Origin of particles during reactive sputtering of oxides using planar and cylindrical magnetrons.

Particles generated during reactive magnetron sputtering cause defects in optical thin films, which may lead to losses in optical performance, pinholes, loss of adhesion, decreased laser-induced damage thresholds and many more negative effects. Therefore, it is important to reduce the particle contamination during the manufacturing process. In the present paper, the origin of particles during the deposition of various oxide films by midfrequency pulsed reactive magnetron sputtering was investigated. Several steps have been undertaken to decrease the particle contamination during the complete substrate handling procedure. It was found that conditioning of the vacuum chamber can help to decrease the defect level significantly. This level remains low for several hours of sputtering and increases after 100 hours of process time. Particle densities of SiO(2) films deposited with cylindrical and planar dual magnetrons at different process parameters as well as different positions underneath the target were compared. It was observed that the process power influences the particle density significantly in case of planar targets while cylindrical targets have no such strong dependence. In addition, the particle contamination caused by different cylindrical target materials was analyzed. No major differences in particle contamination of different cylindrical target types and materials were found.

[1]  Michael D. Abràmoff,et al.  Image processing with ImageJ , 2004 .

[2]  Gary S. Selwyn,et al.  In-situ analysis of particle contamination in magnetron sputtering processes , 1998 .

[3]  Z. Liu,et al.  Pulsed DC titanium nitride coatings for improved tribological performance and tool life , 2007 .

[4]  J. Szczyrbowski,et al.  New approaches for reactive sputtering of dielectric materials on large scale substrates , 1997 .

[5]  Yoshio Katakura,et al.  Particle measurements in vacuum tools by in situ particle monitor , 1999 .

[6]  C. Wickersham,et al.  Arc generation from sputtering plasma-dielectric inclusion interactions , 2002 .

[7]  P. Juliet,et al.  Surface defects and arc generation in reactive magnetron sputtering of aluminium oxide thin films , 1999 .

[8]  A. Anders.  Physics of arcing, and implications to sputter deposition , 2005 .

[9]  Klaus Goedicke,et al.  Pulsed magnetron sputter technology , 1993 .

[10]  S. Berg,et al.  Fundamental understanding and modeling of reactive sputtering processes , 2005 .

[11]  J. Musil,et al.  Reactive magnetron sputtering of thin films: present status and trends , 2005 .

[12]  P. Kelly,et al.  Magnetron sputtering: a review of recent developments and applications , 2000 .

[13]  N. Malkomes,et al.  Dynamic simulation of process control of the reactive sputter process and experimental results , 2001 .

[14]  I. Safi,et al.  Recent aspects concerning DC reactive magnetron sputtering of thin films: a review , 2000 .

[15]  Oliver Werner,et al.  New developments in magnetron sputter processes for precision optics , 2008, Optical Systems Design.

[16]  Kevin Robbie,et al.  State of the art in thin film thickness and deposition rate monitoring sensors , 2005 .

[17]  J. Strobel.  Cleaning of parts for precision-optic and glass substrates before coating , 2003, Optifab.