How Do Spherical Diblock Copolymer Nanoparticles Grow during RAFT Alcoholic Dispersion Polymerization?

A poly(2-(dimethylamino)ethyl methacrylate) (PDMA) chain transfer agent (CTA) is used for the reversible addition–fragmentation chain transfer (RAFT) alcoholic dispersion polymerization of benzyl methacrylate (BzMA) in ethanol at 70 °C. THF GPC analysis indicated a well-controlled polymerization with molecular weight increasing linearly with conversion. GPC traces also showed high blocking efficiency with no homopolymer contamination apparent and Mw/Mn values below 1.35 in all cases. 1H NMR studies confirmed greater than 98% BzMA conversion for a target PBzMA degree of polymerization (DP) of up to 600. The PBzMA block becomes insoluble as it grows, leading to the in situ formation of sterically stabilized diblock copolymer nanoparticles via polymerization-induced self-assembly (PISA). Fixing the mean DP of the PDMA stabilizer block at 94 units and systematically varying the DP of the PBzMA block enabled a series of spherical nanoparticles of tunable diameter to be obtained. These nanoparticles were characterized by TEM, DLS, MALLS, and SAXS, with mean diameters ranging from 35 to 100 nm. The latter technique was particularly informative: data fits to a spherical micelle model enabled calculation of the core diameter, surface area occupied per copolymer chain, and the mean aggregation number (Nagg). The scaling exponent derived from a double-logarithmic plot of core diameter vs PBzMA DP suggests that the conformation of the PBzMA chains is intermediate between the collapsed and fully extended state. This is in good agreement with 1H NMR studies, which suggest that only 5−13% of the BzMA residues of the core-forming chains are solvated. The Nagg values calculated from SAXS and MALLS are in good agreement and scale approximately linearly with PBzMA DP. This suggests that spherical micelles grow in size not only as a result of the increase in copolymer molecular weight during the PISA synthesis but also by exchange of individual copolymer chains between micelles and/or by sphere–sphere fusion events.

[1]  P. Fowler,et al.  Determination of Effective Particle Density for Sterically Stabilized Carbon Black Particles: Effect of Diblock Copolymer Stabilizer Composition. , 2015, Langmuir : the ACS journal of surfaces and colloids.

[2]  S. Armes,et al.  Industrially-relevant polymerization-induced self-assembly formulations in non-polar solvents: RAFT dispersion polymerization of benzyl methacrylate , 2015 .

[3]  S. Armes,et al.  Semi-crystalline diblock copolymer nano-objects prepared via RAFT alcoholic dispersion polymerization of stearyl methacrylate , 2015 .

[4]  A. Lowe,et al.  Synthesis of poly(stearyl methacrylate-b-3-phenylpropyl methacrylate) nanoparticles in n-octane and associated thermoreversible polymorphism , 2015 .

[5]  A. Lowe,et al.  RAFT Dispersion Polymerization in Nonpolar Media: Polymerization of 3-Phenylpropyl Methacrylate in n-Tetradecane with Poly(stearyl methacrylate) Homopolymers as Macro Chain Transfer Agents , 2015 .

[6]  Lauren Boldon,et al.  Review of the fundamental theories behind small angle X-ray scattering, molecular dynamics simulations, and relevant integrated application , 2015, Nano reviews.

[7]  Wangqing Zhang,et al.  Dispersion RAFT polymerization: comparison between the monofunctional and bifunctional macromolecular RAFT agents , 2014 .

[8]  P. Sun,et al.  A New Strategy To Synthesize Temperature- and pH-Sensitive Multicompartment Block Copolymer Nanoparticles by Two Macro-RAFT Agents Comediated Dispersion Polymerization , 2014 .

[9]  S. Armes,et al.  Tuning the critical gelation temperature of thermo-responsive diblock copolymer worm gels , 2014 .

[10]  Wangqing Zhang,et al.  Doubly thermoresponsive brush‐linear‐linear ABC triblock copolymer nanoparticles prepared through dispersion RAFT polymerization , 2014 .

[11]  S. Armes,et al.  Poly(glycerol monomethacrylate)-Poly(benzyl methacrylate) Diblock Copolymer Nanoparticles via RAFT Emulsion Polymerization: Synthesis, Characterization, and Interfacial Activity , 2014 .

