Abstract The chloride ion (Cl − ) is known as an aggressive species in the aqueous solutions that adsorbs to the imperfect sites on the metal surfaces, such as defects, impurities and second-phase particles. This adsorption process could change the chemical composition and properties, such as ion conductivity, of the passive film. As a result, the passive film becomes less protective and breaks down at some places where the underlying metals are exposed to the electrolyte and dissolved through anodic reaction forming a pit. In the meantime, the hydrolysis (cathodic reaction) occurs inside the pit giving rise to a lower pH and leading to an increased dissolution rate of the metals. Subsequently, more chloride ions migrate into the pit in order to maintain electrical neutrality and adsorb onto the pit surface. The repeating of such process causes the pitting propagation. However, anodic polarization allows the chloride ions to migrate into the passive film more easily. With growth of the pit, more corrosion products make both in plane diffusion across the sample surface and out-of-plane diffusion to bulk solution from the pit mouth [M.G. Fontana, N.D. Greene, Corrosion Engineering, second ed., McGraw-Hill, New York, 1978].
[1]
K. Habib,et al.
Detection of crevice corrosion of steels in seawater by optical interferometry
,
2000
.
[2]
K. Habib,et al.
Detection of localized corrosion of stainless steels by optical interferrometry
,
1999
.
[3]
D. Mayorga-Cruz,et al.
Evaluation of corrosion in electrochemical systems using Michelson interferometry
,
2007
.
[4]
K. Habib,et al.
Holographic interferometry as electrochemical emission spectroscopy of a carbon steel in 5–20 ppm TROS C-70 inhibited seawater
,
2002
.
[5]
Shenhao Chen,et al.
Digital holographic study of the effect of magnetic field on the potentiostatic current oscillations of iron in sulfuric acid
,
2006
.
[6]
David E. Williams,et al.
Metallurgy (communication arising): Stainless-steel corrosion and MnS inclusions
,
2003,
Nature.