Construction of porous anode by sacrificial template for a passive direct methanol fuel cell

Abstract Simple addition of magnesium oxide (MgO) nanoparticles as a sacrificial pore-former into the catalytic layer (CL) and micro-porous layer (MPL) in the anode of a membrane electrode assembly (MEA) leads to the formation of porous anodic structure, thus greatly enhancing the performance of a passive direct methanol fuel cell. At the same PtRu(1:1) loading of 2.0 mg cm −2 , the MEAs with porous CL and with both porous MPL and CL exhibit the maximal power densities of 37.0 and 43.7 mW cm −2 at a temperature of 25 °C and with 3 M of methanol solution, respectively. When the PtRu loading decreases to 1.0 mg cm −2 , the maximum power density of an MEA with both porous MPL and CL is ca. 32.8 mW cm −2 , which is even higher than that of a conventional MEA with a PtRu loading of 2.0 mg cm −2 . The improved performance of the novel MEA can be ascribed to an increased electrochemical surface area, a decreased charge-transfer resistance as well as an efficient mass transfer of methanol after the formation of porous structure in the anode. The present work provides a very simple but very effective way to reduce the dosage of the noble metal catalysts for fuel cells.

[1]  Suli Wang,et al.  Improvement of direct methanol fuel cell performance by modifying catalyst coated membrane structure , 2005 .

[2]  Joon-Hee Kim,et al.  High performance membrane electrode assemblies by optimization of coating process and catalyst layer , 2011 .

[3]  Y. Sung,et al.  Improved mass transfer using a pore former in cathode catalyst layer in the direct methanol fuel cell , 2012 .

[4]  Lei Zhang,et al.  A review of anode catalysis in the direct methanol fuel cell , 2006 .

[5]  K. Jeng,et al.  Fabrication and impedance studies of DMFC anode incorporated with CNT-supported high-metal-content electrocatalyst , 2007 .

[6]  San Ping Jiang,et al.  Performance of direct methanol fuel cells prepared by hot-pressed MEA and catalyst-coated membrane (CCM) , 2007 .

[7]  Chaoyang Wang,et al.  Optimization of cathode catalyst layer for direct methanol fuel cells. Part I. Experimental investigation , 2006 .

[8]  Yituo Wang,et al.  Pore‐forming technology and performance of MEA for direct methanol fuel cells , 2013 .

[9]  S. Litster,et al.  PEM fuel cell electrodes , 2004 .

[10]  Marcelo Carmo,et al.  Alternative supports for the preparation of catalysts for low-temperature fuel cells: the use of carbon nanotubes , 2005 .

[11]  Suli Wang,et al.  Improving the DMFC performance with Ketjen Black EC 300J as the additive in the cathode catalyst layer , 2008 .

[12]  Hee‐Tak Kim,et al.  Modification of cathode structure by introduction of CNT for air-breathing DMFC , 2008 .

[13]  Mark Pritzker,et al.  On the role of the microporous layer in PEMFC operation , 2009 .

[14]  Wenjing Zhang,et al.  High-performance nanofiber fuel cell electrodes. , 2011, ChemSusChem.

[15]  Peter Lund,et al.  The Pore Structure of Direct Methanol Fuel Cell Electrodes , 2005 .

[16]  Zhaobin Wei,et al.  Influence of electrode structure on the performance of a direct methanol fuel cell , 2002 .

[17]  Tatyana V. Reshetenko,et al.  Cathode structure optimization for air-breathing DMFC by application of pore-forming agents , 2007 .

[18]  Suk Woo Nam,et al.  Direct formic acid fuel cell portable power system for the operation of a laptop computer , 2006 .

[19]  D. Candusso,et al.  A review on polymer electrolyte membrane fuel cell catalyst degradation and starvation issues: Causes, consequences and diagnostic for mitigation , 2009 .

[20]  Impact of anode catalyst layer porosity on the performance of a direct formic acid fuel cell , 2012 .

[21]  Qin Xin,et al.  Comparative studies of configurations and preparation methods for direct methanol fuel cell electrodes , 2007 .

[22]  Yu Wei,et al.  Improvement in high temperature proton exchange membrane fuel cells cathode performance with ammonium carbonate , 2005 .

[23]  Zhixiang Liu,et al.  Behavior of PEMFC in starvation , 2006 .

[24]  R. O’Hayre,et al.  Fuel Cell Fundamentals , 2005 .

[25]  Mu Pan,et al.  Porosity-graded micro-porous layers for polymer electrolyte membrane fuel cells , 2007 .

[26]  Ting Yuan,et al.  New anodic diffusive layer for passive micro-direct methanol fuel cell , 2009 .

[27]  H. Daiguji,et al.  Effect of glycerol on micro/nano structures of catalyst layers in polymer electrolyte membrane fuel cells , 2006 .

[28]  Y. S. Choi,et al.  Effect of Porosity in Catalyst Layers on Direct Methanol Fuel Cell Performances , 2013 .

[29]  M. Weaver,et al.  Effect of boron doping in the carbon support on platinum nanoparticles and carbon corrosion , 2009 .

[30]  Antonino S. Aricò,et al.  DMFCs: From Fundamental Aspects to Technology Development , 2001 .