Characterisation of nano-sized Al–Mn–(Mg) particles in AZ91 and their effect on Mg17Al12 precipitation

Al–Mn–(Mg) particles in the size range of 20–200 nm have been found in a sand cast AZ91 magnesium alloy. Their morphologies, chemical composition and structures were investigated using transmission electron microscopy. It was found that these particles have a chemical composition of (Al6.52Mn)1−xMgx (x < 0.13) and a decagonal quasi-crystalline structure. These particles were stable during a solution treatment at 420 °C for 72 h and acted as preferential nucleation sites for Mg17Al12 precipitates during the subsequent ageing. The potential effect of these Al–Mn–(Mg) particles on the strengthening of AZ91 magnesium alloys is discussed.

[1]  A. Singh,et al.  Strengthening in magnesium alloys by icosahedral phase , 2005 .

[2]  E. Fleury,et al.  Formation of quasicrystalline phases in Al-rich Al–Mn–Be alloys , 2004 .

[3]  V. Gertsman,et al.  Microstructure and second-phase particles in low- and high-pressure die-cast magnesium alloy AM50 , 2005 .

[4]  H. I. Laukli,et al.  Divorced eutectic in a HPDC magnesium–aluminum alloy , 2004 .

[5]  A. Inoue,et al.  Microstructure of Rapidly Solidified Al–V–Ce–M (M=Fe, Co or Ni) High Strength Alloys Containing High Volume Fraction of Fine Icosahedral Precipitation , 1995 .

[6]  S. Celotto.  TEM study of continuous precipitation in Mg–9 wt%Al–1 wt%Zn alloy , 2000 .

[7]  D. StJohn,et al.  Effect of manganese on grain refinement of Mg–Al based alloys , 2006 .

[8]  M. Nakamura,et al.  Quasicrystal strengthened Mg-Zn-Y alloys by extrusion , 2003 .

[9]  A. Inoue,et al.  Fabrications and mechanical properties of bulk amorphous, nanocrystalline, nanoquasicrystalline alloys in aluminum-based system , 2001 .

[10]  D. Dubé,et al.  Characterization of Al-Mn particles in AZ91D investment castings , 2007 .

[11]  Yoshio Saito,et al.  Transition temperature to crystal phase of Al86Mn14 quasicrystal ultrafine particles determined by direct observation and characterization of surface oxide layer , 2005 .

[12]  M. Nakamura,et al.  Nanoprecipitates of icosahedral phase in quasicrystal-strengthened Mg-Zn-Y alloys , 2003 .

[13]  Z. Stadnik.  Physical Properties of Quasicrystals , 1999 .

[14]  Akihisa Inoue,et al.  High-strength aluminum alloys containing nanoquasicrystalline particles , 2000 .

[15]  A. Inoue,et al.  High-strength aluminum- and zirconium-based alloys containing nanoquasicrystalline particles , 2000 .

[16]  J. Cahn,et al.  Metallic Phase with Long-Range Orientational Order and No Translational Symmetry , 1984 .

[17]  W. Steurer.  Why are quasicrystals quasiperiodic? , 2012, Chemical Society reviews.

[18]  A. Luo,et al.  Cast magnesium alloys for elevated temperature applications , 1994 .

[19]  A. Inoue,et al.  Microstructure and Mechanical Properties of Rapidly Solidified Al–Cr–Ce–M (M=Transition Metal) Alloys Containing High Volume Fraction of the Icosahedral Phase , 1995 .

[20]  W. Liang,et al.  Effect of Mg-based spherical quasicrystals on microstructure and mechanical properties of AZ91 alloys , 2008 .

[21]  L. Bendersky.  Quasicrystals and quasicrystal-related phases in the AlMn system☆ , 1988 .

[22]  D. Bae,et al.  Application of quasicrystalline particles as a strengthening phase in Mg–Zn–Y alloys , 2002 .

[23]  R. Schmid-Fetzer,et al.  The influence of manganese on the microstructure and mechanical properties of AZ31 gravity die cast alloys , 2006 .