Application of laser in seam welding of dissimilar steel to aluminium joints for thick structural components

Abstract Laser welding-brazing technique, using a continuous wave (CW) fibre laser with 8000 W of maximum power, was applied in conduction mode to join 2 mm thick steel (XF350) to 6 mm thick aluminium (AA5083-H22), in a lap joint configuration with steel on the top. The steel surface was irradiated by the laser and the heat was conducted through the steel plate to the steel-aluminium interface, where the aluminium melts and wets the steel surface. The welded samples were defect free and the weld micrographs revealed presence of a brittle intermetallic compounds (IMC) layer resulting from reaction of Fe and Al atoms. Energy Dispersive Spectroscopy (EDS) analysis indicated the stoichiometry of the IMC as Fe2Al5 and FeAl3, the former with maximum microhardness measured of 1145 HV 0.025/10. The IMC layer thickness varied between 4 to 21 μm depending upon the laser processing parameters. The IMC layer showed an exponential growth pattern with the applied specific point energy (Esp) at a constant power density (PD). Higher PD values accelerate the IMC layer growth. The mechanical shear strength showed a narrow band of variation in all the samples (with the maximum value registered at 31.3 kN), with a marginal increase in the applied Esp. This could be explained by the fact that increasing the Esp results into an increase in the wetting and thereby the bonded area in the steel-aluminium interface.

[1]  Stewart Williams,et al.  Investigation of the effects of basic laser material interaction parameters in laser welding , 2012 .

[2]  F. Vollertsen,et al.  Effect of Thermal Cycle on the Formation of Intermetallic Compounds in Laser Welding of Aluminum-Steel Overlap Joints , 2011 .

[3]  Ranfeng Qiu,et al.  Interfacial microstructure and strength of steel/aluminum alloy joints welded by resistance spot welding with cover plate , 2009 .

[4]  Jamshid Sabbaghzadeh,et al.  DISSIMILAR WELDING OF CARBON STEEL TO 5754 ALUMINUM ALLOY BY ND:YAG PULSED LASER , 2010 .

[5]  Emil Schubert,et al.  Laser beam joining of material combinations for automotive applications , 1997, Other Conferences.

[6]  S. Shabestari,et al.  Microstructural analysis of interfacial reaction between molten aluminium and solid iron , 2002 .

[7]  P. Peyre,et al.  Steel to aluminium key-hole laser welding , 2007 .

[8]  Seung-Boo Jung,et al.  Interfacial reaction in steel–aluminum joints made by friction stir welding , 2006 .

[9]  Fehim Findik,et al.  Recent developments in explosive welding , 2011 .

[11]  Eugen Cicala,et al.  Dissimilar material joining using laser (aluminum to steel using zinc-based filler wire) , 2007 .

[12]  F. Botana,et al.  Laser welding of AA 5083 samples by high power diode laser , 2009 .

[13]  T. Yakou,et al.  Control of intermetallic compound layers at interface between steel and aluminum by diffusion-treatment , 2002 .

[14]  M. Kutsuna,et al.  Laser-roll welding of a dissimilar metal joint of low carbon steel to aluminium alloy using 2 kW fibre laser , 2009 .

[15]  Yoshiro Ito,et al.  Detection technique for transition between deep penetration mode and shallow penetration mode in CO2 laser welding of metals , 2000 .

[16]  T. Shih,et al.  Interaction of steel with pure Al, Al–7Si and A356 alloys , 2007 .

[17]  D. Yapp,et al.  Interaction time and beam diameter effects on the conduction mode limit , 2012 .

[18]  John C. Ion,et al.  Laser Processing of Engineering Materials: Principles, Procedure and Industrial Application , 2005 .

[19]  Jerry E. Gould,et al.  Dissimilar friction welding of 6061-T6 aluminum and AISI 1018 steel: Properties and microstructural characterization , 2010 .

[20]  Alexander Kaplan,et al.  The Application of Specific Point Energy Analysis to Laser Cutting with 1 μm Laser Radiation , 2014 .

[21]  F. Olsen.  Hybrid laser-arc welding , 2009 .

[22]  Mustafa Acarer,et al.  An investigation of mechanical and metallurgical properties of explosive welded aluminum–dual phase steel , 2008 .

[23]  Ranfeng Qiu,et al.  The influence of reaction layer on the strength of aluminum/steel joint welded by resistance spot welding , 2009 .

[24]  P. Peyre,et al.  Steel to aluminium braze welding by laser process with Al–12Si filler wire , 2008 .

[25]  K. P. Rao,et al.  Study on laser welding-brazing of zinc coated steel to aluminum alloy with a zinc based filler , 2011 .

[26]  F. Botana,et al.  Laser welding of aluminium alloys 5083 and 6082 under conduction regime , 2009 .

[27]  C. Iwamoto,et al.  Effect of interfacial reaction layer continuity on the tensile strength of resistance spot welded joints between aluminum alloy and steels , 2009 .

[28]  Clemens Wallmann,et al.  Fluxless laser beam joining of aluminium with zinc coated steel , 2005 .

[29]  F. Barbier,et al.  Intermetallic compound layer growth between solid iron and molten aluminium , 1998 .

[30]  A. Mekhrabov,et al.  The effect of substitutional impurities on the evolution of FeAl diffusion layer , 1998 .

[31]  Yoshiharu Mutoh,et al.  Suppression of intermetallic reaction layer formation by controlling heat flow in dissimilar joining of steel and aluminum alloy , 2007 .

[32]  C. Iwamoto,et al.  Interfacial characterization of joint between mild steel and aluminum alloy welded by resistance spot welding , 2010 .

[33]  M. Kutsuna,et al.  Joining of Aluminum Alloy 5052 and Low-Carbon Steel by Laser Roll Welding A combination of laser heating and roll welding is suggested to join aluminum Alloy 5052 and low-carbon steel sheets , 2004 .