论文信息 - Effect of diluents on high purity β-SiAlONs by mechanically activated combustion synthesis

Effect of diluents on high purity β-SiAlONs by mechanically activated combustion synthesis

The influence of diluent addition on purities of β-Si5AlON7 powders synthesized by mechanically activated combustion synthesis (MA-CS) under a very low nitrogen atmosphere of 1 MPa was investigated. The purity of β-Si5AlON7 powders increased with diluent concentrations in raw materials and had a maximum value of 91% when 40 mass% of diluents were added, a 25% more pure when compared to powders procured without diluents. In contrast, when diluents were included 50% or more, the combustion synthesis (CS) reaction did not occur due to reduced exothermic heat. The results also showed that the particle sizes of β-Si5AlON7 powders synthesized with 40 mass% of diluents were only one-tenth when compared to powders synthesized without diluents.

T. Akiyama | Toshiyuki Watanabe | R. Sivakumar | Xuemei Yi | K. Aoyagi

[1] T. Akiyama,et al. Effect of mechanically activated raw materials on β-sialon formation by combustion synthesis , 2007 .

[2] T. Akiyama,et al. A new route to synthesize β-Si6- zAlzOzN8- z powders , 2007 .

[3] T. Akiyama,et al. Mechanically Activated Combustion Synthesis of β‐Si6−zAlzOzN8−z (z=1–4) , 2007 .

[4] J. Ferreira,et al. Effect of diluents and NH4F additive on the combustion synthesis of Yb α-SiAlON , 2005 .

[5] H. Mandal,et al. Functionally graded SiAlON ceramics , 2004 .

[6] D. Dollimore,et al. Mechanism of the formation of β–Sialon by self-propagating high-temperature synthesis , 1998 .

[7] Y. Miyamoto,et al. Combustion Synthesis of Sialon Powders (Si6‐zAlzOzN8‐z, Z = 0.3, 0.6) , 1990 .

[8] Z. A. Munir,et al. Self-propagating exothermic reactions: the synthesis of high-temperature materials by combustion , 1989 .