Spheroidization Behavior of Nano-Primary Silicon Induced by Neodymium under High-Current Pulsed Electron Beam Irradiation

The spheroidization behavior of the nano-primary silicon phase induced by Nd under high-current pulsed electron beam (HCPEB) irradiation was investigated in this study. The study results revealed that, compared to the Al–17.5Si alloy, spheroidized nano-primary silicon phase emerged in the alloy’s HCPEB-irradiated surface layer due to the presence of Nd. Because Nd was abundantly enriched on the fast-growing silicon crystal plane, its surface tension was reduced under the extreme undercooling caused by HCPEB irradiation, causing the growth velocity of each crystal plane to be the same and spherical nanometers of silicon to appear. The spheroidization of nano-primary silicon phases occurred in the remelted layer. The microhardness test revealed that Nd could depress the microhardness of the Al matrix at the same number of pulses, but conversely increase the microhardness of the primary silicon phase, compared to the Al–17.5Si alloy. The tribological test showed that the presence of spherical nano-primary silicon could significantly improve the alloy’s tribological property.

[1]  Kui Li,et al.  The Influence of Neodymium Element on the Crater Structure Formed on Al-17.5Si Alloy Surface Processed by High-Current Pulsed Electron Beam , 2020 .

[2]  Wenhui Ma,et al.  Effects of silicon content on the separation and purification of primary silicon from hypereutectic aluminum–silicon alloy by alternating electromagnetic directional solidification , 2019, Separation and Purification Technology.

[3]  Z. Guo,et al.  Characterization of high-pressure die-cast hypereutectic Al-Si alloys based on microstructural distribution and fracture morphology , 2019, Journal of Materials Science & Technology.

[4]  R. Jamaati,et al.  Effect of ECAP on microstructure and tensile properties of A390 aluminum alloy , 2019, Transactions of Nonferrous Metals Society of China.

[5]  J. Shin,et al.  Si phase modification on the elevated temperature mechanical properties of Al-Si hypereutectic alloys , 2019, Materials Science and Engineering: A.

[6]  G. Tu,et al.  The effect of neodymium on the microcracks generated on the Al–17.5Si alloy surface treated by high current pulsed electron beam , 2016 .

[7]  G. Tu,et al.  The metastable structure of hypereutectic Al–17·5Si alloy surface induced by high current pulsed electron beam , 2015 .

[8]  J. Li,et al.  Nucleation and Growth of Eutectic Si in Al-Si Alloys with Na Addition , 2015, Metallurgical and Materials Transactions A.

[9]  T. Xia,et al.  Effect of rare earth cerium addition on the microstructure and tensile properties of hypereutectic Al–20%Si alloy , 2013 .

[10]  Pengting Li,et al.  Distribution of TiB2 particles and its effect on the mechanical properties of A390 alloy , 2012 .

[11]  C. Dong,et al.  Surface modification of Al–20Si alloy by high current pulsed electron beam , 2011 .

[12]  Z. Wang,et al.  Influence of High Current Pulsed Electron Beam (HCPEB) Treatment on Wear Resistance of Hypereutectic Al-17.5Si and Al-20Si Alloys , 2011 .

[13]  Yang Li,et al.  Effect of ultrasonic treatment on microstructures of hypereutectic Al-Si alloy , 2008 .

[14]  Liping Wang,et al.  Effects of Light and Heavy Rare Earths on Anti-Degradation of Nodular Cast Iron , 2006 .

[15]  Q. Jiang,et al.  Effect of new Al–P–Ti–TiC–Y modifier on primary silicon in hypereutectic Al–Si alloys , 2005 .

[16]  J. Y. Kim,et al.  Effect of rare earth element on microstructure formation and mechanical properties of thin wall ductile iron castings , 2004 .

[17]  N. Fatahalla,et al.  Effect of microstructure on the mechanical properties and fracture of commercial hypoeutectic Al-Si alloy modified with Na, Sb and Sr , 1999 .

[18]  T. M. Chandrashekharaiah,et al.  Studies on Relationship between Wear Behaviour and Microstructure of a Hypereutectic Al-Si Alloy , 2018 .

[19]  S. Sun,et al.  Halo evolution of hypereutectic Al-17.5Si alloy treated with high-current pulsed electron beam , 2015 .