An experimental analysis of fatigue behavior of AZ31B magnesium alloy welded joint based on infrared thermography

Abstract The fatigue behavior of AZ31B magnesium alloy welded joint during high cycle fatigue test was investigated by infrared thermography. Five stages of superficial temperature evolution were observed: an initial temperature increase, a temperature decline, a temperature equilibrium, an abrupt temperature increase and a temperature drop after the failure. The theoretical models were formulated to explain the observed temperature evolution. The mean temperature decline caused by thermoelastic effect was observed and discussed when the maximum stresses were below 30 MPa. The influence of weld reinforcement on fatigue behavior was also investigated. A good precision was achieved in fatigue strength prediction by means of infrared thermography.

[1]  R. Zhu,et al.  Effect of aging treatment on low-cycle fatigue behavior of extruded Mg–8Al–0.5Zn alloys , 2012 .

[2]  Chengwei Wu,et al.  A new application of the infrared thermography for fatigue evaluation and damage assessment , 2012 .

[4]  Wang Xun-hong,et al.  Microstructure and properties of friction stir butt-welded AZ31 magnesium alloy , 2006 .

[5]  F. V. Lawrence,et al.  Analytical and Graphical Aids for the Fatigue Design of Weldments , 1985 .

[6]  Michael M. Khonsari,et al.  Rapid determination of fatigue failure based on temperature evolution: Fully reversed bending load , 2010 .

[7]  Jean-Eric Masse,et al.  Friction stir welding of AZ31 magnesium alloy rolled sheets: Influence of processing parameters , 2009 .

[8]  A. K. Wong,et al.  On the revised theory of the thermoelastic effect , 1988 .

[9]  Alberto Marino,et al.  Fatigue analysis of butt welded AH36 steel joints: Thermographic Method and design S–N curve , 2009 .

[10]  Graziano Curti,et al.  Analisi tramite infrarosso termico della temperatura limite in prove di fatica , 1986 .

[11]  Yajie Quan,et al.  Effects of heat input on microstructure and tensile properties of laser welded magnesium alloy AZ31 , 2008 .

[12]  Vincenzo Crupi,et al.  Using Infrared Thermography in Low-Cycle Fatigue Studies of Welded Joints , 2010 .

[13]  J. Fan,et al.  Research on fatigue behavior evaluation and fatigue fracture mechanisms of cruciform welded joints , 2011 .

[14]  Antonino Risitano,et al.  Cumulative damage evaluation of steel using infrared thermography , 2010 .

[15]  William Thomson,et al.  Mathematical and physical papers , 1880 .

[16]  Y. Uematsu,et al.  Effect of extrusion conditions on grain refinement and fatigue behaviour in magnesium alloys , 2006 .

[17]  Peter K. Liaw,et al.  Thermographic investigation of the fatigue behavior of reactor pressure vessel steels , 2001 .

[18]  M. P. Luong,et al.  Infrared thermographic scanning of fatigue in metals , 1995 .

[19]  M. Khonsari,et al.  A thermographic method for remaining fatigue life prediction of welded joints , 2013 .

[20]  Thomas Ummenhofer,et al.  On the use of infrared thermography for the analysis of fatigue damage processes in welded joints , 2009 .