Early age thermal cracking of mass concrete blocks with Portland cement and ground granulated blast-furnace slag

Evolution of heat due to an exothermic reaction between cementitious materials and water plays a significant role in the temperature rise in mass concrete at an early age. The temperature gradient between the core of mass concrete and its surfaces leads to the development of thermal stresses and may cause cracking if these stresses exceed the evolving tensile strength of concrete. This paper presents the results of an experimental and finite-element investigation of heat generation and dissipation in full-scale mass concrete blocks 2 m × 2 m × 2 m in size. A concrete mix with 100% OPC and 70% cement replaced by GGBFS was used in these blocks. The temperature profile across the depth of the block was measured at the centre, side and corner of the block. A semi-adiabatic calorimeter was used to measure the heat of hydration of the two concrete mixes. Finite-element simulation of these blocks captured with good accuracy the measured evolution of temperature in the blocks. Numerical simulation was subsequentl...

[1]  D. Higgins,et al.  Resistance of concrete containing ggbs to the thaumasite form of sulfate attack , 2003 .

[2]  Mark Alexander,et al.  The influence of binder type, cracking and cover on corrosion rates of steel in chloride-contaminated concrete , 2007 .

[3]  Recep Yumrutaş,et al.  Theoretical and experimental investigation of total equivalent temperature difference (TETD) values for building walls and flat roofs in Turkey , 2009 .

[4]  Ø. Bjøntegaard,et al.  Coefficient of thermal expansion of cement paste and concrete: Mechanisms of moisture interaction , 2006 .

[5]  H. Binici,et al.  Sulfate resistance of plain and blended cement , 2006 .

[6]  J. S. Ryou,et al.  Variation in the chloride threshold level for steel corrosion in concrete arising from different chloride sources , 2008 .

[7]  Gyu-Yong Kim,et al.  Autogenous shrinkage of concrete containing granulated blast-furnace slag , 2006 .

[8]  Zhenbo Wang,et al.  Cement hydration based model to predict the mechanical properties of precast concrete , 2014 .

[9]  Yan Yao,et al.  A study on creep and drying shrinkage of high performance concrete , 2001 .

[10]  G. De Schutter,et al.  Finite element simulation of thermal cracking in massive hardening concrete elements using degree of hydration based material laws , 2002 .

[11]  Akh Kwan,et al.  Adding limestone fines, fly ash and silica fume to reduce heat generation of concrete , 2013 .

[12]  N. Robeyst,et al.  Study of the hydration of Portland cement blended with blast-furnace slag by calorimetry and thermogravimetry , 2010 .

[13]  M. Collepardi,et al.  A state-of-the-art review on delayed ettringite attack on concrete , 2003 .

[14]  Xiangming Zhou,et al.  Effects of PFA and GGBS on Early-Ages Engineering Properties of Portland Cement Systems , 2012 .

[15]  D. V. Phillips,et al.  Direct tension tests on notched and un-notched plain concrete specimens , 1993 .

[16]  Frank P. Incropera,et al.  Fundamentals of Heat and Mass Transfer , 1981 .

[17]  L. Wadsö,et al.  A method based on isothermal calorimetry to quantify the influence of moisture on the hydration rate of young cement pastes , 2010 .