Strength and barrier properties of MFC films

The preparation of microfibrillar cellulose (MFC) films by filtration on a polyamide filter cloth, in a dynamic sheet former and as a surface layer on base paper is described. Experimental evidence of the high tensile strength, density and elongation of films formed by MFC is given. Typically, a MFC film with basis weight 35 g/m2 had tensile index 146 ± 18 Nm/g and elongation 8.6 ± 1.6%. The E modulus (17.5 ± 1.0 GPa) of a film composed of randomly oriented fibrils was comparable to values for cellulose fibres with a fibril angle of 50°. The strength of the films formed in the dynamic sheet former was comparable to the strength of the MFC films prepared by filtration. The use of MFC as surface layer (0–8% of total basis weight) on base paper increased the strength of the paper sheets significantly and reduced their air permeability dramatically. FEG-SEM images indicated that the MFC layer reduced sheet porosity, i.e. the dense structure formed by the fibrils resulted in superior barrier properties. Oxygen transmission rates (OTR) as low as 17 ml m−2 day−1 were obtained for films prepared from pure MFC. This result fulfils the requirements for oxygen transmission rate in modified atmosphere packaging.

[1]  Leena‐Sisko Johansson,et al.  Properties and characterization of hydrophobized microfibrillated cellulose , 2006 .

[2]  S. G. Frank,et al.  MICROCRYSTALLINE CELLULOSE STABILIZEDEMULSIONS , 1986 .

[3]  R. Parry,et al.  Principles and applications of modified atmosphere packaging of foods , 1993 .

[4]  Kunihiko Watanabe,et al.  Emulsion-stabilizing Effect of Bacterial Cellulose , 1997 .

[5]  J. W. Farrent,et al.  High-performance composites from low-cost plant primary cell walls , 2005 .

[6]  N. Jain,et al.  A stable multiple emulsion system bearing isoniazid: preparation and characterization. , 1998, Drug development and industrial pharmacy.

[7]  J. Lagarón,et al.  Characterization of the barrier properties of composites of HDPE and purified cellulose fibers , 2007 .

[8]  A. Dufresne,et al.  Thermoplastic nanocomposites based on cellulose microfibrils from Opuntia ficus-indica parenchyma cell , 2005 .

[9]  Mikko J. Alava,et al.  The physics of paper , 2006 .

[10]  M. Jägerstad,et al.  Foods and packaging materials : chemical interactions , 1995 .

[11]  Per Stenstad,et al.  Chemical surface modifications of microfibrillated cellulose , 2008 .

[12]  O. Ikkala,et al.  Enzymatic hydrolysis combined with mechanical shearing and high-pressure homogenization for nanoscale cellulose fibrils and strong gels. , 2007, Biomacromolecules.

[13]  Alain Dufresne,et al.  Mechanical behavior of sheets prepared from sugar beet cellulose microfibrils , 1997 .

[14]  Hiroyuki Yano,et al.  Novel high-strength biocomposites based on microfibrillated cellulose having nano-order-unit web-like network structure , 2005 .

[15]  J. Lagarón,et al.  Enhanced film forming and film properties of amylopectin using micro-fibrillated cellulose , 2007 .

[16]  K. R. Sandberg,et al.  Microfibrillated cellulose, a new cellulose product: properties, uses, and commercial potential , 1983 .

[17]  Leena‐Sisko Johansson,et al.  Nonleaching antimicrobial films prepared from surface-modified microfibrillated cellulose. , 2007, Biomacromolecules.

[18]  P. Stenius,et al.  Water‐in‐oil Emulsions Stabilized by Hydrophobized Microfibrillated Cellulose , 2007 .

[19]  L. Berglund,et al.  Structure and Properties of Cellulose Nanocomposite Films Containing Melamine Formaldehyde , 2007 .

[20]  H. Yano,et al.  Obtaining cellulose nanofibers with a uniform width of 15 nm from wood. , 2007, Biomacromolecules.

[21]  Henrik Kjellgren,et al.  Paper and paper coating performance chemicals , 2006 .

[22]  H. Fink,et al.  Structure formation of regenerated cellulose materials from NMMO-solutions , 2001 .

[23]  Rafael Gavara,et al.  Structural characteristics defining high barrier properties in polymeric materials , 2004 .

[24]  Takashi Taniguchi,et al.  New films produced from microfibrillated natural fibres , 1998 .

[25]  D. Page,et al.  Elastic modulus of single wood pulp fibers , 1977 .

[26]  H. L. Cox.  The elasticity and strength of paper and other fibrous materials , 1952 .

[27]  Henrik Kjellgren,et al.  Influence of base paper on the barrier properties of chitosan-coated papers , 2006 .