Calculation of unstable mixing region in wurtzite In1−x−yGaxAlyN

The wurtzite structure In1−x−yGaxAlyN quaternary system with a wide band gap, which is useful for light emitters in the wavelength region shorter than green, is studied with respect to the unstable region in mixing. This unstable region in mixing is calculated from the free energy of mixing using the strictly regular solution model. The interaction parameter used in this calculation is obtained using the delta-lattice-parameter method. From this calculation, the ternary alloys of InAlN, InGaN, and GaAlN are, respectively, predicted to always, sometimes, and hardly ever have a unstable mixing region at the temperature lower than 3000 °C.

Takashi Matsuoka | T. Matsuoka

[1] S. Nakamura,et al. InGaN-Based Multi-Quantum-Well-Structure Laser Diodes , 1996 .

[2] Kentaro Onabe,et al. Unstable Regions in III–V Quaternary Solid Solutions Composition Plane Calculated with Strictly Regular Solution Approximation , 1982 .

[3] K. Hiramatsu,et al. Doping of GaN with Si and properties of blue m/i/n/n+ GaN LED with Si-doped n+-layer by MOVPE , 1991 .

[4] Shuji Nakamura,et al. GaN Growth Using GaN Buffer Layer , 1991 .

[5] H. Amano,et al. Metalorganic vapor phase epitaxial growth of a high quality GaN film using an AlN buffer layer , 1986 .

[6] G. B. Stringfellow. Calculation of ternary and quaternary III–V phase diagrams , 1974 .

[7] T. Matsuoka,et al. Wide-gap semiconductor InGaN and InGaAln grown by MOVPE , 1992 .

[8] J. C. Phillips. Dielectric Definition of Electronegativity , 1968 .

[9] Takashi Mukai,et al. Superbright Green InGaN Single-Quantum-Well-Structure Light-Emitting Diodes , 1995 .

[10] H. Amano,et al. P-Type Conduction in Mg-Doped GaN Treated with Low-Energy Electron Beam Irradiation (LEEBI) , 1989 .