论文信息 - CORROSION OF AMORPHOUS AND NANOCRYSTALLINE Fe-BASED ALLOYS IN NaCl AND H2SO4 SOLUTIONS

CORROSION OF AMORPHOUS AND NANOCRYSTALLINE Fe-BASED ALLOYS IN NaCl AND H2SO4 SOLUTIONS

Corrosion resistance of nanocrystalline Fe73.5Si13.5B9Nb3Cu1 alloy was investigated and compared to its amorphous counterpart. Low-temperature crystallization occurred during the annealing of amorphous tapes was used to obtain a nanocrystalline structure. The influence of annealing condition on the structure and corrosion resistance of the alloy in NaCl and H2SO4 solutions was investigated. Based on the testing results, it was found that nanocrystalline tapes have higher corrosion resistance than amorphous counterpart and H2SO4 can promote the occurrence of corrosion compared with NaCl.

W. Lu | B. Yan | Xiang Li | Yuxin Wang | Deng Pan

[1] S. E. Franklin,et al. Characterization of gas-nitrided austenitic steel with an amorphous/nanocrystalline top layer , 2008 .

[2] G. Nawrat,et al. Corrosion of amorphous and nanocrystalline Fe-based alloys and its influence on their magnetic behavior , 2007 .

[3] M. Delamar,et al. Influence of nickel content on the electrochemical behavior of Finemet type amorphous and nanocrystalline alloys , 2007 .

[4] B. S. Murty,et al. Electrochemical behavior of multicomponent amorphous and nanocrystalline Zr-based alloys in different environments , 2006 .

[5] A. Baron,et al. Electrochemical corrosion and its influence on magnetic properties of Fe75.5Si13.5B9Nb3Cu1 alloy , 2005 .

[6] C. Kiminami,et al. Influence of the corrosion on the saturation magnetic density of amorphous and nanocrystalline Fe73Nb3Si15.5B7.5Cu1 and Fe80Zr3.5Nb3.5B12Cu1 alloys , 2002 .

[7] V. Cremaschi,et al. Electrochemical studies of amorphous, nanocrystalline, and crystalline FeSiB based alloys , 2002 .

[8] Y. Yoshizawa,et al. New Fe-based soft magnetic alloys composed of ultrafine grain structure , 1988 .