Effect of Magnetic Orientation on the Microwave Absorption Properties for Planar-Anisotropy Ce2Fe17N3-δ Powders/Silicone Composite

The electromagnetic parameters of magnetic unoriented and oriented Ce2Fe17N3-δ powders/Silicone composite with 15 vol% were investigated in the 0.1–18 GHz range. It was found that the initial permeability increased from 2.78 to 3.6 as well as the optimal RL reached –61.3 dB with a thickness of 1.91 mm at 9.01 GHz for the composite after orientation. The microwave absorbing properties of oriented composite were greatly enhanced resulting from the perfect impedance match condition improved by rotational magnetic orientation. This novel rotational magnetic orientation method might provide a new way to design high performance microwave absorbers.

[1]  Run‐Wei Li,et al.  Microwave absorption properties of planar-anisotropy Ce2Fe17N3−δ powders/Silicone composite in X-band , 2017 .

[2]  Tao Wang,et al.  High-frequency electromagnetic properties of soft magnetic Nd2Co17 micron flakes fractured along c crystal plane with natural resonance frequency exceeding 10 GHz , 2016 .

[3]  Jianbo Wang,et al.  High-frequency electromagnetic properties of soft magnetic Y2Fe17Nx particles with easy-plane anisotropy , 2015 .

[4]  Xiaohu Ren,et al.  Electromagnetic and microwave absorbing properties of carbonyl iron/BaTiO3 composite absorber for matched load of isolator , 2015 .

[5]  Fashen Li,et al.  Synthesis and excellent electromagnetic wave absorption properties of parallel aligned FeCo@C core–shell nanoflake composites , 2015 .

[6]  Liyun Tang,et al.  Greatly enhanced microwave absorbing properties of planar anisotropy carbonyl-iron particle composites , 2015 .

[7]  W. Zuo,et al.  Microwave absorption properties of oriented Pr2Fe17N3−δ particles/paraffin composite with planar anisotropy , 2014 .

[8]  Tong Liu,et al.  Microporous Co@CoO nanoparticles with superior microwave absorption properties. , 2014, Nanoscale.

[9]  W. Zuo,et al.  Greatly enhanced permeability for planar anisotropy Ce2Fe17N3−δ compound with rotational orientation in various external magnetic fields , 2012 .

[10]  Fashen Li,et al.  Effect of shape of Fe3Al particles on their microwave permeability and absorption properties , 2011 .

[11]  W. Zuo,et al.  Complex permeability and microwave absorption properties of planar anisotropy Ce2Fe17N3−δ particles , 2011 .

[12]  Fashen Li,et al.  Investigation on peak frequency of the microwave absorption for carbonyl iron/epoxy resin composite , 2011 .

[13]  Fashen Li,et al.  Microwave reflection characteristics of surface-modified Fe50Ni50 fine particle composites , 2010 .

[14]  T. Kato,et al.  Performance of Z-type hexagonal ferrite core under demagnetizing and external static fields , 2010 .

[15]  Tao Wang,et al.  Microwave permeability of flake-shaped FeCuNbSiB particle composite with rotational orientation , 2010 .

[16]  L. P. Purohit,et al.  Modified composition of barium ferrite to act as a microwave absorber in X-band frequencies , 2010 .

[17]  S. Jacobo,et al.  Microwave-absorbing characteristics of epoxy resin composites containing nanoparticles of NiZn- and NiCuZn-ferrites , 2009 .

[18]  Yujie Feng,et al.  Microwave absorption properties of La doped barium titanate in X-band , 2009 .

[19]  Qiao Liang,et al.  Microwave Magnetic Properties of Nd2Fe17N3-δ with Planar Anisotropy , 2008 .

[20]  K. Rozanov.  Ultimate thickness to bandwidth ratio of radar absorbers , 2000 .

[21]  M. Matsumoto,et al.  Thin electromagnetic wave absorber for quasi-microwave band containing aligned thin magnetic metal particles , 1997 .

[22]  J. Coey,et al.  Magnetic properties of a new family of ternary rare‐earth iron nitrides R2Fe17N3−δ (invited) , 1991 .

[23]  J. L. Snoek.  Dispersion and absorption in magnetic ferrites at frequencies above one Mc/s , 1948 .