Fatigue life assessment under a complex multiaxial load history: an approach based on damage mechanics

In order to assess the fatigue behaviour of structural components under a complex (cyclic or random) multiaxial stress history, methods based on damage mechanics concepts can be employed. In this paper, a model for fatigue damage evaluation in the case of an arbitrary multiaxial loading history is proposed by using an endurance function which allows us to determine the damage accumulation up to the final failure of the material. By introducing an evolution equation for the endurance function, the final collapse can be assumed to occur when the damage D is complete, that is when D reaches the unity. The parameters of this model, which adopts the stress invariants and the deviatoric stress invariants to quantify the damage phenomenon, are determined through a Genetic Algorithm once experimental data on the fatigue behaviour of the material being examined are known for some complex stress histories. With respect to traditional approaches to multiaxial fatigue assessment, the proposed model presents the following advantages: (1) the evaluation of a critical plane is not necessary; (2) no cycle counting algorithm to determine the fatigue life is required, because it considers the progressive damage process during the fatigue load history; (3) the model can be applied to any kind of stress history (uniaxial cyclic loading, multiaxial in-phase or out-of-phase cyclic loading, uniaxial or multiaxial random loading).

[1]  Luca Susmel,et al.  A stress‐based method to predict lifetime under multiaxial fatigue loadings , 2003 .

[2]  S. Stephanov,et al.  A curvilinear integral method for multiaxial fatigue life computing under non-proportional, arbitrary or random stressing , 1993 .

[3]  A. Carpinteri,et al.  A multiaxial fatigue criterion for random loading , 2003 .

[4]  Serge Lasserre,et al.  Multiaxial fatigue of steel—testing out of phase and in blocks: validity and applicability of some criteria , 1992 .

[5]  Luca Susmel,et al.  A stress invariant based criterion to estimate fatigue damage under multiaxial loading , 2008 .

[6]  Andrea Carpinteri,et al.  Expected principal stress directions under multiaxial random loading. Part I: theoretical aspects of the weight function method , 1999 .

[7]  R. Haftka,et al.  Structural shape optimization — a survey , 1986 .

[8]  Matti Ristinmaa,et al.  Continuum approach to high-cycle fatigue modeling , 2008 .

[9]  Andrea Carpinteri,et al.  A genetic algorithm applied to optimisation of patch repairs for cracked plates , 2006 .

[10]  Serge Lasserre,et al.  Multiaxial fatigue endurance of 30NCD16 steel , 1989 .

[11]  Filippo Berto,et al.  Multi-axial fatigue behaviour of a severely notched carbon steel , 2006 .

[12]  Andrea Carpinteri,et al.  Expected principal stress directions under multiaxial random loading. Part II: numerical simulation and experimental assessment through the weight function method , 1999 .

[13]  W. Findley.  A Theory for the Effect of Mean Stress on Fatigue of Metals Under Combined Torsion and Axial Load or Bending , 1959 .

[14]  Christine M. Anderson-Cook,et al.  A genetic algorithm with memory for mixed discrete–continuous design optimization , 2003 .

[15]  Mácha,et al.  Energy criteria of multiaxial fatigue failure , 1999 .

[16]  Takahiro Hata,et al.  A design procedure for assessing low cycle fatigue life under proportional and non-proportional loading , 2006 .

[17]  Masahiro Endo,et al.  Shear mode threshold for a small fatigue crack in a bearing steel , 2011 .

[18]  Tarek I. Zohdi,et al.  Constrained inverse formulations in random material design , 2003 .

[19]  Andrea Carpinteri,et al.  Multiaxial high-cycle fatigue criterion for hard metals , 2001 .

[20]  C. M. Sonsino,et al.  A notch stress intensity approach to assess the multiaxial fatigue strength of welded tube‐to‐flange joints subjected to combined loadings , 2004 .

[21]  Masaya Kameoka,et al.  A new model for describing a stable cyclic stress-strain relationship under non-proportional loading based on activation state of slip systems , 2004 .

[22]  Ewald Macha,et al.  Fatigue lives of 18G2A and 10HNAP steels under variable amplitude and random non-proportional bending with torsion loading , 2008 .