[12]  S. Armes,et al.  Rational synthesis of low-polydispersity block copolymer vesicles in concentrated solution via polymerization-induced self-assembly. , 2014, Journal of the American Chemical Society.

[13]  P. Roth,et al.  RAFT dispersion polymerization of 3-phenylpropyl methacrylate with poly[2-(dimethylamino)ethyl methacrylate] macro-CTAs in ethanol and associated thermoreversible polymorphism. , 2014, Soft matter.

[14]  Steven P. Armes,et al.  Polymerization-Induced Self-Assembly of Block Copolymer Nano-objects via RAFT Aqueous Dispersion Polymerization , 2014, Journal of the American Chemical Society.

[15]  S. Armes,et al.  Poly(methacrylic acid)-based AB and ABC block copolymer nano-objects prepared via RAFT alcoholic dispersion polymerization , 2014 .

[16]  S. Armes,et al.  Thermo-responsive Diblock Copolymer Worm Gels in Non-polar Solvents , 2014, Journal of the American Chemical Society.

[17]  Olivier Colombani,et al.  The analysis of solution self-assembled polymeric nanomaterials. , 2014, Chemical Society reviews.

[18]  A. Lowe,et al.  Polymerization-induced self-assembly: ethanolic RAFT dispersion polymerization of 2-phenylethyl methacrylate , 2014 .

[19]  S. Armes,et al.  RAFT Aqueous Dispersion Polymerization Yields Poly(ethylene glycol)-Based Diblock Copolymer Nano-Objects with Predictable Single Phase Morphologies , 2013, Journal of the American Chemical Society.

[20]  S. Armes,et al.  Efficient Synthesis of Poly(methacrylic acid)-block-Poly(styrene-alt-N-phenylmaleimide) Diblock Copolymer Lamellae Using RAFT Dispersion Polymerization , 2013 .

[21]  Sarah E. Mastroianni,et al.  Poly(methyl methacrylate-block-vinyl-m-triphenylamine): synthesis by RAFT polymerization and melt-state self-assembly , 2013 .

[22]  J. Rieger,et al.  Soft nanostructured films with an ultra-low volume fraction of percolating hard phase. , 2013, Macromolecular rapid communications.

[23]  S. Howdle,et al.  Advantages of Block Copolymer Synthesis by RAFT-Controlled Dispersion Polymerization in Supercritical Carbon Dioxide , 2013 .

[24]  Olivier Boyron,et al.  Effect of the pH on the RAFT Polymerization of Acrylic Acid in Water. Application to the Synthesis of Poly(acrylic acid)-Stabilized Polystyrene Particles by RAFT Emulsion Polymerization , 2013 .

[25]  Jianxiong Xu,et al.  RAFT Dispersion Polymerization of Styrene in Water/Alcohol The Solvent Effect on Polymer Particle Growth during Polymer Chain Propagation , 2013 .

[26]  S. Armes,et al.  RAFT dispersion polymerization in non-polar solvents: facile production of block copolymer spheres, worms and vesicles in n-alkanes , 2013 .

[27]  C. Pan,et al.  Recent advances in RAFT dispersion polymerization for preparation of block copolymer aggregates , 2013 .

[28]  M. Monteiro,et al.  Influence of the Z‐group on the RAFT‐mediated polymerizations in nanoreactors , 2012 .

[29]  C. Pan,et al.  Formation of the block copolymer aggregates via polymerization-induced self-assembly and reorganization , 2012 .

[30]  S. Armes,et al.  Efficient Synthesis of Sterically‐Stabilized Nano‐Objects via RAFT Dispersion Polymerization of Benzyl Methacrylate in Alcoholic Media , 2012, Advanced materials.

[31]  J. Rieger,et al.  Polymerization-Induced Self-Assembly: From Soluble Macromolecules to Block Copolymer Nano-Objects in One Step , 2012 .

[32]  S. Armes,et al.  Efficient Synthesis of Amine-Functional Diblock Copolymer Nanoparticles via RAFT Dispersion Polymerization of Benzyl Methacrylate in Alcoholic Media , 2012 .

