Printability of calcium phosphate: calcium sulfate powders for the application of tissue engineered bone scaffolds using the 3D printing technique.

In this study, calcium phosphate (CaP) powders were blended with a three-dimensional printing (3DP) calcium sulfate (CaSO4)-based powder and the resulting composite powders were printed with a water-based binder using the 3DP technology. Application of a water-based binder ensured the manufacture of CaP:CaSO4 constructs on a reliable and repeatable basis, without long term damage of the printhead. Printability of CaP:CaSO4 powders was quantitatively assessed by investigating the key 3DP process parameters, i.e. in-process powder bed packing, drop penetration behavior and the quality of printed solid constructs. Effects of particle size, CaP:CaSO4 ratio and CaP powder type on the 3DP process were considered. The drop penetration technique was used to reliably identify powder formulations that could be potentially used for the application of tissue engineered bone scaffolds using the 3DP technique. Significant improvements (p<0.05) in the 3DP process parameters were found for CaP (30-110 μm):CaSO4 powders compared to CaP (<20 μm):CaSO4 powders. Higher compressive strength was obtained for the powders with the higher CaP:CaSO4 ratio. Hydroxyapatite (HA):CaSO4 powders showed better results than beta-tricalcium phosphate (β-TCP):CaSO4 powders. Solid and porous constructs were manufactured using the 3DP technique from the optimized CaP:CaSO4 powder formulations. High-quality printed constructs were manufactured, which exhibited appropriate green compressive strength and a high level of printing accuracy.

[1]  Jintamai Suwanprateeb,et al.  Effect of binder content on the material properties of polymethyl methacrylate fabricated by three dimensional printing technique , 2008 .

[2]  S. Milz,et al.  Hydroxyapatite scaffolds for bone tissue engineering made by 3D printing , 2005, Journal of materials science. Materials in medicine.

[3]  Mark A. Ganter,et al.  A review of process development steps for new material systems in three dimensional printing (3DP) , 2008 .

[4]  Y. Greish.  Phase evolution during the low temperature formation of calcium-deficient hydroxyapatite–gypsum composites , 2011 .

[5]  D. Hutmacher,et al.  Scaffold development using 3D printing with a starch-based polymer , 2002 .

[6]  Youxin Hu,et al.  Mechanical characteristics of solid-freeform-fabricated porous calcium polyphosphate structures with oriented stacked layers. , 2011, Acta biomaterialia.

[7]  V. Rudolph,et al.  Interparticle van der Waals force in powder flowability and compactibility. , 2004, International journal of pharmaceutics.

[8]  K. Lu,et al.  3DP process for fine mesh structure printing , 2008 .

[9]  M Bohner,et al.  Structural and material approaches to bone tissue engineering in powder-based three-dimensional printing. , 2011, Acta biomaterialia.

[10]  Scott C. Brown,et al.  A three-dimensional osteochondral composite scaffold for articular cartilage repair. , 2002, Biomaterials.

[11]  Jake E. Barralet,et al.  3D Powder Printing of β‐Tricalcium Phosphate Ceramics Using Different Strategies , 2008 .

[12]  E. Fernández,et al.  Characterization of a novel calcium phosphate/sulphate bone cement. , 2002, Journal of biomedical materials research.

[13]  D. Bradford,et al.  Calcium sulfate- and calcium phosphate-based bone substitutes. Mimicry of the mineral phase of bone. , 1999, The Orthopedic clinics of North America.

[14]  H. Seitz,et al.  Three-dimensional printing of porous ceramic scaffolds for bone tissue engineering. , 2005, Journal of biomedical materials research. Part B, Applied biomaterials.

[15]  F. Petzoldt,et al.  Effect of production parameters on the properties of IN 718 superalloy by three-dimensional printing , 2008 .

[16]  Nicholas Dunne,et al.  Effects of Heat Treatment on the Mechanical and Degradation Properties of 3D-Printed Calcium-Sulphate-Based Scaffolds , 2013 .

