Water-soluble complexes between cationic surfactants and comb-type copolymers consisting of an anionic backbone and hydrophilic nonionic poly(N,N-dimethylacrylamide) side chains.
暂无分享,去创建一个
The formation of complexes between the cationic surfactant dodecyl trimethylammonium bromide (DTAB) and the comb-type anionic polyelectrolytes poly(sodium acrylate-co-sodium 2-acrylamido-2-methylpropane sulfonate)-g-poly(N,N-dimethylacrylamide) (P(NaA-co-NaAMPS)-g-PDMAMx) was investigated in dilute aqueous solutions by means of turbidimetry, pyrene fluorescence probing, viscometry, z-potential measurements, and dynamic light scattering. The comb-type copolymers consist of an anionic copolymer backbone, P(NaA-co-NaAMPS), containing 84 mol % NaAMPS units, while the weight percentage, x, of the PDMAM side chains varies from x = 12% (w:w) up to x = 58% (w:w). It was found that, contrary to the water-insoluble complexes formed between the linear polyelectrolyte P(NaA-co-NaAMPS) and DTAB, the solubility in water of the complexes formed between the comb-type copolymers and DTAB is significantly improved with increasing x. The complexation process starts at the same critical aggregation concentration (about 2 orders of magnitude lower than the critical micelle concentration of DTAB), regardless of x, and it is accompanied by charge neutralization and appearance of hydrophobic microdomains. Both effects lead to the substantial collapse of the polyelectrolyte chain upon addition of DTAB. However, the complexes of the comb-type copolymers with DTAB are stabilized in water as nanoparticles, and probably consisted of a water-insoluble core (the polyelectrolyte/surfactant complex), protected by a hydrophilic nonionic PDMAM corona. The size of the nanoparticles varies from approximately 35 nm up to approximately 120 nm, depending on x.