[33]  S. Armes,et al.  Predictive Phase Diagrams for RAFT Aqueous Dispersion Polymerization: Effect of Block Copolymer Composition, Molecular Weight, and Copolymer Concentration , 2012 .

[34]  S. Armes,et al.  Facile Synthesis of Methacrylic ABC Triblock Copolymer Vesicles by RAFT Aqueous Dispersion Polymerization , 2012 .

[35]  Adam Blanazs,et al.  Sterilizable gels from thermoresponsive block copolymer worms. , 2012, Journal of the American Chemical Society.

[36]  J. Rieger,et al.  Effect of the solvent composition on the morphology of nano-objects synthesized via RAFT polymerization of benzyl methacrylate in dispersed systems , 2012 .

[37]  M. Cunningham,et al.  Polymer Nanoparticles via Living Radical Polymerization in Aqueous Dispersions: Design and Applications , 2012 .

[38]  Krzysztof Matyjaszewski,et al.  Atom Transfer Radical Polymerization (ATRP): Current Status and Future Perspectives , 2012 .

[39]  S. Armes,et al.  Anionic polyelectrolyte-stabilized nanoparticles via RAFT aqueous dispersion polymerization. , 2012, Langmuir : the ACS journal of surfaces and colloids.

[40]  R. Pecora,et al.  Dynamic Light Scattering: Applications of Photon Correlation Spectroscopy , 2011 .

[41]  S. Armes,et al.  Non-spherical morphologies from cross-linked biomimetic diblock copolymers using RAFT aqueous dispersion polymerization , 2011 .

[42]  S. Armes,et al.  Mechanistic insights for block copolymer morphologies: how do worms form vesicles? , 2011, Journal of the American Chemical Society.

[43]  S. Armes,et al.  Aqueous dispersion polymerization: a new paradigm for in situ block copolymer self-assembly in concentrated solution. , 2011, Journal of the American Chemical Society.

[44]  J. Rieger,et al.  One-Pot Synthesis of Poly(methacrylic acid-co-poly(ethylene oxide) methyl ether methacrylate)-b-polystyrene Amphiphilic Block Copolymers and Their Self-Assemblies in Water via RAFT-Mediated Radical Emulsion Polymerization. A Kinetic Study , 2011 .

[45]  J. Rieger,et al.  Influence of the stirring speed and CaCl2 concentration on the nano‐object morphologies obtained via RAFT‐mediated aqueous emulsion polymerization in the presence of a water‐soluble macroRAFT agent , 2011 .

[46]  J. Rieger,et al.  Well-Defined Amphiphilic Block Copolymers and Nano-objects Formed in Situ via RAFT-Mediated Aqueous Emulsion Polymerization , 2011 .

[47]  C. Pan,et al.  Multiple Morphologies of PAA-b-PSt Assemblies throughout RAFT Dispersion Polymerization of Styrene with PAA Macro-CTA , 2011 .

[48]  C. Boyer,et al.  Building nanostructures using RAFT polymerization , 2011 .

[49]  C. Pan,et al.  Morphology Transitions in RAFT Polymerization , 2010 .

[50]  C. Pan,et al.  Direct preparation of vesicles from one-pot RAFT dispersion polymerization , 2010 .

[51]  C. Pan,et al.  One-pot synthesis of polymeric nanomaterials via RAFT dispersion polymerization induced self-assembly and re-organization , 2010 .

[52]  J. Rieger,et al.  Surfactant-Free RAFT Emulsion Polymerization Using Poly(N,N-dimethylacrylamide) Trithiocarbonate Macromolecular Chain Transfer Agents , 2010 .

[53]  S. Armes,et al.  RAFT synthesis of sterically stabilized methacrylic nanolatexes and vesicles by aqueous dispersion polymerization. , 2010, Angewandte Chemie.

[54]  J. Rieger,et al.  Amphiphilic block copolymer nano-fibers via RAFT-mediated polymerization in aqueous dispersed system. , 2010, Chemical communications.

[55]  C. Pan,et al.  Formation of Vesicular Morphologies via Polymerization Induced Self-Assembly and Re-Organization. , 2010, Macromolecular rapid communications.

