Theory of cyclic creep of concrete based on Paris law for fatigue growth of subcritical microcracks

Recent investigations prompted by a disaster in Palau revealed that worldwide there are 69 long-span segmental prestressed-concrete box-girder bridges that suffered excessive multi-decade deflections, while many more surely exist. Although the excessive deflections were shown to be caused mainly by obsolescence of design recommendations or codes for static creep, some engineers suspect that cyclic creep might have been a significant additional cause. Many investigators explored the cyclic creep of concrete experimentally, but a rational mathematical model that would be anchored in the microstructure and would allow extrapolation to a 100-year lifetime is lacking. Here it is assumed that the cause of cyclic creep is the fatigue growth of pre-existing microcracks in hydrated cement. The resulting macroscopic strain is calculated by applying fracture mechanics to the microcracks considered as either tensile or, in the form of a crushing band, as compressive. This leads to a mathematical model for cyclic creep in compression, which is verified and calibrated by laboratory test data from the literature. The cyclic creep is shown to be proportional to the time average of stress and to the 4th power of the ratio of the stress amplitude to material strength. The power of 4 is supported by the recent finding that, on the atomistic scale, the Paris law should have the exponent of 2 and that the exponent must increase due to scale bridging. Exponent 4 implies that cyclic creep deflections are enormously sensitive to the relative amplitude of the applied cyclic stress. Calculations of the effects of cyclic creep in six segmental prestressed concrete box girders indicate that, because of self-weight dominance, the effect on deflections absolutely negligible for large spans (>150m). For small spans (<40m) the cyclic creep deflections are not negligible but do not matter since the static creep causes in such bridges upward deflections. However, the cyclic creep is shown to cause in bridges with medium and small spans (<80m) a significant residual tensile strain which can produce deleterious tensile cracking at top or bottom face of the girder.

[1]  R. L'hermite.  Les déformations du béton , 1961 .

[2]  S. Nemat-Nasser,et al.  Compression‐induced nonplanar crack extension with application to splitting, exfoliation, and rockburst , 1982 .

[3]  G. I. Barenblatt,et al.  Similarity, Self-Similarity and Intermediate Asymptotics , 1979 .

[4]  A. Neville,et al.  Mechanism of Cyclic Creep of Concrete , 1978 .

[5]  Zdenek P. Bazant,et al.  Excessive Creep Deflections: An Awakening , 2011 .

[6]  H. Saunders,et al.  Advanced Fracture Mechanics , 1985 .

[7]  Zdenek P. Bazant,et al.  Size Effect in Fatigue Fracture of Concrete , 1991 .

[8]  Gene M. Nordby.  Fatigue of Concrete- A Review of Research* , 1958 .

[9]  F. Wittmann,et al.  Kriechverformung des Betons unter statischer und unter dynamischer Belastung , 1971 .

[10]  H. Jennings,et al.  The fatigue hardening behaviour of cement-based materials , 1979 .

[11]  Magazine of Concrete Research , 1964, Nature.

[12]  Koichi Maekawa,et al.  Cyclic Cumulative Damaging of Reinforced Concrete in Post-Peak Regions , 2004 .

[13]  C. Teitelboim.  RADIATION REACTION AS A RETARDED SELF-INTERACTION. , 1971 .

[14]  Zdenek P. Bazant,et al.  Fatigue Fracture of High-Strength Concrete and Size Effect , 1993 .

[15]  Qiang Yu,et al.  Pervasiveness of Excessive Segmental Bridge Deflections: Wake-Up Call for Creep , 2011 .

[16]  infolge des Schwingkriechens,et al.  Langzeitige Durchbiegungen Von Spannbetonbrucken Infolge Des Schwingkriechens Unter Verkehrslasten , .

[17]  P. Forsyth,et al.  Influence of frequency of cyclic load on creep of concrete , 1986 .

[18]  J. R. Ockendon,et al.  SIMILARITY, SELF‐SIMILARITY AND INTERMEDIATE ASYMPTOTICS , 1980 .

[19]  S. Suresh.  Fatigue of materials , 1991 .

[20]  Hiroshi Tada,et al.  The stress analysis of cracks handbook , 2000 .

