Effects of activating flux on the welded joint characteristics in gas metal arc welding

Abstract This paper presents the effect of each welding parameter on the weld bead geometry, and then sets out to determine the optimal process parameters using the Taguchi method to determine the parameters. Three kinds of oxides, Fe 2 O 3 , SiO 2 , and MgCO 3 , were used to investigate the effect of activating flux aided gas metal arc welding (GMAW) on weld bead geometry, angular distortion and mechanical properties in AISI 1020 carbon steel. During welding, a charge coupled device (CCD) camera system was used to observe and record images of the welding arc and analyze the relationship between penetration increase and arc profile. The experimental results showed that activating flux aided GMAW increased the weld area and penetration and tended to reduce the angular distortion of the weldment. The MgCO 3 flux produced the most noticeable effect. Furthermore, the welded joint presented better tensile strength and hardness.

[1]  W Lucas,et al.  ACTIVATING FLUX - INCREASING THE PERFORMANCE AND PRODUCTIVITY OF THE TIG AND PLASMA PROCESSES , 1996 .

[2]  Kenneth C. Mills,et al.  Factors affecting variable weld penetration , 1990 .

[3]  Edward William Reutzel,et al.  Joining Pipe with the Hybrid Laser-GMAW Process: Weld Test Results and Cost Analysis , 2006 .

[4]  J. F. Porter,et al.  Laser-assisted gas metal arc welding of 25-mm-thick HY-80 plate , 2001 .

[5]  R. Green.  How to optimize mild steel GMAW , 2004 .

[6]  B. Huneau,et al.  Optimizing the design of silica coating for productivity gains during the TIG welding of 304L stainless steel , 2007 .

[7]  Theodore T. Allen,et al.  A method for robust process design based on direct minimization of expected loss applied to arc welding , 2001 .

[8]  P. Burgardt,et al.  Interaction between Impurities and Welding Variables in Determining GTA Weld Shape Depending on the trace elements in the base materials, identical changes in welding variables can have an opposite effect on weld shape , 1986 .

[9]  T. Paskell,et al.  GTAW flux increases weld joint penetration , 1997 .

[10]  S. Katayama,et al.  High-power CO2 laser-MIG hybrid welding for increased gap tolerance. Hybrid weldability of thick steel plates with a square groove , 2004 .

[11]  M. Kuo,et al.  Laser welding with activating flux , 2001 .

[12]  E. Karadeniz,et al.  The effect of process parameters on penetration in gas metal arc welding processes , 2007 .

[13]  Luca Tomesani,et al.  The influence of arc transfer mode in hybrid laser-mig welding , 2007 .

[14]  Yuming Zhang,et al.  Image processing algorithm for automated monitoring of metal transfer in double-electrode GMAW , 2007 .

[15]  M. Marya,et al.  Chloride contributions in flux-assisted GTA welding of magnesium alloys , 2002 .

[16]  Pierluigi Mollicone,et al.  Simple thermo-elastic–plastic models for welding distortion simulation , 2006 .

[17]  H. Tsai,et al.  Modeling of the effects of surface-active elements on flow patterns and weld penetration , 2001 .

[18]  YuMing Zhang,et al.  Metal Transfer in Double-Electrode Gas Metal Arc Welding , 2007 .

[19]  R. Scott Funderburk,et al.  Key Concepts in Welding Engineering , 1999 .

[20]  P. Maropoulos,et al.  Effects of welding speed, energy input and heat source distribution on temperature variations in butt joint welding , 2005 .

[21]  T. R. Bement,et al.  Taguchi techniques for quality engineering , 1995 .

[22]  A. G. Olabi,et al.  Optimization of different welding processes using statistical and numerical approaches - A reference guide , 2008, Adv. Eng. Softw..