Temperature effects on the switching kinetics of a Cu–Ta2O5-based atomic switch

Voltage-current (I-V) measurements in a wide temperature range from 88 to 573 K demonstrated the effects of temperature on the switching behavior of a Cu/Ta(2)O(5)/Pt resistive memory cell that is referred to as a gapless-type atomic switch. After the forming process, the cells were SET from the OFF state to the ON state at a positive bias to the Cu electrode and then RESET from the ON state to the OFF state at a negative bias. In a previous study (Tsuruoka et al 2010 Nanotechnology 21 425205), it was demonstrated that the SET process corresponds to the reformation of a metal filament between the electrodes by the inhomogeneous nucleation and subsequent growth of Cu whereas the RESET process can be attributed to the Joule-heating-assisted dissolution of the metal filament. In the work described here, we observed that the voltages at which the cells are SET and RESET (SET and RESET voltages) decreased in magnitude with an increase in temperature. From calculations of the nucleation rate of Cu nuclei based on the classical nucleation theory, it was found that the observed temperature variation of the SET voltage is primarily determined by supersaturation in the vicinity of the Pt electrode, which is controlled by the application of positive bias. The supersaturation required for spontaneous growth of a Cu nucleus decreases with increasing temperature, resulting in lower SET voltages at higher temperatures. The RESET voltage is determined by the thermal stability of the metal filament formed. Moreover, using the temperature variation in cell resistances of the ON state, the growth speed of the Cu nucleus after the nucleation was found to decease with increasing temperature. These results are consistent with our switching model.

[1]  G. White,et al.  Thermophysical properties of some key solids: An update , 1997 .

[2]  W. E. Beadle,et al.  Switching properties of thin Nio films , 1964 .

[3]  R. Gurney,et al.  Electronic Processes in Ionic Crystals , 1964 .

[4]  K Balasubramanian,et al.  Absorption and thermal conductivity of oxide thin films measured by photothermal displacement and reflectance methods. , 1993, Applied optics.

[5]  A. Milchev.  Electrocrystallization: Fundamentals of Nucleation and Growth , 2002 .

[6]  M. Kozicki,et al.  A Low-Power Nonvolatile Switching Element Based on Copper-Tungsten Oxide Solid Electrolyte , 2006, IEEE Transactions on Nanotechnology.

[7]  R. Waser,et al.  Nanoionics-based resistive switching memories. , 2007, Nature materials.

[8]  T. Hasegawa,et al.  Nanoionics Switching Devices: “Atomic Switches” , 2009 .

[9]  M. Haemori,et al.  Impact of Cu Electrode on Switching Behavior in a Cu/HfO2/Pt Structure and Resultant Cu Ion Diffusion , 2009 .

[10]  M. D. Rooij,et al.  Electrochemical Methods: Fundamentals and Applications , 2003 .

[11]  Qi Liu,et al.  On the resistive switching mechanisms of Cu/ZrO2:Cu/Pt , 2008 .

[12]  Ligang Gao,et al.  The growth of metallic nanofilaments in resistive switching memory devices based on solid electrolytes , 2009 .

[13]  T. Hasegawa,et al.  Electronic transport in Ta2O5 resistive switch , 2007 .

[14]  D. Turnbull.  Formation of Crystal Nuclei in Liquid Metals , 1950 .

[15]  Jae Hyuck Jang,et al.  Atomic structure of conducting nanofilaments in TiO2 resistive switching memory. , 2010, Nature nanotechnology.

[16]  Daan Frenkel,et al.  Suppression of crystal nucleation in polydisperse colloids due to increase of the surface free energy , 2001, Nature.

[17]  C. Henager,et al.  Thermal conductivities of thin, sputtered optical films. , 1993, Applied optics.

[18]  R. Dittmann,et al.  Redox‐Based Resistive Switching Memories – Nanoionic Mechanisms, Prospects, and Challenges , 2009, Advanced materials.

[19]  P. Gonon,et al.  Resistance switching of Cu/SiO2 memory cells studied under voltage and current-driven modes , 2010 .

[20]  C. N. Lau,et al.  The mechanism of electroforming of metal oxide memristive switches , 2009, Nanotechnology.

[21]  R. Digilov,et al.  Solid–liquid interfacial tension in metals: correlation with the melting point , 2004 .

[22]  Shu Yamaguchi,et al.  Nonstoichiometry-Induced Carrier Modification in Gapless Type Atomic Switch Device Using Cu2S Mixed Conductor , 2009 .

[23]  T. Hasegawa,et al.  Nanometer-scale switches using copper sulfide , 2003 .

[24]  D. Morgan,et al.  Electrical phenomena in amorphous oxide films , 1970 .

[25]  J. J. O'Dwyer,et al.  The theory of electrical conduction and breakdown in solid dielectrics , 1973 .

[26]  Qi Liu,et al.  Controllable growth of nanoscale conductive filaments in solid-electrolyte-based ReRAM by using a metal nanocrystal covered bottom electrode. , 2010, ACS nano.

[27]  A. Pergament,et al.  Electroforming and Switching in Oxides of Transition Metals: The Role of Metal-Insulator Transition in the Switching Mechanism , 1996 .

[28]  K. Terabe,et al.  Forming and switching mechanisms of a cation-migration-based oxide resistive memory , 2010, Nanotechnology.

[29]  C. B. Richardson,et al.  A study of heterogeneous nucleation in aqueous solutions , 1994 .

[30]  M. Kozicki,et al.  Low current resistive switching in Cu–SiO2 cells , 2008 .

[31]  G. Atwood,et al.  Future directions and challenges for ETox flash memory scaling , 2004, IEEE Transactions on Device and Materials Reliability.

[32]  M. Kozicki,et al.  Nanoscale memory elements based on solid-state electrolytes , 2005, IEEE Transactions on Nanotechnology.

[33]  K. L. Chopra,et al.  Avalanche‐Induced Negative Resistance in Thin Oxide Films , 1965 .

[34]  K. Kinoshita,et al.  Consideration of switching mechanism of binary metal oxide resistive junctions using a thermal reaction model , 2007 .

[35]  D. Pique,et al.  Calculation of solid-liquid-vapour contact angles for binary metallic systems , 1980 .

[36]  B. Vinet,et al.  Correlations between surface and interface energies with respect to crystal nucleation. , 2002, Journal of colloid and interface science.

[37]  K. Terabe,et al.  Quantized conductance atomic switch , 2005, Nature.