Probabilistic analysis of aircraft gas turbine disk life and reliability

Two series of low-cycle-fatigue (LCF) test data for two different groups of aircraft gas turbine engine compressor disk geometries were reanalyzed and compared by using Weibull statistics. Both groups of disks were manufactured from titanium (Ti-6AI-4V) alloy. A probabilistic computer code called Probable Cause was used to predict disk life and reliability. A material-life factor A was determined for the titanium (Ti-6AI-4V) alloy by using fatigue disk data and was applied to predict disk life as a function of speed. A comparison was made with results from the currently used life prediction method, which is based on crack growth rate. Applying an endurance limit to the computer code did not significantly affect the predicted lives under engine operating conditions. Failure location predictions correlated with experimentally observed failure locations in the LCF tests. A reasonable correlation was obtained between the disk lives predicted by using the Probable Cause code and those predicted by using a modified crack growth method. Both methods slightly overpredicted life for one disk group and significantly underpredicted it for the other.

[1]  Erwin V. Zaretsky,et al.  Effect of Design Variables, Temperature Gradients, and Speed on Life and Reliability of a Rotating Disk , 1989 .

[2]  John Gannon,et al.  Getting the most from turbine flowmeters , 1994 .

[3]  W. Weibull,et al.  The phenomenon of rupture in solids , 1939 .

[4]  Erwin Y. Zaretsky.  Fatigue criterion to system design, life and reliability , 1985 .

[5]  Erwin V. Zaretsky,et al.  Incorporating finite element analysis into component life and reliability , 1993 .

[6]  Jennifer K. Chalsma,et al.  Design for life, plan for death , 1994 .

[7]  Erwin V. Zaretsky,et al.  Probabilistic Failure Prediction of SCS-6/Ti-15-3 MMC Ring , 1998 .

[8]  John P. Gyekenyesi,et al.  Designing ceramic components with the CARES computer program , 1989 .

[9]  Salvatore J. Grisaffe.  Analysis of shear bond strength of plasma- sprayed alumina coatings on stainless steel , 1965 .

[10]  W. J. Anderson,et al.  The Effect of Contact Angle on Rolling-Contact Fatigue and Bearing Load Capacity , 1962 .

[11]  Thomas L Carter.  Preliminary studies of rolling-contact fatigue life of high-temperature bearing materials , 1958 .

[12]  T. A. Harris,et al.  A New Fatigue Life Model for Rolling Bearings , 1985 .

[13]  W. Weibull.  A statistical theory of the strength of materials , 1939 .

[14]  R. Mahorter,et al.  Life prediction methodology for aircraft gas turbine engine disks , 1985 .

[15]  Erwin V. Zaretsky,et al.  A. Palmgren Revisited-A Basis for Bearing Life Prediction , 1997 .

[16]  W. Weibull.  A Statistical Distribution Function of Wide Applicability , 1951 .