Influence of cell shape on mechanical properties of Ti-6Al-4V meshes fabricated by electron beam melting method.

Ti-6Al-4V reticulated meshes with different elements (cubic, G7 and rhombic dodecahedron) in Materialise software were fabricated by additive manufacturing using the electron beam melting (EBM) method, and the effects of cell shape on the mechanical properties of these samples were studied. The results showed that these cellular structures with porosities of 88-58% had compressive strength and elastic modulus in the range 10-300MPa and 0.5-15GPa, respectively. The compressive strength and deformation behavior of these meshes were determined by the coupling of the buckling and bending deformation of struts. Meshes that were dominated by buckling deformation showed relatively high collapse strength and were prone to exhibit brittle characteristics in their stress-strain curves. For meshes dominated by bending deformation, the elastic deformation corresponded well to the Gibson-Ashby model. By enhancing the effect of bending deformation, the stress-strain curve characteristics can change from brittle to ductile (the smooth plateau area). Therefore, Ti-6Al-4V cellular solids with high strength, low modulus and desirable deformation behavior could be fabricated through the cell shape design using the EBM technique.

[1]  Emeka Nkenke,et al.  Effects of topographical surface modifications of electron beam melted Ti-6Al-4V titanium on human fetal osteoblasts. , 2008, Journal of biomedical materials research. Part A.

[2]  G. Menges,et al.  Estimation of mechanical properties for rigid polyurethane foams , 1975 .

[3]  M. H. Luxner,et al.  A finite element study on the effects of disorder in cellular structures. , 2009, Acta biomaterialia.

[4]  Ola L. A. Harrysson,et al.  Properties of Ti–6Al–4V non-stochastic lattice structures fabricated via electron beam melting , 2008 .

[5]  Shivakumar Raman,et al.  Mechanical evaluation of porous titanium (Ti6Al4V) structures with electron beam melting (EBM). , 2010, Journal of the mechanical behavior of biomedical materials.

[6]  Ryan B. Wicker,et al.  Characterization of Ti–6Al–4V open cellular foams fabricated by additive manufacturing using electron beam melting , 2010 .

[7]  Wenguang Zhang,et al.  Fabrication and characterization of porous Ti6Al4V parts for biomedical applications using electron beam melting process , 2009 .

[8]  Jeffrey Wadsworth,et al.  Effect of cell morphology on the compressive properties of open-cell aluminum foams , 2000 .

[9]  Matej Vesenjak,et al.  Cell shape effect evaluation of polyamide cellular structures , 2010 .

[10]  S. Goldstein.  The mechanical properties of trabecular bone: dependence on anatomic location and function. , 1987, Journal of biomechanics.

[11]  Xin-Lin Gao,et al.  Effects of Cell Shape and Strut Cross-Sectional Area Variations on the Elastic Properties of Three-Dimensional Open-cell Foams , 2004 .

[12]  Yang Hao,et al.  Compression fatigue behavior of Ti-6Al-4V mesh arrays fabricated by electron beam melting , 2012 .

[13]  Hamid Nayeb-Hashemi,et al.  Mechanical properties of open-cell rhombic dodecahedron cellular structures , 2012 .

[14]  Luc Salvo,et al.  Effect of microstructural topology upon the stiffness and strength of 2D cellular structures , 2002 .

[15]  Abhay Pandit,et al.  Fabrication methods of porous metals for use in orthopaedic applications. , 2006, Biomaterials.

[16]  M. Ashby,et al.  Cellular solids: Structure & properties , 1988 .

[17]  A. Burstein,et al.  The Mechanical Properties of Cortical Bone , 1974 .

[18]  L. Murr,et al.  Compression deformation behavior of Ti-6Al-4V alloy with cellular structures fabricated by electron beam melting. , 2012, Journal of the mechanical behavior of biomedical materials.

[19]  Masao Nakamura,et al.  Mechanical Properties of Plastic Foams , 1969 .

[20]  Robert F. Singer,et al.  Cellular Titanium by Selective Electron Beam Melting , 2007 .

[21]  Vikram Deshpande,et al.  The compressive and shear responses of corrugated and diamond lattice materials , 2006 .

[22]  Xin-Lin Gao,et al.  Effects of cell shape and cell wall thickness variations on the elastic properties of two-dimensional cellular solids , 2005 .

[23]  Rui Yang,et al.  Young’s modulus and mechanical properties of Ti-29Nb-13Ta-4.6Zr in relation to α″ martensite , 2002 .

[24]  Yasuo Yamada,et al.  Compressive Deformation Characteristics of Open-Cell Mg Alloys with Controlled Cell Structure , 2002 .

[25]  R. Poprawe,et al.  Laser additive manufacturing of metallic components: materials, processes and mechanisms , 2012 .

[26]  A. A. Zadpoor,et al.  Mechanical properties of open-cell metallic biomaterials manufactured using additive manufacturing , 2013 .

[27]  J. M. Lederman.  The prediction of the tensile properties of flexible foams , 1971 .

[28]  L. Murr,et al.  Next-generation biomedical implants using additive manufacturing of complex, cellular and functional mesh arrays , 2010, Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences.

[29]  Zhi-Yong Zhang,et al.  Porous titanium-6 aluminum-4 vanadium cage has better osseointegration and less micromotion than a poly-ether-ether-ketone cage in sheep vertebral fusion. , 2013, Artificial organs.

[30]  C. Wen,et al.  Investigation of cell shape effect on the mechanical behaviour of open-cell metal foams , 2012 .

[31]  Clemens A van Blitterswijk,et al.  Bone ingrowth in porous titanium implants produced by 3D fiber deposition. , 2007, Biomaterials.

[32]  M. B. Rhodes,et al.  Mechanical properties of particulate‐filled polyurethane foams , 1978 .

[33]  W. Ko.  Deformations of Foamed Elastomers , 1965 .

[34]  R. Singer,et al.  Cellular Ti-6Al-4V structures with interconnected macro porosity for bone implants fabricated by selective electron beam melting. , 2008, Acta biomaterialia.

[35]  M. Ashby,et al.  The mechanics of three-dimensional cellular materials , 1982, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[36]  L. Murr,et al.  Microstructure and mechanical properties of open-cellular biomaterials prototypes for total knee replacement implants fabricated by electron beam melting. , 2011, Journal of the mechanical behavior of biomedical materials.

[37]  M. Ashby,et al.  Metal Foams: A Design Guide , 2000 .