Fatigue testing of composite patches for ship plating fracture repair

ABSTRACT The objective of this study is to examine, through physical testing, the use of composite patches for preventing crack growth and extending the service life of ship plating. Fatigue tests were conducted on steel plates to experimentally validate the effectiveness of using composite patches as a means to prevent crack growth and extend the fatigue life of structural components. Specimens were tested with and without the use of composite reinforcements. Previous results of numerical analysis studies had indicated that a one- to two-order of magnitude increase in service life can be expected for the conditions tested. The experimental results presented here show increases closer to a single order of magnitude. The difference is attributed to two factors: failure mechanisms associated with debonding of the patch and cracking of the patch itself. Of critical importance, therefore, are the implementation of a quality-controlled bonding procedure and optimisation of the geometry and properties of the patch systems based upon the parent plate's properties and fracture conditions.

[1]  Nicholas G. Tsouvalis,et al.  Experimental and numerical study of the fatigue behaviour of composite patch reinforced cracked steel plates , 2009 .

[2]  Naveen Rastogi,et al.  Analysis of bonded composite patch repaired metallic structures - An overview , 1998 .

[3]  I. M. May,et al.  Modelling composite repairs to cracked metal structures , 2009 .

[4]  Rhys Jones,et al.  Continued Airworthiness of Composite Repairs to Primary Structures for Military Aircraft , 1995 .

[5]  J. D. Clarke,et al.  Use of adhesives in repair of cracks in ship structures , 1988 .

[6]  M. Belhouari,et al.  Computation of the stress intensity factors for repaired cracks with bonded composite patch in mode I and mixed mode , 2002 .

[7]  Alan Baker,et al.  Modelling of the fatigue growth behaviour of patched cracks , 1997 .

[8]  William Edberg,et al.  REHABILITATION OF STEEL BRIDGES WITH COMPOSITE MATERIALS , 1996 .

[9]  Alain Nussbaumer,et al.  Analysis of cracked steel members reinforced by pre-stress composite patch , 2003 .

[10]  Heshmat A. Aglan,et al.  Fatigue behavior of bonded composite repairs , 2001 .

[11]  David Whittaker,et al.  Application of bonded composites in the repair of ships structures – A 15-year service experience , 2009 .

[12]  C.-L. Ong,et al.  The reinforcing effect of composite patch repairs on metallic aircraft structures , 1992 .

[13]  X. Zhao,et al.  State-of-the-art review on FRP strengthened steel structures , 2007 .

[14]  Riadh Al-Mahaidi,et al.  Experimental study of fatigue crack growth behaviour in adhesively reinforced steel structures , 2009 .

[15]  Tai-Yan Kam,et al.  Fatigue analysis of cracked aluminum plates repaired with bonded composite patches , 1998 .

[16]  Heshmat A. Aglan,et al.  Design guidelines for composite patches bonded to cracked aluminum substrates , 2002 .

[17]  Hamid Saadatmanesh,et al.  Fatigue Strength of Steel Girders Strengthened with Carbon Fiber Reinforced Polymer Patch , 2003 .

[18]  Andrew R. Thoreson,et al.  The effect of patch geometry on the static and fatigue behaviors of defective aluminum panels repaired with a composite patch , 2006 .

[19]  Marios K. Chryssanthopoulos,et al.  FRACTURE MECHANICS 2D-FEA OF A CRACKED STEEL PLATE WITH A CFRP PATCH , 2004 .

[20]  Kwang Hwa Chung,et al.  Fracture Mechanics Analysis of Cracked Plate Repaired by Composite Patch , 2000 .

[21]  Bijan Mohammadi,et al.  Mixed-mode fracture analysis of aluminium repaired panels using composite patches , 2006 .

[22]  Zaira P. Marioli-Riga,et al.  Study of composite patch repair by analytical and numerical methods , 2001 .

[23]  C. T. Sun,et al.  Composite patches as reinforcements and crack arrestors in aircraft structures , 1998 .

[24]  Yuris A. Dzenis,et al.  Analysis of single lap adhesive composite joints with delaminated adherends , 2003 .

[25]  R.M.V. Pidaparti,et al.  Static characteristics and fatigue behavior of composite-repaired aluminum plates , 2002 .

[26]  S. K. Malhotra,et al.  Residual strength and fatigue life assessment of composite patch repaired specimens , 1999 .

[27]  J. Rice,et al.  Elementary engineering fracture mechanics , 1974 .

[28]  Alain Nussbaumer,et al.  Delamination effects on cracked steel members reinforced by prestressed composite patch , 2003 .

[29]  A. Karimi,et al.  Master‟s thesis , 2011 .

[30]  F. Livingstone,et al.  Oil platforms, destroyers and frigates—case studies of QinetiQ's marine composite patch repairs , 2005 .

[31]  M. Kanninen,et al.  A finite element calculation of stress intensity factors by a modified crack closure integral , 1977 .

[32]  Hideki Sekine,et al.  Numerical simulation study of fatigue crack growth behavior of cracked aluminum panels repaired with a FRP composite patch using combined BEM/FEM , 2005 .