Present status and future prospect of coated conductor development and its application in Japan

The current national project on coated conductors using Y-system superconductors has been carried out over the project period (FY2003–FY2007). In this paper, the current status and the future prospect of this project are reviewed. The high performance tape development group, consisting of Fujikura and SRL-NCCC, has worked on the tape by PLD-REBCO superconducting layers on PLD-CeO2/IBAD-GZO buffered substrates. A high product of Ic and L, higher than 112 166 A m, was achieved in a 368 m–304.8 A GdBCO tape whose Ic value is mostly above 350 A/cm in width. The performance under magnetic field was also improved up to 42 A at 3 T in a GdBCO short film with doping of ZrO2. 61 m long GdBCO tape with ZrO2 doping showed a high Ic value of 220 A at self field and 30 A at 3 T. On the other hand, another group focusing on low production cost has worked on TFA-MOD and MOCVD processes. The extremely high Ic value of 735 A/cm-w was obtained in TFA-MOD films on PLD-CeO2/IBAD-GZO/Hastelloy substrate due to the effect of Ba-poor nominal composition. In efforts towards long tape production by the SWCC group, a 200 m long tape with a high Ic value of 200 A/cm-w was obtained using a batch-type furnace. The Ic × L value of this tape was 40 000 A m, which is the highest value in the world obtained by the TFA-MOD process. Based on the above achievements in coated conductor process development, two new additional goals were set in the project. One is the development of extremely low cost tape and the other is the development of the basic technologies for making electric power devices of cables, transformers, motors, current-limiters and cryocoolers. Some of the new investigations have already revealed marvellous results, such as a 15 kW motor, low AC loss coils, low AC loss cables, etc.