Dynamic response and damage modeling of glass/epoxy tubular structures: Numerical investigation

This paper presents a finite element analysis of static and dynamic tests on thick filament wound glass/epoxy tubes. The first part deals with the validation of elastic properties and identification of damage initiation and its development in dynamic tests. The FEA results of the quasi-static and dynamic tests resulting in no damage appeared satisfactory. The second part of the paper is concerned with an impact model, including material property degradation, used for damage prediction. Simulated damage is compared with that obtained experimentally. The sizes of projected and cumulated surfaces are of the same order of magnitude as in the experimental measurements. The improved understanding of these phenomena and the development of predictive tools are part of an ongoing effort to improve the long-term integrity of composite structures for underwater applications.

[1]  S. R. Swanson,et al.  Analysis of Simply-Supported Orthotropic Cylindrical Shells Subject to Lateral Impact Loads , 1990 .

[2]  Peter Davies,et al.  Prediction of Damage in Composite Cylinders After Impact , 2005 .

[3]  G. Sih,et al.  Mathematical theories of brittle fracture. , 1968 .

[4]  Anthony M. Waas,et al.  Impact response of cylindrically curved laminates including a large deformation scaling study , 1998 .

[5]  N. Iyengar,et al.  Progressive failure of symmetric laminates under in-plane shear : I-positive shear , 1998 .

[6]  G. I. Barenblatt.  THE MATHEMATICAL THEORY OF EQUILIBRIUM CRACKS IN BRITTLE FRACTURE , 1962 .

[7]  Kenneth E. Evans,et al.  Failure mechanisms during the transverse loading of filament-wound pipes under static and low velocity impact conditions , 1992 .

[8]  F. Chang,et al.  A Progressive Damage Model for Laminated Composites Containing Stress Concentrations , 1987 .

[9]  R Ambur Damodar,et al.  Analytical Prediction of Damage Growth in Notched Composite Panels Loaded in Axial Compression , 1999 .

[10]  A. Needleman.  An analysis of tensile decohesion along an interface , 1990 .

[11]  V. Tvergaard.  Effect of fibre debonding in a whisker-reinforced metal , 1990 .

[12]  Peter Davies,et al.  Damage development in thick composite tubes under impact loading and influence on implosion pressure: experimental observations , 2005 .

[13]  R. K. Mittal,et al.  Impact response and damage in laminated composite cylindrical shells , 2003 .

[14]  Fu-Kuo Chang,et al.  A Model for Predicting Damage in Graphite/Epoxy Laminated Composites Resulting from Low-Velocity Point Impact , 1992 .

[15]  Serge Abrate,et al.  Impact on Composite Structures: Frontmatter , 1998 .

[16]  J. N. Reddy,et al.  Three-Dimensional Finite Element Progressive Failure Analysis of Composite Laminates Under Axial Extension , 1993 .

[17]  A. A. Griffith.  The Phenomena of Rupture and Flow in Solids , 1921 .

[18]  K. Chandrashekhara,et al.  Nonlinear Impact Analysis of Laminated Cylindrical and Doubly Curved Shells , 1995 .

[19]  Mn Nahas,et al.  Survey of Failure and Post-Failure Theories of Laminated Fiber-Renforced Composites , 1986 .

[20]  M. Kanninen,et al.  A finite element calculation of stress intensity factors by a modified crack closure integral , 1977 .

[21]  Nam Seo Goo,et al.  The effect of curvature on the dynamic response and impact-induced damage in composite laminates , 1997 .

[22]  C. Dávila,et al.  Analytical prediction of damage growth in notched composite panels loaded in compression , 2000 .

[23]  M. Tarfaoui,et al.  Scale and Size Effects on Dynamic Response and Damage of Glass/Epoxy Tubular Structures , 2007 .

[24]  Z. Hashin.  Failure Criteria for Unidirectional Fiber Composites , 1980 .

[25]  Anthony M. Waas,et al.  On the response of curved laminated panels subjected to transverse impact loads , 1999 .