[21]  R. Green,et al.  Sustained and Cyclic Loading of Concrete Columns , 1971 .

[22]  Qiang Yu,et al.  Excessive Long-Time Deflections of Prestressed Box Girders. II: Numerical Analysis and Lessons Learned , 2012 .

[23]  Z. P. Bažant,et al.  Practical prediction of time-dependent deformations of concrete , 1978 .

[24]  S. Suresh,et al.  Fatigue crack growth in cementitious materials under cyclic compressive loads , 1989 .

[25]  A. M. Neville,et al.  ACTIVATION ENERGY OF CREEP OF CONCRETE UNDER SHORT-TERM STATIC AND CYCLIC STRESSES , 1977 .

[26]  A. M. Neville,et al.  NON-ELASTIC DEFORMATION OF CONCRETE UNDER CYCLIC COMPRESSION , 1973 .

[27]  E. Schulson,et al.  Failure of columnar saline ice under biaxial compression: Failure envelopes and the brittle‐to‐ductile transition , 1995 .

[28]  Zdenek P. Bazant,et al.  Nano-mechanics based modeling of lifetime distribution of quasibrittle structures , 2009 .

[29]  A. Pandolfi,et al.  Bounding Surface Models Applied to Fatigue of Plain Concrete , 1998 .

[30]  Zdenek P. Bazant,et al.  SIZE EFFECT IN COMPRESSION FRACTURE: SPLITTING CRACK BAND PROPAGATION , 1997 .

[32]  M. Kachanov,et al.  A microcrack model of rock inelasticity part I: Frictional sliding on microcracks , 1982 .

[33]  Zdeněk P. Zažant,et al.  Improved prediction model for time-dependent deformations of concrete: Part 5 — Cyclic load and cyclic humidity , 1992 .

[34]  Lubin Gao,et al.  FATIGUE OF CONCRETE UNDER UNIAXIAL COMPRESSION CYCLIC LOADING , 1998 .

[35]  E. Buckingham.  On Physically Similar Systems; Illustrations of the Use of Dimensional Equations , 1914 .

[36]  C E Kesler,et al.  THE FATIGUE OF PLAIN CONCRETE , 1968 .

[37]  Martin Z. Bazant,et al.  Unified nano-mechanics based probabilistic theory of quasibrittle and brittle structures: I. Strength, static crack growth, lifetime and scaling , 2011 .

[38]  Zdenek P. Bazant,et al.  Creep and Shrinkage Prediction Model for Analysis and Design of Concretetructures: Model B3 , 2000, SP-194: The Adam Neville Symposium: Creep and Shrinkage-Structural Design Effects.

[39]  Jia-Liang Le,et al.  Modeling of mode-I fatigue crack growth in quasibrittle structures under cyclic compression , 2012 .

[40]  Qiang Yu,et al.  Wake-up call for creep, myth about size effect and black holes in safety: What to improve in fib model code draft , 2011 .

[41]  N. J. Gardner,et al.  Design Provisions for Drying Shrinkage and Creep of Normal-Strength Concrete , 2001 .

[42]  Qiang Yu,et al.  Excessive Long-Time Deflections of Prestressed Box Girders. I: Record-Span Bridge in Palau and Other Paradigms , 2012 .

[43]  W. Flügge.  Handbook of Engineering Mechanics , 1962 .

[44]  Michael F. Ashby,et al.  The failure of brittle porous solids under compressive stress states , 1986 .

[45]  P. C. Paris,et al.  A Critical Analysis of Crack Propagation Laws , 1963 .

[46]  Practical prediction of time-dependent deformations of concrete , 1978 .

[47]  S. D. Hallam,et al.  The failure of brittle solids containing small cracks under compressive stress states , 1986 .

[48]  E. W. Bennett,et al.  SOME FATIGUE TESTS OF HIGH-STRENGTH CONCRETE IN AXIAL COMPRESSION , 1967 .

[49]  G. I. Barenblatt.  Scaling: Self-similarity and intermediate asymptotics , 1996 .

[50]  F. Cornet,et al.  Rock Fracture And Fragmentation , 1981 .