A versatile strategy towards semi-interpenetrating polymer network for proton exchange membranes

Abstract A universal method to prepare proton exchange membrane (PEM) with semi-interpenetrating polymer network (semi-IPN) via a versatile crosslinker 1,3-benzenedisulfonyl azide (1,3-BDSA) is proposed. Sulfonyl azide groups can react with any polymer with carbon-hydrogen bonds via hydrogen abstraction. Polyvinylidene fluoride (PVDF) and perfluorosulfonic acid (PFSA) polymer are selected as two precursors for semi-IPN. When 1,3-BDSA is heated to a sufficiently high temperature it can form the nitrene and connect with PVDF via hydrogen abstraction reaction, recombination, or CH-bond insertion. The crosslinking structure of PVDF is formed, and semi-IPN is constructed in the presence of PFSA at the same time. The mechanical properties, degree of crosslinking, water uptake, and proton conductivity of semi-IPN membranes are investigated. Compared with pure PFSA membrane, the mechanical properties and the dimensional stability of the semi-IPN membranes are improved significantly. The tensile strength of the composite membrane (27.2 MPa) is much higher than that of PFSA membrane (10.1 MPa). The maximum power density of the composite membrane can reach 382 mW cm −2 at 940 mA cm −2 . Sulfonyl azide based crosslinkers can be used to prepare semi-IPN or IPN PEMs from any paired polymers with carbon–hydrogen bonds.

[1]  D. Wan,et al.  Proton exchange membranes based on semi-interpenetrating polymer networks of Nafion and poly(vinyl , 2011 .

[2]  D. Baker,et al.  Synthesis and characterization of some disulfonyl azides as potential crosslinking agents for textile fibers , 2001 .

[3]  H. Doğan,et al.  Sulfonated PEEK and fluorinated polymer based blends for fuel cell applications: Investigation of th , 2010 .

[4]  H. R. Kunz,et al.  Chemically-modified Nafion®/poly(vinylidene fluoride) blend ionomers for proton exchange membrane fuel cells , 2003 .

[5]  X. Jian,et al.  Synthesis of fluoro-containing sulfonated poly(phthalazinone ether ketone ketone)s and their properties as PEM in PEMFC and DMFC , 2009 .

[6]  G. C. Sarti,et al.  Gas permeation in perflurosulfonated membranes: Influence of temperature and relative humidity , 2013 .

[7]  P. Björnbom,et al.  Electrochemical characterization of PVDF-based proton conducting membranes for fuel cells , 1998 .

[8]  L. Hong,et al.  Semi-interpenetrating polymer network proton exchange membranes with narrow and well-connected hydrophilic channels , 2013 .

[9]  P. Ekdunge,et al.  Oxygen and hydrogen permeation properties and water uptake of Nafion® 117 membrane and recast film for PEM fuel cell , 1997 .

[10]  Lidan Lou,et al.  Preparation and properties of proton exchange membranes based-on Nafion® and phosphonic acid-functionalized hollow silica spheres , 2011 .

[11]  D. Wan,et al.  A facile crosslinking method of polybenzimidazole with sulfonyl azide groups for proton conducting membranes , 2012 .

[12]  L. Klein,et al.  Methods for modifying proton exchange membranes using the sol–gel process , 2005 .

[13]  Arumugam Manthiram,et al.  Nafion-impregnated electrospun polyvinylidene fluoride composite membranes for direct methanol fuel cells , 2008 .

[14]  E. Quartarone,et al.  PVDF and P(VDF-HFP)-based proton exchange membranes , 2004 .

[15]  H. Pu,et al.  Polymer nanoparticles via intramolecular crosslinking of sulfonyl azide functionalized polymers , 2011 .

[16]  Suli Wang,et al.  FT-IR study of the microstructure of Nafion ® membrane , 2004 .

[17]  Hwayong Kim,et al.  Preparation of PVdF/PSSA composite membranes using supercritical carbon dioxide for direct methanol fuel cells , 2009 .

[18]  H. Pu,et al.  Proton conducting membranes based on semi-interpenetrating polymer network of Nafion and polybenzimidazole , 2010 .

[19]  A. Morin,et al.  Influence of the membrane treatment on structure and properties of sulfonated poly(etheretherketone) semi-interpenetrating polymer network , 2013 .

[20]  Ho-Young Jung,et al.  Long-term performance of DMFC based on the blend membrane of sulfonated poly(ether ether ketone) and poly(vinylidene fluoride) , 2009 .

[21]  D. Wan,et al.  Chemical oxidative degradation of Polybenzimidazole in simulated environment of fuel cells , 2009 .

[22]  S. Hanna,et al.  Hydration of Nafion® studied by AFM and X-ray scattering , 2000 .

[23]  K. Friedrich,et al.  Transport properties of ionomer composite membranes for direct methanol fuel cells , 2002 .

[24]  Jung-Ki Park,et al.  Characteristics of PVdF copolymer/Nafion blend membrane for direct methanol fuel cell (DMFC) , 2004 .

[25]  O. Fichet,et al.  (Semi-)Interpenetrating polymer networks as fuel cell membranes , 2011 .

[26]  Jae‐Suk Lee,et al.  Cross-Linking Density Effect of Fluorinated Aromatic Polyethers on Transport Properties , 2009 .

[27]  Zhenglong Yang,et al.  Towards high water retention of proton exchange membranes at elevated temperature via hollow nanospheres , 2010 .

[28]  G. Robertson,et al.  Sulfonated copoly(phthalazinone ether ketone nitrile)s as proton exchange membrane materials , 2006 .