Superparamagnetism of ferrite particles dispersed in spherical polymeric materials

Superparamagnetic iron oxide particles synthesized in water-in-oil microemulsions have been incorporated into a polymer matrix. The microstructured micellar environment provides a template for polymer synthesis, leading to the formation of interconnected polymer particles with spherical morphologies. The resulting iron oxide-polymer composites reveal superparamagnetic properties and low temperature remanence and susceptibility characteristic of a superparamagnet. The results of temperature and field dependent magnetic characterizations of these composites are described. Ultramicrotomed TEM micrographs show that the iron oxide particles (size >

[1] José Rivas,et al. Chemical Reactions in Microemulsions: A Powerful Method to Obtain Ultrafine Particles , 1993 .

[2] S. Mann,et al. Template mineralization of self-assembled anisotropic lipid microstructures , 1993, Nature.

[3] C. O'connor. SPIN GLASS PROPERTIES OF AMORPHOUS INTERMETALLIC SOLIDS , 1993 .

[4] D. Kaplan,et al. Catalytic and interfacial aspects of enzymatic polymer synthesis in reversed micellar systems , 1993, Biotechnology and bioengineering.

[5] V. Mehrotra,et al. Matrix-Mediated Synthesis of Nanocrystalline γ-Fe2O3: A New Optically Transparent Magnetic Material , 1992, Science.

[6] D. Fiorani. Comparison between fine particles and spin-glass properties , 1992 .

[7] Ramesh C. Patel,et al. The use of associated surfactant media for the synthesis of fine particles: Preparation of iron oxides , 1991 .

[8] C. O'connor,et al. Magnetic and electrical properties of a new chromium telluride phase: CrTe2 , 1990 .

[9] M. Pileni,et al. Synthesis of cadmium sulfide in situ in reverse micelles. 2. Influence of the interface on the growth of the particles , 1990 .

[10] S. Mann,et al. Formation of iron oxides in unilamellar vesicles , 1988 .