Effect of Zirconia Precursor on the Properties of ZrO2-SiO2 Sol-Gel Oxides

Sol-gel zirconia-silica oxides were synthesized with two zirconium precursors, zirconium n-butoxide and zirconium acetylacetonate, and two different hydrolysis catalysts, HCl and H2SO4. The samples prepared with HCl were additionally sulfated with a 1 M solution of H2SO4. Characterization was performed with FTIR and 29Si-MAS-NMR spectroscopy, as well as with nitrogen adsorption. Because zirconium and silicon alkoxides have different hydrolysis rates, it was necessary to perform a pre-hydrolysis of the silicon alkoxide before mixing. The atom distribution in the ZrO2-SiO2 system depended on the zirconium precursor, which also determined the zirconium incorporation in the silica lattice, which was greater for zirconium acetylacetonate. The zirconium precursor also was responsible for the silanol concentration, which increases when samples were sulfated. Sulfating stabilizes the specific surface area. On sulfate samples calcined at 800°C BET areas larger than 500 m2/g were obtained.

[1]  G. Ghiotti,et al.  Infrared study of surface modes on silica , 1978 .

[2]  P. Ugliengo,et al.  Cage-like clusters as models for the hydroxyls of silica: ab initio calculation of 1H and 29Si NMR chemical shifts , 1999 .

[3]  Inmaculada Rodríguez-Ramos,et al.  Influence of Si/Zr ratio on the formation of surface acidity in silica-zirconia aerogels , 2000 .

[4]  Y. Murakami,et al.  Generation of acid sites by SiO2 deposition on groups IVB metal oxides , 1992 .

[5]  K. Nakamoto.  Infrared and Raman Spectra of Inorganic and Coordination Compounds , 1978 .

[6]  D. Acosta,et al.  Crystalline phases of sol-gel ZrO_2 in the ZrO_2-SiO_2 system: Differential thermal analysis and electron microscopy studies , 1995 .

[7]  F. H. Hambleton,et al.  Surface structure and catalytic cracking properties of the SiO2BCl3, SiO2AlMe3, and SiO2AlCl3 systems: I. Infrared and analytical studies , 1971 .

[8]  F. Monte,et al.  Stabilization of Tetragonal ZrO2 in ZrO2–SiO2 Binary Oxides , 2004 .

[9]  F. Illas,et al.  Ab initio calculations of 29Si solid state NMR chemical shifts of silane and silanol groups in silica , 2000 .

[10]  R. Gómez,et al.  Zirconia/Silica Sol−Gel Catalysts: Effect of the Surface Heterogeneity on the Selectivity of 2-Propanol Decomposition† , 1997 .

[11]  M. A. D’Amato,et al.  Isomerization of n-Butane on Pt/So2−4-ZrO2 and Mechanical Mixtures of Pt/Al2O3+SO2−4–ZrO2 , 1995 .

[12]  H. Kung.  Formation of new acid sites in dilute oxide solid solutions: A predictive model , 1984 .

[13]  H. Bosman,et al.  Characterization of the Acid Strength of SiO2-ZrO2 Mixed Oxides , 1994 .

[14]  R. Gómez,et al.  Preparation of sol-gel sulfated ZrO2SiO2 and characterization of its surface acidity , 1995 .

[15]  R. Gómez,et al.  Free Radical Formation in ZrO2–SiO2Sol–Gel Derived Catalysts , 1999 .

[16]  F. Rojas,et al.  Hydrolysis, Condensation, and Tetragonal Phase Formation in Sol-Gel Zirconia Prepared with Electron-Irradiated Alkoxide Solutions , 2000 .

[17]  B. Davis,et al.  Sulfated zirconia as a hydrocarbon conversion catalyst , 1994 .

[18]  J. Védrine,et al.  Superacid and Catalytic Properties of Sulfated Zirconia , 1993 .

[19]  J. Sohn,et al.  Catalytic and surface properties of ZrO2 modified with sulfur compounds , 1989 .

[20]  E. I. Ko,et al.  One-step synthesis and characterization of zirconia-sulfate aerogels as solid superacids , 1994 .

[21]  C. Morterra,et al.  On the Acid-Catalyzed Isomerization of Light Paraffins over a ZrO2/SO4 System: The Effect of Hydration , 1994 .

[22]  G. Mcvicker,et al.  Acidity of silica-substituted zirconia , 1992 .