Electronic and structural properties of doped amorphous and nanocrystalline silicon deposited at low substrate temperatures by radio-frequency plasma-enhanced chemical vapor deposition

The gas phase doping of hydrogenated amorphous silicon and hydrogenated nanocrystalline silicon thin films deposited on glass and on plastic (polyethylene terephthalate) substrates is reported. Two substrate temperatures were used during deposition: 25 °C and 100 °C. Films were deposited by radio-frequency plasma-enhanced chemical vapor deposition using phosphine or diborane for n- or p-type doping, respectively. Similar electronic and structural properties are obtained for the doped films deposited on either substrate. Hydrogen dilution of silane is used to improve the electronic and structural properties of the amorphous films and to obtain nanocrystalline films. The most conductive amorphous films have n-type dark conductivity at room temperature ∼10−3 Ω−1 cm−1 and ∼10−5 Ω−1 cm−1 when deposited at 100 °C and 25 °C, respectively, or p-type room-temperature dark conductivity ∼10−7 Ω−1 cm−1 at both substrate temperatures. The most conductive nanocrystalline films deposited at 100 °C have n- and p-type dark conductivity at room temperature above 10−2 Ω−1 cm−1 while nanocrystalline films deposited at 25 °C only have p-type conductivity higher than 10−2 Ω−1 cm−1 at room temperature. Isochronal annealing at temperatures up to 300 °C showed that the dopants are fully activated at the deposition temperature in doped nanocrystalline samples and that they are only partially activated in amorphous films deposited at low substrate temperatures.The gas phase doping of hydrogenated amorphous silicon and hydrogenated nanocrystalline silicon thin films deposited on glass and on plastic (polyethylene terephthalate) substrates is reported. Two substrate temperatures were used during deposition: 25 °C and 100 °C. Films were deposited by radio-frequency plasma-enhanced chemical vapor deposition using phosphine or diborane for n- or p-type doping, respectively. Similar electronic and structural properties are obtained for the doped films deposited on either substrate. Hydrogen dilution of silane is used to improve the electronic and structural properties of the amorphous films and to obtain nanocrystalline films. The most conductive amorphous films have n-type dark conductivity at room temperature ∼10−3 Ω−1 cm−1 and ∼10−5 Ω−1 cm−1 when deposited at 100 °C and 25 °C, respectively, or p-type room-temperature dark conductivity ∼10−7 Ω−1 cm−1 at both substrate temperatures. The most conductive nanocrystalline films deposited at 100 °C have n- and p-type dar...

[1]  V. Lumelsky,et al.  Sensitive skin , 2000, IEEE Sensors Journal.

[2]  Gregory N. Parsons,et al.  Stability of low-temperature amorphous silicon thin film transistors formed on glass and transparent plastic substrates , 2000 .

[3]  V. Chu,et al.  Doping of amorphous and microcrystalline silicon films by hot-wire CVD and RFPECVD at low substrate temperatures on plastic substrates , 2000 .

[4]  V. Chu,et al.  Amorphous and microcrystalline silicon films grown at low temperatures by radio-frequency and hot-wire chemical vapor deposition , 1999 .

[5]  M. Yamaguchi,et al.  Effect of hydrogen dilution on the optical properties of hydrogenated amorphous silicon prepared by plasma deposition , 1999 .

[6]  Sigurd Wagner,et al.  a-Si:H TFTs made on polyimide foil by PE-CVD at 150 °C , 1998 .

[7]  P. Cabarrocas,et al.  Metastability of Phosphorus- or Boron Doped a-Si:H Films , 1998 .

[8]  J. Abelson,et al.  Low temperature fabrication of amorphous silicon thin film transistors by dc reactive magnetron sputtering , 1997 .

[9]  S. Gates Prospects for Active Matrix Displays on Plastic , 1997 .

[10]  K. Clausen,et al.  Hydrogen concentration and mass density of diamondlike carbon films obtained by x‐ray and neutron reflectivity , 1994 .

[11]  P. Cabarrocas DEPOSITION OF INTRINSIC, PHOSPHORUS-DOPED, AND BORON-DOPED HYDROGENATED AMORPHOUS SILICON FILMS AT 50 C , 1994 .

[12]  Masatoshi Wakagi,et al.  Change in crystalline morphologies of polycrystalline silicon films prepared by radio‐frequency plasma‐enhanced chemical vapor deposition using SiF4+H2 gas mixture at 350 °C , 1994 .

[13]  M. Feng,et al.  Effects of Plasma Enhanced Chemical Vapor Deposition Substrate Heating on the Electrical Properties of α‐Si:H Thin Film Transistors , 1994 .

[14]  Robert A. Street,et al.  Amorphous Silicon Electronics , 1992 .

[15]  Street Ra Model for growth of a-Si:H and its alloys , 1991 .

[16]  R. Street,et al.  Hydrogenated amorphous silicon: Index , 1991 .

[17]  Street Hydrogen chemical potential and structure of a-Si:H. , 1991, Physical Review B (Condensed Matter).

[18]  M. Schubert,et al.  Deposition of phosphorus doped microcrystalline silicon below 70 °C at 70 MHz , 1991 .

[19]  Stavola,et al.  Vibrational spectroscopy of acceptor-hydrogen complexes in silicon: Evidence for low-frequency excitations. , 1988, Physical review. B, Condensed matter.

[20]  Veprek,et al.  Effect of grain boundaries on the Raman spectra, optical absorption, and elastic light scattering in nanometer-sized crystalline silicon. , 1987, Physical review. B, Condensed matter.

[21]  Stutzmann Hydrogen passivation of boron acceptors in silicon: Raman studies. , 1987, Physical review. B, Condensed matter.

[22]  Jin Jang,et al.  Anomalous substrate and annealing temperature dependencies of heavily boron‐doped hydrogenated amorphous silicon , 1987 .

[23]  Johnson,et al.  Interstitial hydrogen and neutralization of shallow-donor impurities in single-crystal silicon. , 1986, Physical review letters.

[24]  J. Pankove,et al.  Hydrogen localization near boron in silicon , 1985 .

[25]  Rustum Roy,et al.  Materials Research Society , 1984 .

[26]  J. Stuchlík,et al.  Density of the gap states in undoped and doped glow discharge a-Si:H , 1983 .

[27]  W. Spear,et al.  Electronic properties of substitutionally doped amorphous Si and Ge , 1976 .