Oriented thin films from soluble polythiophenes

The degree of orientation of thin films of eight different polymeric structures, belonging to the class of soluble polyalkylthiophenes (PATs) has been studied. Thin films of the polymers, obtained by spin coating onto glass substrates, were oriented by means of the rubbing technique. The degree of orientation is related to the regioregularity of the system: highly regioregular polymers can be oriented, while regiorandom materials are not oriented. The degree of orientation can be improved by thermal annealing of the oriented films. As a result of annealing, which was performed at different temperatures according to the thermal behavior of the polymers, it was possible to increase the polarization ratio for poly(3-decylthiophene) up to 12–13 as detected from the UV-vis spectra in polarized light. Moreover in the investigated PATs, both the key role of molecular weight and its distribution for achieving a high orientation degree has been assessed. Copyright © 2003 John Wiley & Sons, Ltd.

[1]  A. Bolognesi,et al.  Structural and thermal behavior of poly(3-octylthiophene): a DSC, 13C MAS NMR, XRD, photoluminescence, and Raman scattering study , 2001 .

[2]  A. Bolognesi,et al.  Polarized photoluminescence and electroluminescence in oriented films of regioregular poly(3-alkylthiophenes) , 2000 .

[3]  M. Grell,et al.  Highly polarized blue electroluminescence from homogeneously aligned films of poly(9,9-dioctylfluorene) , 2000 .

[4]  Donal D. C. Bradley,et al.  Polarized Luminescence from Oriented Molecular Materials , 1999 .

[5]  A. Bolognesi,et al.  Highly regioregular poly(3‐alkylthiophenes): a new synthetic route and characterization of the resulting polymers , 1999 .

[6]  G. Bidan,et al.  New convenient synthesis of highly regioregular poly(3-octylthiophene) based on the Suzuki coupling reaction , 1998 .

[7]  M. Catellani,et al.  Structural effects in poly(3‐alkylthiophene)s on the exposition to poor solvent , 1997 .

[8]  K. Yoshino,et al.  Polarized fluorescence and electroluminescence from rubbing‐aligned conjugated polymers and their composites with fluorescent dyes , 1997 .

[9]  A. Bolognesi,et al.  The thermal behaviour of poly(3-octylthienylene) synthesized by an Ni-based catalyst: DSC, optical microscopy and XRD analyses , 1996 .

[10]  Tiberio A. Ezquerra,et al.  The thermal behaviour of low-molecular-weight poly(3-decylthiophene) , 1993 .

[11]  K. Yoshino,et al.  Structure and thermochromic solid‐state phase transition of poly (3‐alkylthiophene) , 1991 .

[12]  S. Enzo,et al.  A Profile-Fitting Procedure for Analysis of Broadened X-ray Diffraction Peaks. I. Methodology , 1988 .

[13]  U. Scherf,et al.  Photoaddressable Alignment Layers for Fluorescent Polymers in Polarized Electroluminescence Devices , 2002 .

[14]  E. Salatelli,et al.  Novel poly(3,3″ - and 3′, 4′-dialkyl-2, 2′:5′, 2″- terthiophene)s by chemical oxidative synthesis: evidence for a new step towards the optimization of this process , 1996 .