Abstract Variations of remanent polarization and coercive field of undoped and yttrium doped Pb(Zr0.65Ti0.35)O3 thin films prepared by Sol-Gel processing were observed using hysteresis measurement according to the cumulative switching cycles. Remanent polarization and coercive field of undoped Pb(Zr0.65Ti0.35)O3 thin films after 1010 polarization reversals were decreased and increased, respectively. But the variations of remanent polarization and coercive field of yttrium doped specimens with the polarization switching cycles were different from those of undoped specimens. In the case of yttrium doped specimens, remanent polarizations were not decreased and coercive fields were increased more than those of undoped specimens after fatigue. It was well known that doped yttrium reduced holes and increased vacancies in PZT thin films. This strongly suggests that the variations of holes and vacancies influence on the remanent polarizations and the coercive fields of Pb(Zr0.65Ti0.35)O3 thin films after fatigue....
[1]
T. Mihara,et al.
Anomalous fatigue behavior in Zn doped PZT
,
1993
.
[2]
C. Araujo,et al.
Recent results on switching, fatigue and electrical characterization of sol-gel based PZT capacitors
,
1991
.
[3]
Masao Takahashi.
Electrical Resistivity of Lead Zirconate Titanate Ceramics Containing Impurities
,
1971
.
[4]
R. Holman,et al.
Substitution of Bi and Nb Ions in Lead Zirconate‐Titanate
,
1971
.
[5]
H. Jaffe,et al.
ELECTRICAL CONDUCTIVITY IN LEAD TITANATE ZIRCONATE CERAMICS
,
1963
.