[17]  A. Coetzee.  Regeneration of bone in the presence of calcium sulfate. , 1980, Archives of otolaryngology.

[18]  I. Hutchings,et al.  Inkjet printing - the physics of manipulating liquid jets and drops , 2008 .

[19]  Kriskrai Sitthiseripratip,et al.  3D printing of hydroxyapatite: Effect of binder concentration in pre-coated particle on part strength , 2007 .

[20]  K. Lu,et al.  Effect of particle size on three dimensional printed mesh structures , 2009 .

[21]  G. Walker,et al.  Static and Dynamic Degradation of Sintered Calcium Phosphate Ceramics , 2011 .

[22]  Christian Bergmann,et al.  3D printing of bone substitute implants using calcium phosphate and bioactive glasses , 2010 .

[23]  J. Litster,et al.  Drop penetration into porous powder beds. , 2002, Journal of colloid and interface science.

[24]  N. Dunne,et al.  In vitro study investigating the mechanical properties of acrylic bone cement containing calcium carbonate nanoparticles , 2008, Journal of materials science. Materials in medicine.

[25]  M. Zilberman.  Active implants and scaffolds for tissue regeneration , 2011 .

[26]  Ralph Müller,et al.  Printability of calcium phosphate powders for three-dimensional printing of tissue engineering scaffolds. , 2012, Acta biomaterialia.

[27]  Julia Will,et al.  Porous ceramic bone scaffolds for vascularized bone tissue regeneration , 2008, Journal of materials science. Materials in medicine.

[28]  M. Klein,et al.  Comparative Study of patient individual implants from β‐tricalcium phosphate made by different techniques based on CT data , 2006 .

[29]  L. Zichner,et al.  Nanocrystalline hydroxyapatite and calcium sulphate as biodegradable composite carrier material for local delivery of antibiotics in bone infections. , 2005, Biomaterials.

[30]  R. V. Hille,et al.  Aspects of gypsum precipitation in scaling waters , 2004 .

[31]  D. Brabazon,et al.  Effect of Saturation and Post Processing on 3D Printed Calcium Phosphate Scaffolds , 2008 .

[32]  Hermann Seitz,et al.  Bioceramic Granulates for use in 3D Printing: Process Engineering Aspects , 2006 .

[33]  M. Tunney,et al.  In vitro study of the efficacy of acrylic bone cement loaded with supplementary amounts of gentamicin: Effect on mechanical properties, antibiotic release, and biofilm formation , 2007, Acta orthopaedica.

[34]  J. Borrelli,et al.  Treatment of Nonunions and Osseous Defects With Bone Graft and Calcium Sulfate , 2003, Clinical orthopaedics and related research.

[35]  W. Zhou,et al.  A novel injectable and degradable calcium phosphate/calcium sulfate bone cement , 2011 .

[36]  A. Zima,et al.  New bone implant material with calcium sulfate and Ti modified hydroxyapatite , 2010 .

[37]  Abraham Marmur,et al.  The radial capillary , 1988 .

[38]  Amy J Wagoner Johnson,et al.  A review of the mechanical behavior of CaP and CaP/polymer composites for applications in bone replacement and repair. , 2011, Acta biomaterialia.

[39]  L. Peltier,et al.  The Use of Plaster of Paris to Fill Defects in Bone , 1957, Annals of surgery.

[40]  M. De Luca,et al.  Comparison of calcium sulfate and autogenous bone graft to bioabsorbable membranes plus autogenous bone graft in the treatment of intrabony periodontal defects: a split-mouth study. , 2001, Journal of periodontology.

[41]  Jintamai Suwanprateeb,et al.  Influence of raw powder preparation routes on properties of hydroxyapatite fabricated by 3D printing technique , 2010 .

[42]  Gabriele Grimm,et al.  Development of a new calcium phosphate powder-binder system for the 3D printing of patient specific implants , 2007, Journal of materials science. Materials in medicine.

[43]  Sadegh Rahmati,et al.  Perusing piezoelectric head performance in a new 3-D printing design , 2009 .