Effect of Oxygen Flow Rate on Electrical and Optical Properties of ATO Thin Films Prepared by RF Magnetron Sputtering

Transparent conducting antimony doped tin oxide (ATO) films were sputtered on quartz glass substrates by RF magnetron sputtering at an oxygen flow rate ranging from 0 to 15 sccm. The films were prepared at room temperature and annealed for 15 min in air atmospheres at a temperature of 450 °C. The effect of oxygen flow rate has been investigated by comparing eletrical and optical properties of ATO films. The results suggest that, oxygen flow rate has a great impact on Sb5+/Sb3+ ratio and lattice structure integrity, which finally affects the transmittance and electrical resistivity. With the increase of oxygen flow rate, the grain size is enlarged, which leads to a higher average optical transmittance. On the other hand, with oxygen flow rate increasing, the Sb5+/Sb3+ ratio first increases and then decreases sharply when the oxygen flow rate exceeds 5 sccm. The increase of Sb5+/Sb3+ ratio results in the increase of carrier concentration and finally contributes to a decrease of electrical resistivity. The optimal resistivity is 8.9×10-2 Ω·cm and the average transmittance is about 95% at an oxygen flow rate of 5 sccm.

[1]  Weifeng Zhang,et al.  Properties of Sb-doped SnO2 transparent conductive thin films deposited by radio-frequency magnetron sputtering , 2013 .

[2]  P. Biswas,et al.  Synthesis and photoluminescence property of nanostructured sol–gel antimony tin oxide film on silica glass , 2013 .

[3]  C. Guillén,et al.  Nanocrystalline antimony doped tin oxide (ATO) thin films: A thermal restructuring study , 2012 .

[4]  Q. Shen,et al.  Fabrication of transparent conducting ATO films using the ATO sintered targets by pulsed laser deposition , 2012 .

[5]  B. Hong,et al.  Structural, Electrical, and Optical Properties of SnO2:Sb Films Prepared on Flexible Substrate at Room Temperature , 2011 .

[6]  C. Guillén,et al.  Preparation of reactively sputtered Sb-doped SnO2 thin films: Structural, electrical and optical properties , 2010 .

[7]  Jong‐Lam Lee,et al.  Corrigendum to “Criteria for ITO (indium–tin–oxide) thin film as the bottom electrode of an organic light emitting diode” [Thin Solid Films 411 (2002) 12–16] , 2009 .

[8]  Y. Sung,et al.  Discharge power dependence of structural and electrical properties of Al-doped ZnO conducting film by magnetron sputtering (for PDP) , 2008 .

[9]  Daoli Zhang,et al.  Surface morphologies and properties of pure and antimony-doped tin oxide films derived by sol–gel dip-coating processing , 2006 .

[10]  Daoli Zhang,et al.  Microstructure and electrical properties of antimony-doped tin oxide thin film deposited by sol–gel process , 2006 .

[11]  Jow-Lay Huang,et al.  Annealing effects on properties of antimony tin oxide thin films deposited by RF reactive magnetron sputtering , 2004 .

[12]  X. Hao,et al.  Comparison of the electrical and optical properties for SnO2:Sb films deposited on polyimide and glass substrates , 2003 .

[13]  Y. Tak,et al.  Criteria for ITO (indium tin-oxide) thin film as the bottom electrode of an organic light emitting diode , 2002 .