[56]  Guojun Liu,et al.  Self-assembled ABC triblock copolymer double and triple helices. , 2009, Angewandte Chemie.

[57]  P. Zetterlund,et al.  Controlled/living heterogeneous radical polymerization in supercritical carbon dioxide , 2009 .

[58]  A. Ryan,et al.  Templated formation of giant polymer vesicles with controlled size distributions. , 2009, Nature materials.

[59]  Pete R. Jemian,et al.  Irena: tool suite for modeling and analysis of small‐angle scattering , 2009 .

[60]  Christine Jérôme,et al.  Amphiphilic Poly(ethylene oxide) Macromolecular RAFT Agent as a Stabilizer and Control Agent in ab Initio Batch Emulsion Polymerization , 2008 .

[61]  Sheng Zhong,et al.  Block Copolymer Assembly via Kinetic Control , 2007, Science.

[62]  C. Moire,et al.  Synthesis of Well-Defined Polyacrylate Particle Dispersions in Organic Medium Using Simultaneous RAFT Polymerization and Self-Assembly of Block Copolymers. A Strong Influence of the Selected Thiocarbonylthio Chain Transfer Agent , 2007 .

[63]  Graeme Moad,et al.  Living Radical Polymerization by the RAFT Process - A Second Update , 2006 .

[64]  Graeme Moad,et al.  Living radical polymerization by the RAFT process , 2005 .

[65]  G. Ozin,et al.  Block copolymers under periodic, strong three-dimensional confinement. , 2005, Journal of the American Chemical Society.

[66]  A. Ryan,et al.  Bilayers and interdigitation in block copolymer vesicles. , 2005, Journal of the American Chemical Society.

[67]  Britton Chance,et al.  Near-infrared-emissive polymersomes: self-assembled soft matter for in vivo optical imaging. , 2005, Proceedings of the National Academy of Sciences of the United States of America.

[68]  M. Andersson,et al.  Accuracy in multiangle light scattering measurements for molar mass and radius estimations. Model calculations and experiments. , 2003, Analytical chemistry.

[69]  M. P. Tarazona,et al.  Combination of SEC/MALS experimental procedures and theoretical analysis for studying the solution properties of macromolecules. , 2003, Journal of Biochemical and Biophysical Methods.

[70]  D. Maysinger,et al.  Micellar Nanocontainers Distribute to Defined Cytoplasmic Organelles , 2003, Science.

[71]  J. S. Pedersen,et al.  The structure of P85 Pluronic block copolymer micelles determined by small-angle neutron scattering , 2003 .

[72]  F. Bates,et al.  Molecular Exchange in PEO−PB Micelles in Water , 2003 .

[73]  E. Harth,et al.  New polymer synthesis by nitroxide mediated living radical polymerizations. , 2001, Chemical reviews.

[74]  R. Jerome,et al.  Core-Shell-Corona Micelles with a Responsive Shell. , 2001, Angewandte Chemie.

[75]  F. Bates,et al.  Preparation, stability, and in vitro performance of vesicles made with diblock copolymers. , 2000, Biotechnology and bioengineering.

[76]  J. S. Pedersen.  Form factors of block copolymer micelles with spherical, ellipsoidal and cylindrical cores , 2000 .

[77]  M. P. Tarazona,et al.  A simple method to determine unperturbed dimensions of polymers using size exclusion chromatography and multiangle light scattering , 2000 .

[78]  J. Chiefari,et al.  Living free-radical polymerization by reversible addition - Fragmentation chain transfer: The RAFT process , 1998 .

[79]  C. Burger,et al.  Scattering Functions of Polymeric Core−Shell Structures and Excluded Volume Chains , 1998 .

[80]  Zana,et al.  Dynamics of Micelles of Polyethyleneoxide-Polypropyleneoxide-Polyethyleneoxide Block Copolymers in Aqueous Solutions. , 1997, Journal of colloid and interface science.

[81]  S. Armes,et al.  Micellization of poly(2-(dimethylamino)ethyl methacrylate-block-methyl methacrylate) copolymers in aqueous solution , 1996 .

