论文信息 - The reduction of Eu3+ to Eu2+ in BaMgSiO4∶Eu prepared in air and the luminescence of BaMgSiO4∶Eu2+ phosphor

The reduction of Eu3+ to Eu2+ in BaMgSiO4∶Eu prepared in air and the luminescence of BaMgSiO4∶Eu2+ phosphor

The reduction of Eu3+ to Eu2+ in air has been observed in a silicate matrix for the first time in BaMgSiO4∶Eu prepared by high-temperature solid-state reaction. Emission and excitation spectra were employed to detect the presence of Eu2+ ions in the compound and this reduction was explained by a charge compensation model proposed previously. In BaMgSiO4∶Eu2+, Eu2+ ions occupy three different lattice sites by substitution for Ba2+ ions. Eu2+ ions on Ba(1) and Ba(2) sites gave emissions at about 500 nm while that on Ba(3) site showed an emission band at 398 nm. All the emissions of Eu2+ ions in BaMgSiO4∶Eu2+ were not quenched at room temperature.

[1] I. Tale,et al. Recombination luminescence mechanisms in Ba3(PO4)2 , 1979 .

[2] Q. Su,et al. Luminescent properties of divalent samarium-doped strontium hexaborate , 1999 .

[3] G. Adachi,et al. Structure of europium(II) tetraborate , 1980 .

[4] R. D. Shannon. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides , 1976 .

[5] Q. Su,et al. The Reduction of Re3+ in Srb6O10 Prepared in Air and the Luminescence of Srb6O10:Re2+(Re=Eu, Sm, Tm) , 1999 .

[6] Qiang Su,et al. VUV excited luminescence of europium activated calcium borophosphate prepared in air , 2002 .

[7] C. Pyun,et al. Phosphors for Plasma Display Panels , 2000 .

[8] Q. Su,et al. The valence change from RE3+ to RE2+ (REEu, Sm, Yb) in SrB4O7: RE prepared in air and the spectral properties of RE2+ , 1993 .

[9] P. Hagenmuller,et al. Luminescence of Eu3+ and Eu2+ in the new BaLnB9O16 borates (Ln = rare earth) , 1987 .

[10] A. Lakshmanan,et al. Development of BaSO4:Eu thermoluminescence phosphor , 1999 .

[11] G. Blasse,et al. Luminescence of Eu2+ in silicate host lattices with alkaline earth ions in a row , 1996 .