formation of Cu2R2O5 (R = Dy, Ho, Er, Yb) from component oxides employing solid oxide electrochemical cells

R. V. Kumar | D. Fray | G. Kale | R. V. Kumar

[1] D. Fray,et al. Gibbs Energy of Formation of CuGd2O4 and Phase Relations in the Cu‐Gd‐O System , 1995 .

[2] C. Rao,et al. Synthesis and characterization of superconducting YbBa2Cu3O7−δ and Y1−xLuxBa2Cu3O7−δ (0.0 < x < 0.75): Lower limit of the rare-earth ion radius tolerated in the 123 cuprate system , 1990 .

[3] J. Karpinski,et al. Bulk synthesis of the 81-K superconductor YBa2Cu4O8 at high oxygen pressure , 1988, Nature.

[4] T. Takabatake,et al. Characterization of the high-tc phase and its metamorphic phases, Ba2YCu3O7−δ , 1987 .

[5] Chu,et al. Superconductivity above 90 K in the square-planar compound system ABa2Cu3O6+x with A=Y, La, Nd, Sm, Eu, Gd, Ho, Er and Lu. , 1987, Physical review letters.

[6] D. Murphy,et al. Bulk superconductivity at 91 K in single-phase oxygen-deficient perovskite Ba2YCu , 1987, Physical review letters.

[7] A. Kaul,et al. An electrochemical study of high-temperature stability of compounds between the rare earths and copper oxide , 1976 .