Two-parameter characterization of elastic–plastic crack front fields: Surface cracked plates under uniaxial and biaxial bending

Abstract In this paper the J–Q two-parameter characterization of elastic–plastic crack front fields is examined for surface cracked plates under static uniaxial and biaxial bending. Extensive three-dimensional elastic–plastic finite element analyses are performed for semi-elliptical surface cracks in a finite thickness plate, under remote uniaxial and biaxial bending conditions, covering from small-scale to large-scale yielding. Surface cracks with aspect ratios a / c  = 0.2, 1.0 and relative depths a / t  = 0.2, 0.6, corresponding to four specimen configurations, are investigated. The full stress field solutions are obtained in topological planes perpendicular to the crack fronts. The question of J–Q characterization is addressed by comparing these elastic–plastic crack-front stress fields with J–Q family of stress fields. It is found that the J–Q characterization provides good estimate for the constraint loss for crack front stress fields. It is also shown that for medium load levels, reasonable agreements are achieved between the T -stress based Q -factors and the Q -factors obtained from the finite element analyses. Complete distributions of the J -integral and Q -factors for the wide range of geometry and loading conditions are obtained. Size requirements in terms of crack depth (for shallow cracks) or ligament size (for deep cracks) that are necessary to ensure J–Q characterization of crack front fields in surface cracked plates are also discussed.

[1]  Characterization of crack-tip field and constraint for bending specimens under large-scale yielding , 2004 .

[2]  Noel P. O’Dowd.  Applications of two parameter approaches in elastic-plastic fracture mechanics , 1995 .

[3]  N. Arakere,et al.  J-T characterized stress fields of surface-cracked metallic liners bonded to a structural backing - I. Uniaxial tension , 2010 .

[4]  Yuh J. Chao,et al.  On the fracture of solids characterized by one or two parameters: Theory and practice , 1994 .

[5]  M. D. German,et al.  Requirements for a one parameter characterization of crack tip fields by the HRR singularity , 1981, International Journal of Fracture.

[6]  Xin Wang,et al.  On the Constraint-Based Failure Assessment of Surface Cracked Plates under Biaxial Loading , 2005 .

[7]  G. C. Sih,et al.  Review of triaxial crack border stress and energy behavior , 1989 .

[8]  Guandong Wang,et al.  Two Parameter Fracture Mechan-ics: Theory and Applications , 1993 .

[9]  Bjørn Skallerud,et al.  Two-parameter fracture assessment of surface cracked cylindrical shells during collapse , 2006 .

[10]  Yongyi Wang,et al.  A two-parameter characterization of elastic-plastic crack tip fields and applications to cleavage fracture , 1991 .

[11]  C. F. Shih,et al.  Higher-order analysis of crack tip fields in elastic power-law hardening materials , 1993 .

[12]  Xin Wang,et al.  Elastic T-stress solutions for semi-elliptical surface cracks in finite thickness plates , 2003 .

[13]  Jin-Su Kim,et al.  Effect of biaxial loads on elastic-plastic J and crack tip constraint for cracked plates: finite element study , 2004 .

[14]  M. M. K. Lee,et al.  Effects of biaxial loading on crack driving force and constraints for shallow semi-elliptical surface flaws , 1999 .

[15]  D. Munz,et al.  Application of the three-term elastic-plastic asymptotic expansion for the characterization of stress fields near a front of a semi-elliptical crack , 1994 .

[16]  Yuh J. Chao,et al.  Higher order asymptotic crack tip fields in a power-law hardening material , 1993 .

[17]  Noel P. O’Dowd,et al.  A Framework for Quantifying Crack Tip Constraint , 1993 .

[18]  Robert H. Dodds,et al.  Continuum and micromechanics treatment of constraint in fracture , 1993, International Journal of Fracture.

[19]  Jonas Faleskog,et al.  Effects of local constraint along three-dimensional crack fronts—a numerical and experimental investigation , 1995 .

[20]  C. Shih,et al.  Family of crack-tip fields characterized by a triaxiality parameter—II. Fracture applications , 1992 .

[21]  Claudio Ruggieri,et al.  Correlation of fracture behavior in high pressure pipelines with axial flaws using constraint designed test specimens. Part II: 3-D effects on constraint , 2006 .

[22]  R. H. Dodds,et al.  Constraint effects in fracture , 1993 .

[23]  R. McMeeking,et al.  On criteria for J-dominance of crack-tip fields in large-scale yielding , 1979 .

[24]  Robert M. McMeeking,et al.  Finite deformation analysis of crack-tip opening in elastic-plastic materials and implications for fracture , 1977 .

[25]  Ping Ding,et al.  An estimation method for the determination of the second elastic–plastic fracture mechanics parameters , 2012 .

[26]  Yuh J. Chao,et al.  J-A2 Characterization of Crack-Tip Fields: Extent of J-A2 Dominance and Size Requirements , 1998 .

[27]  Bård Nyhus,et al.  Structural integrity of pipelines: T‐stress by line‐spring , 2005 .

[28]  G. P. Nikishkov,et al.  An algorithm and a computer program for the three-term asymptotic expansion of elastic-plastic crack tip stress and displacement fields , 1995 .

[29]  Xin Wang,et al.  Solutions of the second elastic–plastic fracture mechanics parameter in test specimens , 2010 .

[30]  Fracture criterion based on the higher-order asymptotic fields , 1995 .

[31]  Y. Wang.  On the Two-Parameter Characterization of Elastic-Plastic Crack-Front Fields in Surface-Cracked Plates , 1993 .

[32]  Kim Wallin,et al.  Validation of constraint‐based methodology in structural integrity of ferritic steels for nuclear reactor pressure vessels , 2006 .

[33]  Bjørn Skallerud,et al.  Two-parameter fracture mechanics and circumferential crack growth in surface cracked pipelines using line-spring elements , 2008 .

[34]  Andrew H. Sherry,et al.  Methods for including constraint effects within the SINTAP procedures , 1998 .

[35]  C. Shih,et al.  Family of crack-tip fields characterized by a triaxiality parameter—I. Structure of fields , 1991 .

[36]  Deutsche Gesellschaft für Zerstörungsfreie Prüfung,et al.  Defect assessment in components : fundamentals and applications , 1991 .

[37]  Xin Wang,et al.  Two-parameter characterization of elastic–plastic crack front fields: Surface cracked plates under tensile loading , 2009 .

[38]  J. Hutchinson.  Fundamentals of the Phenomenological Theory of Nonlinear Fracture Mechanics , 1983 .

[39]  Xin Wang,et al.  Elastic T -stress solutions for semi-elliptical surface cracks in finite thickness plates subject to non-uniform stress distributions , 2004 .

[40]  N. Arakere,et al.  J–Q characterized stress fields of surface-cracked metallic liners – II. Composite overwrapped pressure vessels , 2011 .

[41]  Nikolaos Aravas,et al.  Determination of higher-order terms in asymptotic elastoplastic crack tip solutions , 1991 .

[42]  J. Hancock,et al.  Two-Parameter Characterization of Elastic-Plastic Crack-Tip Fields , 1991 .

[43]  M. Williams,et al.  On the Stress Distribution at the Base of a Stationary Crack , 1956 .