Fatigue crack nucleation and growth in filled natural rubber

Rubber components subjected to fluctuating loads often fail due to nucleation and the growth of defects or cracks. The prevention of such failures depends upon an understanding of the mechanics underlying the failure process. This investigation explores the nucleation and growth of cracks in filled natural rubber. Both fatigue macro-crack nucleation as well as fatigue crack growth experiments were conducted using simple tension and planar tension specimens, respectively. Crack nucleation as well as crack growth life prediction analysis approaches were used to correlate the experimental data. Several aspects of the fatigue process, such as failure mode and the effects of R ratio (minimum strain) on fatigue life, are also discussed. It is shown that a small positive R ratio can have a significant beneficial effect on fatigue life and crack growth rate, particularly at low strain range.

[1]  Ali Fatemi,et al.  A novel specimen for investigating the mechanical behavior of elastomers under multiaxial loading conditions , 2004 .

[2]  P. B. Lindley.  Relation between hysteresis and the dynamic crack growth resistance of natural rubber , 1973, International Journal of Fracture.

[3]  H. W. Greensmith.  Rupture of rubber. XI. Tensile rupture and crack growth in a noncrystallizing rubber , 1964 .

[4]  R. Rivlin,et al.  Rupture of rubber. I. Characteristic energy for tearing , 1953 .

[5]  P. B. Lindley,et al.  The mechanical fatigue limit for rubber , 1965 .

[6]  H. W. Greensmith.  Rupture of rubber. VIII. Comparisons of tear and tensile rupture measurements , 1960 .

[7]  C. Inglis.  Stresses in a plate due to the presence of cracks and sharp corners , 1913 .

[8]  P. B. Lindley,et al.  Cut growth and fatigue of rubbers. II. Experiments on a noncrystallizing rubber , 1964 .

[9]  G. J. Lake.  Fatigue and Fracture of Elastomers , 1995 .

[10]  A. Thomas,et al.  Rupture of rubber. II. The strain concentration at an incision , 1955 .

[11]  H. W. Greensmith.  Rupture of rubber. X. The change in stored energy on making a small cut in a test piece held in simple extension , 1963 .

[12]  P. Paris.  A rational analytic theory of fatigue , 1961 .

[13]  Ali Fatemi,et al.  Factors that affect the fatigue life of rubber: A literature survey , 2004 .

[14]  Ali Fatemi,et al.  Observations of the Constitutive Response and Characterization of Filled Natural Rubber Under Monotonic and Cyclic Multiaxial Stress States , 2004 .

[15]  Ali Fatemi,et al.  A Phenomenological Model for the Effect of R Ratio on Fatigue of Strain Crystallizing Rubbers , 2003 .

[16]  Alan N. Gent,et al.  Cut growth and fatigue of rubbers. I. The relationship between cut growth and fatigue , 1964 .

[17]  D. G. Young.  Dynamic Property and Fatigue Crack Propagation Research on Tire Sidewall and Model Compounds , 1985 .

[18]  H. W. Greensmith.  Rupture of rubber. VII. Effect of rate of extension in tensile tests , 1960 .

[19]  A. A. Griffith.  The Phenomena of Rupture and Flow in Solids , 1921 .

[20]  D. G. Young,et al.  Application of Fatigue Methods Based on Fracture Mechanics for Tire Compound Development , 1990 .

[21]  Ali Fatemi,et al.  A literature survey on fatigue analysis approaches for rubber , 2002 .

[22]  A. Thomas,et al.  Rupture of rubber. VI. Further experiments on the tear criterion , 1960 .

[23]  A. G. Thomas.  Rupture of rubber. V. Cut growth in natural rubber vulcanizates , 1958 .

[24]  S. M. Cadwell,et al.  Dynamic Fatigue Life of Rubber , 1940 .

[25]  A. Thomas,et al.  Rupture of Rubber. III. Determination of Tear Properties , 1955 .

[26]  H. W. Greensmith.  Rupture of rubber. IV. Tear properties of vulcanizates containing carbon black , 1956 .