Friction stir processing: An effective technique to refine grain structure and enhance ductility

Abstract Commercial 5083 Al rolled plates were subjected to friction stir processing (FSP) with a tool rotational speed of 430 rpm and a traverse feed rate of 90 mm/min. This treatment resulted in a fine grained microstructure of 1.6 μm and an average misorientation angle of 24°. Ductility was measured using tensile elongations at a temperature of 250 °C at three strain rates, and demonstrated that a decrease in grain size resulted in significantly enhanced ductility and lower forming loads. The ductility of the friction stir processed material was enhanced by a factor ranging from 2.6 to 5 compared to the ductility of the as received material, in the range of the strain rates tested. The strain rate sensitivity of the processed material is 0.33 while for the as received, it is 0.018. The deformation mechanism, in the fine-grained specimens is mainly controlled by solute drag creep, though the contribution of grain boundary sliding to the deformation process cannot be overlooked. Both mechanisms led to significant flow localization and simultaneous cavity formation.

[1]  M. Soliman.  Effect of Cu concentration on the high-temperature creep behavior of AlCu solid solution alloys , 1995 .

[2]  W. P. Green,et al.  Failure mechanisms in superplastic AA5083 materials , 2006 .

[3]  J. Weertman.  CREEP OF INDIUM, LEAD, AND SOME OF THEIR ALLOYS WITH VARIOUS METALS , 1960 .

[4]  R. Mishra,et al.  Enhanced superplasticity through friction stir processing in continuous cast AA5083 aluminum , 2007 .

[5]  Amit K. Ghosh,et al.  Cavity formation and early growth in a superplastic Al–Mg alloy , 2002 .

[6]  K. A. Padmanabhan,et al.  On the role of process variables in the friction stir processing of cast aluminum A319 alloy , 2010 .

[7]  A. S. Argon,et al.  Steady-state creep of single-phase crystalline matter at high temperature , 1976 .

[8]  F. Mohamed.  Creep behavior of solid solution alloys , 1979 .

[9]  E. Taleff,et al.  The high-temperature deformation and tensile ductility of Al alloys , 1999 .

[10]  W. P. Green,et al.  Deformation mechanisms in superplastic AA5083 materials , 2005 .

[11]  A. Squillace,et al.  High temperature deformation of friction stir processed 7075 aluminium alloy , 2005 .

[12]  Z. Ma,et al.  Achieving exceptionally high superplasticity at high strain rates in a micrograined Al–Mg–Sc alloy produced by friction stir processing , 2008 .

[13]  V. Balasubramanian,et al.  Mechanical property and microstructural changes during friction stir processing of cast aluminum 2285 alloy , 2009 .

[14]  Rajiv S. Mishra,et al.  Friction Stir Welding and Processing , 2007 .

[15]  V. Balasubramanian,et al.  Influences of tool pin profile and tool shoulder diameter on the formation of friction stir processing zone in AA6061 aluminium alloy , 2008 .

[16]  Rajiv S. Mishra,et al.  Superplastic deformation behaviour of friction stir processed 7075Al alloy , 2002 .

[17]  Amit K. Ghosh,et al.  Cavity growth in a superplastic Al–Mg alloy: II. An improved plasticity based model , 2002 .

[18]  A. Argon,et al.  Steady-state creep of alloys due to viscous motion of dislocations☆ , 1976 .

[19]  C. J. Smithells,et al.  Smithells metals reference book , 1949 .

[20]  Moataz M. Attallah,et al.  Friction stir welding parameters: a tool for controlling abnormal grain growth during subsequent heat treatment , 2005 .

[21]  J. C. Huang,et al.  Deformation mechanisms during low-and high-temperature superplasticity in 5083 Al-Mg alloy , 2002 .

[22]  Tracy W. Nelson,et al.  Microstructure evolution during FSW/FSP of high strength aluminum alloys , 2005 .

[23]  Amit K. Ghosh,et al.  Grain size and temperature dependence of superplastic deformation in an Al–Mg alloy under isostructural condition , 2000 .

[24]  H. Hosokawa,et al.  Quantitative assessment of superplastic deformation behavior in a commercial 5083 alloy , 1998 .

[25]  T. Nieh,et al.  Warm-temperature tensile ductility in Al−Mg alloys , 1998 .

[26]  Z. Ma,et al.  Low-temperature superplasticity of friction stir processed Al–Zn–Mg–Cu alloy , 2008 .

[27]  Radovan Kovacevic,et al.  Microstructural evolution in the friction stir welded 6061 aluminum alloy (T6-temper condition) to copper , 2006 .