A poly(lactic acid)/calcium metaphosphate composite for bone tissue engineering.

A new method to prepare PLA/CMP (poly-L-lactide/calcium metaphosphate) composite scaffolds was developed for effective bone tissue engineering. This novel sintering method is composed of pressing the mixture of PLA, CMP, and salt particles at 150 MPa for 3 min followed by heat treatment at 210 degrees C for 30 min. The scaffolds had a homogeneously interconnected porous structure without a skin layer, and they exhibited a narrower pore size distribution and higher mechanical strength in comparison with scaffolds made by a solvent casting method. The scaffolds were seeded by osteoblasts and cultured in vitro or implanted into nude mice subcutaneously for up to 5 weeks. The number of cells attached to and proliferated on the scaffolds at both in vitro and in vivo was in the order of; PLA by novel sintering < PLA/CMP by solvent casting < PLA/CMP by novel sintering. In addition, the alkaline phosphatase activity of and calcium deposition in the scaffolds explanted from mice were enhanced significantly for the scaffolds by novel sintering compared to them by solvent casting. The in vitro results agreed well with the in vivo data. Such a superior characteristic of the novel sintering method should have resulted from the fact that the CMP particles could contact directly with cells/tissues to stimulate the cell proliferation and osteogenic differentiation, while the CMP particles would be coated by polymers and hindered to interact with cells/tissues in the case of a solvent casting method. As the novel sintering method does not use any solvents it offers another advantage to avoid problems associated with solvent residue.

[1]  H R Allcock,et al.  A highly porous 3-dimensional polyphosphazene polymer matrix for skeletal tissue regeneration. , 1996, Journal of biomedical materials research.

[2]  A. Mikos,et al.  Marrow stromal osteoblast function on a poly(propylene fumarate)/beta-tricalcium phosphate biodegradable orthopaedic composite. , 2000, Biomaterials.

[3]  B. Schmidt-Rohlfing,et al.  Stimulation of bone formation with an in situ setting tricalcium phosphate/rhBMP-2 composite in rats. , 2003, Journal of biomedical materials research. Part A.

[4]  A. Mikos,et al.  Effect of osteoblastic culture conditions on the structure of poly(DL-lactic-co-glycolic acid) foam scaffolds. , 1999, Tissue engineering.

[5]  Byung-Soo Kim,et al.  Manufacture of elastic biodegradable PLCL scaffolds for mechano-active vascular tissue engineering , 2004, Journal of biomaterials science. Polymer edition.

[6]  S. Cook,et al.  The effect of recombinant human osteogenic protein-1 on healing of large segmental bone defects. , 1994, The Journal of bone and joint surgery. American volume.

[7]  Antonios G Mikos,et al.  Flow perfusion culture of marrow stromal osteoblasts in titanium fiber mesh. , 2003, Journal of biomedical materials research. Part A.

[8]  C T Laurencin,et al.  A novel amorphous calcium phosphate polymer ceramic for bone repair: I. Synthesis and characterization. , 2001, Journal of biomedical materials research.

[9]  Lichun Lu,et al.  Synthetic bone substitutes , 2000 .

[10]  M. B. Claase,et al.  Porous PEOT/PBT scaffolds for bone tissue engineering: preparation, characterization, and in vitro bone marrow cell culturing. , 2002, Journal of biomedical materials research. Part A.

[11]  Min Wang,et al.  Developing bioactive composite materials for tissue replacement. , 2003, Biomaterials.

[12]  L. Weiss,et al.  In vitro analysis of biodegradable polymer blend/hydroxyapatite composites for bone tissue engineering. , 1999, Journal of biomedical materials research.

[13]  Cato T Laurencin,et al.  Three-dimensional, bioactive, biodegradable, polymer-bioactive glass composite scaffolds with improved mechanical properties support collagen synthesis and mineralization of human osteoblast-like cells in vitro. , 2003, Journal of biomedical materials research. Part A.

[14]  Robert Langer,et al.  Preparation and characterization of poly(l-lactic acid) foams , 1994 .

[15]  Jan Feijen,et al.  Porous polymeric structures for tissue engineering prepared by a coagulation, compression moulding and salt leaching technique. , 2003, Biomaterials.

[16]  M. Falk,et al.  Factors influencing synthesis and mineralization of bone matrix from fetal bovine bone cells grown in vitro , 1992, Journal of bone and mineral research : the official journal of the American Society for Bone and Mineral Research.

[17]  Cato T. Laurencin,et al.  Advancements in tissue engineered bone substitutes , 1999 .

[18]  A. Schilling,et al.  Biologically and chemically optimized composites of carbonated apatite and polyglycolide as bone substitution materials. , 2001, Journal of biomedical materials research.

[19]  Y. M. Lee,et al.  Tissue-engineered growth of bone by marrow cell transplantation using porous calcium metaphosphate matrices. , 2001, Journal of biomedical materials research.

[20]  K E Healy,et al.  Kinetics of bone cell organization and mineralization on materials with patterned surface chemistry. , 1996, Biomaterials.

[21]  Minna Kellomäki,et al.  Tissue reactions of subcutaneously implanted mixture of ε-caprolactone-lactide copolymer and tricalcium phosphate. An electron microscopic evaluation in sheep , 2003, Journal of materials science. Materials in medicine.

[22]  Byung-Soo Kim,et al.  Thermally produced biodegradable scaffolds for cartilage tissue engineering. , 2004, Macromolecular bioscience.

[23]  B. W. Schreurs,et al.  Time-dependent mechanical properties of HA/TCP particles in relation to morsellized bone grafts for use in impaction grafting. , 2001, Journal of biomedical materials research.

[24]  D. Williams,et al.  Fundamental aspects of biocompatibility , 1981 .

[25]  J. Vacanti,et al.  Tissue-engineered growth of bone and cartilage. , 1993, Transplantation proceedings.