Effects of substrate temperature and annealing in air on optical properties of Ag films prepared by thermal evaporation

The effects of the substrate temperature and annealing in air on the structural and optical properties of Ag films have been studied. Ag films were prepared by thermal evaporation on glass substrates at different substrate temperatures (room temperature, 60 °C and 90 °C). Post-deposition annealing of the film was carried out at temperatures among 250 and 350 °C. Surface morphology of Ag film was observed by atomic force microscopy. Surface composition was detected by Raman spectra. Reflectance was measured by a double beam spectrophotometer. The results show that surface of the annealed films grown at higher substrate temperature is more oxidized. For the annealed film grown at 90 °C substrate temperature, the agglomeration seems to follow the grain boundary grooving process and size of islands increases with increasing annealing temperature. However, the annealed film grown at 60 °C substrate temperature agglomerates via nucleation of voids followed by the fractal growth of voids. It is found that the substrate temperature of the films will affect the agglomeration characteristic of the films annealed at different temperature in air, which results in the difference in the optical properties of the annealed films.

[1]  A. Takano,et al.  Highly Texturized Silver Electrode Deposition Using Roll-to-Roll Low-Temperature Sputtering Process , 2004 .

[2]  Y. J. Chen,et al.  Linear Ethanol Sensing of SnO2 Nanorods with Extremely High Sensitivity , 2006 .

[3]  Jow-Lay Huang,et al.  Effect of substrate temperature and annealing treatment on the electrical and optical properties of silver-based multilayer coating electrodes , 2006 .

[4]  A. Pal,et al.  Effect of particle shape distribution on the surface plasmon resonance of Ag–SiO2 nanocomposite thin films , 2003 .

[5]  T. Seong,et al.  Ohmic and degradation mechanisms of Ag contacts on p-type GaN , 2005 .

[6]  J. Spitz,et al.  Hillock formation, hole growth and agglomeration in thin silver films , 1980 .

[7]  Seok‐In Na,et al.  Thermally stable and highly reflective AgAl alloy for enhancing light extraction efficiency in GaN light-emitting diodes , 2006 .

[8]  Doris Schmitt-Landsiedel,et al.  Scaling properties and electromigration resistance of sputtered Ag metallization lines , 2001 .

[9]  V. Karoutsos,et al.  Growth of thin Ag films produced by radio frequency magnetron sputtering , 2006 .

[10]  Limei Lin,et al.  Thermal stability of Ag films in air prepared by thermal evaporation , 2007 .

[11]  T. Seong,et al.  Low-resistance and highly-reflective Zn–Ni solid solution/Ag ohmic contacts for flip-chip light-emitting diodes , 2003 .

[12]  T. Alford,et al.  Thickness dependence on the thermal stability of silver thin films , 2002 .

[13]  Shao Jianda,et al.  Influence of Cr interlayer on the structure and optical properties of Ag films on glass substrate by magnetron sputtering , 2006 .

[14]  Tae-Sik Yoon,et al.  Comparison of the agglomeration behavior of Au and Cu films sputter deposited on silicon dioxide , 2003 .

[15]  Yoshio Abe,et al.  Optical and electrical properties of pure Ag and Ag-based alloy thin films prepared by RF magnetron sputtering , 2002 .

[16]  Terry Alford,et al.  Improvement of the thermal stability of silver metallization , 2003 .

[17]  Sang-ki Chun,et al.  Characterization of the optical properties of silver nanoparticle films , 2007, Nanotechnology.

[18]  Terry Alford,et al.  Agglomeration and percolation conductivity , 2001 .