X-ray tomography observation of crack propagation in nuclear graphite

Abstract X-ray microtomography has been used to investigate the mechanisms responsible for rising crack growth resistance with crack propagation (R curve behaviour) in polygranular nuclear graphite. Tomography can be used to observe changes in the crack shape with propagation, and a side grooved specimen has been developed to produce the planar straight fronted crack necessary for fracture toughness measurement. Crack bridging from frictional contact between the fracture surfaces is observed. A zone of reduced X-ray attenuation, attributed to microstructural damage, is also observed around the crack tip and in its wake. These are the first in situ observations of the mechanisms of the R curve behaviour in nuclear graphites.

[1]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[2]  E. Gdoutos,et al.  Fracture Mechanics , 2020, Encyclopedic Dictionary of Archaeology.

[3]  A. Evans,et al.  The mechanics of matrix cracking in brittle-matrix fiber composites , 1985 .

[4]  J. Rödel,et al.  Effect of geometry and electrical boundary conditions on R-curves for lead zirconate titanate ceramics , 2006 .

[5]  A. Evans,et al.  Fracture Mechanics of Ceramics , 1986 .

[6]  M. Inagaki,et al.  R‐Curve Behavior of a Polycrystalline Graphite: Microcracking and Grain Bridging in the Wake Region , 1988 .

[7]  M. Sakai,et al.  Size-effect on the fracture toughness and the R-curve of carbon materials , 1996 .

[8]  B. Kelly,et al.  IRRADIATION DAMAGE TO PILE GRADE GRAPHITE AT 450 C , 1962 .

[9]  G. Neighbour,et al.  Crack growth resistance in nuclear graphites , 2002 .

[10]  M. Inagaki,et al.  Energy Principle of Elastic-Plastic Fracture and Its Application to the Fracture Mechanics of a Polycrystalline Graphite , 1983 .

[11]  V. Alekseev,et al.  Radiation damage of graphite and carbon-graphite materials , 1995 .

[12]  G. Fantozzi,et al.  Fracture behaviour of carbon materials , 1991 .

[13]  B. Kelly.  The theory of irradiation damage in graphite , 1977 .

[14]  V. Luprano,et al.  Scanning Acoustic Microscopy Observations of High‐Temperature Crack‐Bridging Mechanisms in Alumina , 1993 .

[15]  P. Hariharan,et al.  Holographic and Speckle Interferometry , 2007 .

[16]  A. Evans,et al.  Crack‐Growth Resistance of Microcracking Brittle Materials , 2006 .

[17]  Timothy D. Burchell,et al.  A microstructurally based fracture model for polygranular graphites , 1996 .

[18]  L. Rose.  Effective Fracture Toughness of Microcracked Materials , 1986 .