Over the last couple of years rapid thermal annealing (RTA) equipment suppliers have been aggressively developing lamp-based furnaces capable of achieving ramp-up rates on the order of hundreds of degrees per second. One of the driving forces for adopting such a strategy was the experimental demonstration of 30nm p-type junctions by employing a ramp-up rate of ≈400°C/s. It was subsequently proposed that the ultra-fast temperature ramp-up was suppressing transient enhanced diffusion (TED) of boron which results from the interaction of the implantation damage with the dopant. The capability to achieve very high temperature ramp-rates was thus embraced as an essential requirement of the next generation of RTA equipment. In this paper, recent experimental data examining the effect of the ramp-up rate during spike-and soak-anneals on enhanced diffusion and shallow junction formation is reviewed. The advantage of increasing the ramp-up rate is found to be largest for the shallowest, 0.5-keV, B implants. At such ultra-low energies (ULE) the advantage arises from a reduction of the total thermal budget. Simulations reveal that a point of diminishing return is quickly reached when increasing the ramp-up rate since the ramp-down rate is in practice limited. At energies where TED dominates, a high ramp-up rate is only effective in minimizing diffusion if the implanted dose is sufficiently small so that the TED can be run out during the ramp-up portion of the anneal; for larger doses, a high ramp-up rate only serves to postpone the TED to the ramp-down duration of the anneal. However, even when TED is minimized at higher implant energies via high ramp-up rates, the advantage is unobservable due to the rather large as-implanted depth. It appears then that while spike anneals allow the activation of ULE-implanted dopants to be maximized while minimizing their diffusion the limitation imposed by the ramp-down rate compromises the advantage of very aggressive ramp-up rates.
[1]
R. Fair,et al.
A Quantitative Model for the Diffusion of Phosphorus in Silicon and the Emitter Dip Effect
,
1977
.
[2]
M. Giles.
Transient Phosphorus Diffusion Below the Amorphization Threshold
,
1991
.
[3]
Ultra-shallow junction formation by spike annealing in a lamp-based or hot-walled rapid thermal annealing system: effect of ramp-up rate
,
1998
.
[4]
K. K. Bourdelle,et al.
Electrical activation kinetics for shallow boron implants in silicon
,
1999
.
[5]
Lourdes Pelaz,et al.
Reduction of transient diffusion from 1–5 keV Si+ ion implantation due to surface annihilation of interstitials
,
1997
.
[6]
F. Klemens,et al.
The role of the surface in transient enhanced diffusion
,
1995
.
[7]
Martin Jaraiz,et al.
Simulation of cluster evaporation and transient enhanced diffusion in silicon
,
1996
.
[8]
Bracht,et al.
Properties of intrinsic point defects in silicon determined by zinc diffusion experiments under nonequilibrium conditions.
,
1995,
Physical review. B, Condensed matter.