Protection of marble surfaces by using biodegradable polymers as coating agent

Biodegradable polymers have been replaced over the synthetic polymers in many applications due to their good properties such as reversibility and biodegradability. Therefore they allow new treatment on the surface of the material to be protected and they fulfil the principles generally accepted by the International Conservation Community of Historic Monuments and Buildings. In this study, the efficiency of four different biodegradable polymers as protective coatings on marble–SO2 reaction was investigated. The polymers used were zein, chitosan, polyhydroxybutyrate (PHB), and poly-l-lactide (PLA). The mineralogical composition, bulk density and porosity of uncoated marble were determined. The water vapor permeability, water absorption by capillary forces, surface wettability, and color alteration of uncoated and coated marbles were measured. For sulphation reaction, marble slabs were coated with these polymers and then they were exposed at nearly 8 ppm SO2 concentration at 100% relative humidity conditions together with uncoated ones in a reaction chamber for several days for testing their protection efficiency. The extent of reaction was determined by leaching of gypsum formed on the marble surfaces in deionized water and then determining the sulphate content by ion chromatography. The protection efficiency of polymer treatments was expressed as comparing the gypsum crust thickness of the coated and uncoated marble plates. The comparison among the polymers showed that the surface hydrophobicity, water capillary absorption and structure of polymer would be important factors affecting the protection efficiency. The use of high molecular weight PLA (HMWPLA) polymer on marble surfaces provided significant protection up to 60% which was indicated that HMWPLA polymer seems to be promising polymer as protective coating agent in reducing gypsum formation on marble surfaces in the polluted environment.

[1]  M. Zielecka,et al.  Silicone-containing polymer matrices as protective coatings: Properties and applications , 2006 .

[2]  E. Espuche,et al.  Water sorption and permeation in chitosan films: Relation between gas permeability and relative humidity , 2001 .

[3]  O. Lindqvist,et al.  A study of the sulphation of silane-treated sandstone and limestone in a sulphur dioxide atmosphere , 1994 .

[4]  K. Gauri,et al.  REACTIVITY OF TREATED AND UNTREATED MARBLE SPECIMENS IN AN S02 ATMOSPHERE , 1973 .

[5]  Ioannis Zuburtikudis,et al.  Fabrication of super-hydrophobic surfaces for enhanced stone protection , 2009 .

[6]  Itai Panas,et al.  Model study of the first steps in the deterioration of calcareous stone I. Initial surface sulphite formation on calcite , 1994 .

[7]  R. Tharanathan,et al.  Chitin/Chitosan — Safe, Ecofriendly Packaging Materials with Multiple Potential Uses , 2007 .

[8]  R. F. González,et al.  Basic methodology for the assessment and selection of water-repellent treatments applied on carbonatic materials , 2001 .

[9]  R. N. Tharanathan,et al.  Biodegradable films and composite coatings: past, present and future , 2003 .

[10]  T. Skoulikidis,et al.  Inversion of Marble Sulfation. Reconversion of Gypsum Films into Calcite on the Surfaces of Monuments and Statues , 1984 .

[11]  Munir Cheryan,et al.  Zein: the industrial protein from corn , 2001 .

[12]  G. Padua,et al.  Properties and Microstructure of Plasticized Zein Films , 1997 .

[13]  Susan Selke,et al.  An overview of polylactides as packaging materials. , 2004, Macromolecular bioscience.

[14]  T. Morén,et al.  The influence of wood polymers and extractives on wood colour induced by hydrothermal treatment , 2002, Holz als Roh- und Werkstoff.

[15]  Itai Panas,et al.  Model study of the first steps in the deterioration of calcareous stone II. Sulphate formation on calcite , 1994 .

[16]  E. Chiellini,et al.  Biodegrable polymers and plastics , 2012 .

[17]  Ioannis Zuburtikudis,et al.  Polymer-Silica nanoparticles composite films as protective coatings for stone-based monuments , 2007 .

[18]  Ioannis D Chryssoulakis,et al.  Assessment of synthetic polymeric coatings for the protection and preservation of stone monuments , 2007 .

[19]  Lucia Toniolo,et al.  Tailoring New Fluorinated Acrylic Copolymers as Protective Coatings for Marble , 2002 .

[20]  H. Viles,et al.  Channel flow cell studies on the evaluation of surface pretreatments using phosphoric acid or polymaleic acid for calcite stone protection. , 2003, Journal of colloid and interface science.

[21]  E. GÖktÜrk,et al.  Effect of airborne particle on SO2-calcite reaction , 1999 .

[22]  Dario Camuffo,et al.  Carbonate Stone: Chemical Behaviour, Durability and Conservation , 2000 .

[23]  H. Viles,et al.  Polymer coatings to passivate calcite from acid attack: polyacrylic acid and polyacrylonitrile. , 2003, Journal of colloid and interface science.

[24]  M. Michalski,et al.  Food materials adhesion: a review. , 1997, Critical reviews in food science and nutrition.