Evaluation of critical current density and residual resistance ratio limits in powder in tube Nb3Sn conductors

High critical current density (Jc) Nb3Sn A15 multifilamentary wires require a large volume fraction of small grain, superconducting A15 phase, as well as Cu stabilizer with high Residual Resistance Ratio (RRR) to provide electromagnetic stabilization and protection. In Powder-in-Tube (PIT) wires the unreacted Nb7.5wt.%Ta outer layer of the tubular filaments acts as a diffusion barrier and protects the interfilamentary Cu stabilizer from Sn contamination. A high RRR requirement generally imposes a restricted A15 reaction heat treatment (HT) to prevent localized full reaction of the filament that could allow Sn to reach the Cu. In this paper we investigate recent high quality PIT wires that achieve a Jc(12 T, 4.2 K) up to ~2500 A/mm-2 and find that the minimum diffusion barrier thickness decreases as the filament aspect ratio increases from ~1 in the inner rings of filaments to 1.3 in the outer filament rings. We found that just 2-3 diffusion barrier breaches can degrade RRR from 300 to 150 or less. Using progressive etching of the Cu we also found that the RRR degradation is localized near the external filaments where deformation is highest. Consequently minimizing filament distortion during strand fabrication is important for reducing RRR degradation. The additional challengemore » of developing the highest possible Jc must be addressed by forming the maximum fraction of high Jc small-grain (SG) A15 and minimizing low Jc large-grain (LG) A15 morphologies. Finally, in one wire we found that 15% of the filaments had a significantly enhanced SG/LG A15 ratio and no residual A15 in the core, a feature that opens a path to substantial Jc improvement.« less

[1]  D. Larbalestier,et al.  Irreversibility field and critical current density as a function of heat treatment time and temperature for a pure niobium powder-in-tube Nb3Sn conductor , 2002 .

[2]  L. Oberli Development of the $\hbox{Nb}_{3}\hbox{Sn}$ Rutherford Cable for the EuCARD High Field Dipole Magnet FRESCA2 , 2013, IEEE Transactions on Applied Superconductivity.

[3]  C. Senatore,et al.  Extensive Characterization of the 1 mm PIT ${\rm Nb}_{3}{\rm Sn}$ Strand for the 13-T FRESCA2 Magnet , 2012, IEEE Transactions on Applied Superconductivity.

[4]  J. Elen,et al.  Potential fabrication method of superconducting multifilament wires of the A-15 type , 1975 .

[5]  L. Rossi,et al.  Advanced Accelerator Magnets for Upgrading the LHC , 2012, IEEE Transactions on Applied Superconductivity.

[6]  L. Bottura,et al.  Targets for R&D on Nb3Sn Conductor for High Energy Physics , 2015, IEEE Transactions on Applied Superconductivity.

[7]  J. Elen,et al.  Multifilament Nb 3 Sn superconductors produced by the E.C.N. technique , 1979 .

[8]  C. M. Fischer INVESTIGATION OF THE RELATIONSHIPS BETWEEN SUPERCONDUCTING PROPERTIES AND Nb 3 Sn REACTION CONDITIONS IN POWDER-IN-TUBE NB 3 SN CONDUCTORS , 2002 .

[9]  Kevin W Eliceiri,et al.  NIH Image to ImageJ: 25 years of image analysis , 2012, Nature Methods.

[10]  Youzhu Zhang,et al.  High field Nb/sub 3/Sn conductor development at Oxford Superconducting Technology , 2003 .

[11]  H. Veringa,et al.  Growth kinetics and characterization of superconducting properties of multifilament materials made by the ECN powder method , 1983 .

[12]  A Review of the Properties of Nb3Sn and Their Variation with A15 Composition, Morphology and Strain State , 2006, cond-mat/0606303.

[13]  Michael B. Field,et al.  Optimizing $\hbox{Nb}_{3}\hbox{Sn}$ Conductors for High Field Applications , 2014, IEEE Transactions on Applied Superconductivity.

[14]  David C. Larbalestier,et al.  Microstructural factors important for the development of high critical current density Nb3Sn strand , 2008 .

[15]  D. R. Dietderich,et al.  Nb3Sn research and development in the USA – Wires and cables , 2008 .

[16]  H. Kate,et al.  The strain dependence of the critical properties of Nb3Sn conductors , 1999 .

[17]  Johannes E. Schindelin,et al.  Fiji: an open-source platform for biological-image analysis , 2012, Nature Methods.

[18]  D. Larbalestier,et al.  Composition and connectivity variability of the A15 phase in PIT Nb3Sn wires , 2015 .

[19]  D. Larbalestier,et al.  Examination of the trade-off between intrinsic and extrinsic properties in the optimization of a modern internal tin Nb3Sn conductor , 2013, 1310.6729.

[20]  J. Elen,et al.  Multifilament V 3 Ga and Nb 3 Sn superconductors produced by the ECN-technique , 1977 .

[21]  D. Easton,et al.  Kirkendall voids--A detriment to Nb 3 Sn superconductors , 1979 .

[22]  C. Senatore,et al.  Formation and upper critical fields of the two distinct A15 phases in the subelements of powder-in-tube Nb3Sn wires , 2013, 1301.5251.

[23]  D. Larbalestier,et al.  Corrigendum: Examination of the trade-off between intrinsic and extrinsic properties in the optimization of a modern internal tin Nb3Sn conductor (2014 Supercond. Sci. Technol. 27 065013) , 2015 .

[24]  Albertus Godeke,et al.  Performance boundaries in Nb3Sn superconductors , 2005 .

[25]  D. Larbalestier,et al.  Multifilamentary niobium tin magnet conductors , 1975 .

[26]  D. Larbalestier,et al.  Correlation of filament distortion and RRR degradation in drawn and rolled PIT and RRP Nb3Sn wires , 2016 .

[27]  E. F. Koch,et al.  Flux pinning centers in superconducting Nb3Sn , 1975 .

[28]  S. A. Gourlay,et al.  Magnet R&D for the US LHC Accelerator Research Program (LARP) , 2006 .

[29]  W. Wessel,et al.  Progress in the development of Nb/sub 3/Sn conductors based on the "Powder in tube" method with finer filaments , 1999, IEEE transactions on applied superconductivity.

[30]  D. Larbalestier,et al.  The upper critical field of filamentary Nb3Sn conductors , 2004, cond-mat/0410463.