论文信息 - Simulating soft body impact on glass structures - 字舞流文

Simulating soft body impact on glass structures

Soft body impacts are fundamental loads in safety glass design and usually govern the glass composition and glass thickness. The resistance of these glasses against soft body impact and their safet...

Jens Schneider | Sebastian Schula

[1] Sheldon M. Wiederhorn,et al. Influence of Water Vapor on Crack Propagation in Soda‐Lime Glass , 1967 .

[2] Gerhard Sedlacek,et al. Ein numerisches Verfahren zur Berechnung von Verbundglasscheiben , 1999 .

[3] David J. Green,et al. Influence of indentation crack configuration on strength and fatigue behaviour of soda-lime silicate glass , 1995 .

[4] Sebastian Schula. Charakterisierung der Kratzanfälligkeit von Gläsern im Bauwesen = Characterisation of the scratch sensitivity of glasses in civil engineering , 2015 .

[5] E. Gehrke,et al. Correlation between multistage crack growth and time-dependent strength in commercial silicate glasses. I: Influence of ambient media and types of initial cracks , 1987 .

[6] Mauro Overend,et al. A computer algorithm for determining the tensile strength of float glass , 2012 .

[7] A. G. Evans,et al. Proof testing of ceramic materials—an analytical basis for failure prediction , 1974 .

[8] Sebastian Schula. Festigkeit von Glas im Bauwesen , 2015 .

[9] S. Wiederhorn,et al. Stress Corrosion and Static Fatigue of Glass , 1970 .

[10] D. Maugis,et al. Subcritical crack growth, surface energy, fracture toughness, stick-slip and embrittlement , 1985 .

[11] Maria Fröling,et al. Strength Design Methods for Glass Structures , 2013 .