Effect of hydrogen on carbon formation on Ni/YSZ composites exposed to methane

Abstract Nickel/yttria-stabilized zirconia (Ni/YSZ) is the conventional anode material for solid oxide fuel cells (SOFC). Although these anodes have many advantages, they suffer from carbon formation when exposed to hydrocarbon feeds. One potential way to decrease the severity and extent of carbon formation is to increase the hydrogen content of the feed. In this work, Ni/YSZ composites have been prepared and exposed at 1073 K to humidified feeds containing hydrogen to methane ratios varying between 0 and 1.5. The Ni/YSZ composites were analyzed using temperature-programmed oxidation (TPO), temperature-programmed hydrogenation (TPH), and scanning electron microscopy (SEM). Our results demonstrated that TPH techniques can be effectively used to characterize and fully remove the carbon formed on Ni/YSZ composites provided that the hydrogen content of the analysis stream is sufficient. Hydrogen addition to methane in the inlet feed significantly decreased the degree of carbon formation, and removal of the carbon using hydrogen rather than oxygen resulted in less damage to the microstructure.

[1]  J. Nørskov,et al.  Steam Reforming and Graphite Formation on Ni Catalysts , 2002 .

[2]  C. H. Bartholomew.  Carbon Deposition in Steam Reforming and Methanation , 1982 .

[3]  Seungdoo Park,et al.  Direct Oxidation of Hydrocarbons in a Solid Oxide Fuel Cell: I. Methane Oxidation , 1999 .

[4]  Robert J. Kee,et al.  Homogeneous kinetics and equilibrium predictions of coking propensity in the anode channels of direct oxidation solid-oxide fuel cells using dry natural gas , 2003 .

[5]  D. Trimm,et al.  The kinetics of gasification of carbon deposited on nickel catalysts , 1979 .

[6]  S. A. Barnett,et al.  A direct-methane fuel cell with a ceria-based anode , 1999, Nature.

[7]  S. Neophytides,et al.  The nature and binding strength of carbon adspecies formed during the equilibrium dissociative adsorption of CH4 on Ni–YSZ cermet catalysts , 2003 .

[8]  M. G. Bader,et al.  Design and applications , 2000 .

[9]  Hongpeng He,et al.  Carbon deposition on Ni/YSZ composites exposed to humidified methane , 2007 .

[10]  Mogens Bjerg Mogensen,et al.  Reaction of CO/CO2 gas mixtures on Ni–YSZ cermet electrodes , 1999 .

[11]  S. Barnett,et al.  Direct operation of solid oxide fuel cells with methane fuel , 2005 .

[12]  Josephine M. Hill,et al.  Effect of anodic polarization on carbon deposition on Ni/YSZ anodes exposed to methane , 2008 .

[13]  Toshiaki Mori,et al.  Kinetics of the reverse-Boudouard reaction over supported nickel catalysts , 2006 .

[14]  L. Albright,et al.  Coke formation on metal surfaces , 1983 .

[15]  Y. Nishiyama,et al.  Deposition of carbon and its hydrogenation catalyzed by nickel , 1976 .

[16]  D. Duprez,et al.  Deactivation of steam-reforming model catalysts by coke formation: I. Kinetics of the Formation of Filamentous Carbon in the Hydrogenolysis of cyclopentane on Ni/Al2O3 Catalysts , 1990 .

[17]  I. Metcalfe,et al.  Study of the activity and deactivation of Ni-YSZ cermet in dry CH4 using temperature-programmed techniques , 1995 .

[18]  Ryuji Kikuchi,et al.  Fuel flexibility in power generation by solid oxide fuel cells , 2002 .

[19]  Caine M. Finnerty,et al.  Carbon formation on and deactivation of nickel-based/zirconia anodes in solid oxide fuel cells running on methane , 1998 .

[20]  Ayodeji Jeje,et al.  3D modeling of anode-supported planar SOFC with internal reforming of methane , 2007 .

[21]  N. Jaeger,et al.  Evidence for a hydrogen spillover effect in the deposition of coke on a nickel-faujasite catalyst during syngas conversion , 1992 .

[22]  J. Nørskov,et al.  Why gold is the noblest of all the metals , 1995, Nature.