[82]  Peter Schurtenberger,et al.  Scattering Functions of Semiflexible Polymers with and without Excluded Volume Effects , 1996 .

[83]  Markus Antonietti,et al.  Micellization of strongly segregated block copolymers , 1996 .

[84]  A. Eisenberg,et al.  Multiple Morphologies and Characteristics of “Crew-Cut” Micelle-like Aggregates of Polystyrene-b-poly(acrylic acid) Diblock Copolymers in Aqueous Solutions , 1996 .

[85]  J. S. Pedersen,et al.  Scattering form factor of block copolymer micelles , 1996 .

[86]  Lifeng Zhang,et al.  Multiple Morphologies of "Crew-Cut" Aggregates of Polystyrene-b-poly(acrylic acid) Block Copolymers , 1995, Science.

[87]  Stanislaus S. Wong,et al.  Block Copolymer "Crew-Cut" Micelles in Water , 1994 .

[88]  Anwei Qin,et al.  Hybridization of Block Copolymer Micelles , 1993 .

[89]  P. Wyatt.  Light scattering and the absolute characterization of macromolecules , 1993 .

[90]  A. J. Paine.  Dispersion polymerization of styrene in polar solvents. 7. A simple mechanistic model to predict particle size , 1990 .

[91]  L. Reimer.  Transmission Electron Microscopy: Physics of Image Formation and Microanalysis , 1989 .

[92]  K. Ganesh,et al.  Block copolymer self‐assembly in selective solvents: Spherical micelles with segregated cores , 1989 .

[93]  L. Leibler.  Theory of Microphase Separation in Block Copolymers , 1980 .

[94]  P. Kratochvíl,et al.  Block and graft copolymer micelles in solution , 1976 .

[95]  B. Berne,et al.  Dynamic Light Scattering: With Applications to Chemistry, Biology, and Physics , 1976 .

[96]  G. Berry.  Thermodynamic and Conformational Properties of Polystyrene. I. Light‐Scattering Studies on Dilute Solutions of Linear Polystyrenes , 1966 .

[97]  G. Fournet,et al.  Small‐Angle Scattering of X‐Rays , 1956 .

[98]  Bruno H. Zimm,et al.  Apparatus and Methods for Measurement and Interpretation of the Angular Variation of Light Scattering; Preliminary Results on Polystyrene Solutions , 1948 .

[99]  A. Sánchez,et al.  Exploiting nucleobase-containing materials – from monomers to complex morphologies using RAFT dispersion polymerization , 2015 .

[100]  Wangqing Zhang,et al.  Precise evaluation of the block copolymer nanoparticle growth in polymerization-induced self-assembly under dispersion conditions , 2014 .

[101]  S. Armes,et al.  Comparison of pseudo-living character of RAFT polymerizations conducted under homogeneous and heterogeneous conditions , 2014 .

[102]  G. Delaittre,et al.  Preparation of Hybrid Latex Particles and Core–Shell Particles Through the Use of Controlled Radical Polymerization Techniques in Aqueous Media , 2010 .

[103]  R. Colby,et al.  Chain Dimensions and Entanglement Spacings , 2007 .

[104]  J. E. Mark,et al.  Physical properties of polymers handbook , 2007 .

[105]  C. Svaneborg,et al.  A Small-Angle Neutron and X-ray Contrast Variation Scattering Study of the Structure of Block Copolymer Micelles: Corona Shape and Excluded Volume Interactions , 2003 .

[106]  M. Winnik,et al.  Characterization by Fluorescence Energy Transfer of the Core of Polyisoprene-Poly(Methyl Methacrylate) Diblock Copolymer Micelles. Strong Segregation in Acetonitrile , 1998 .

[107]  U. Dayal,et al.  Studies on molecular weight determination using refractive index and multi-angle laser light scattering detectors in size exclusion chromatography , 1994 .

[108]  R. Pecora.  Dynamic Light Scattering , 1985 .

[109]  B. Ninham,et al.  Theory of self-assembly of hydrocarbon amphiphiles into micelles and bilayers , 1976 .

[110]  P. Debye,et al.  Molecular-weight determination by light scattering. , 1947, The Journal of physical and colloid chemistry.